Proceedings of the Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors -

Volumn , Issue , 1999, Pages 703-710

  Psaila Dombrowski, M J ^a   Hua, F H ^a   Doherty, P E ^a  

^a NONE

Author keywords

[No Author keywords available]

Indexed keywords

ELECTROCHEMISTRY; FAILURE ANALYSIS; HYDROGEN EMBRITTLEMENT; IMPURITIES; STEAM GENERATORS; STRESS CORROSION CRACKING; TEMPERATURE; TUBING;

ELECTROCHEMICAL POLARIZATION; ELECTROCHEMICAL TESTS;

LEAD ALLOYS;

EID: 0033489404     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1002/9781118787618.ch73     Document Type: Conference Paper

References (7)

1. B.P. Miglin, J.M. Sarver, M.J. Psaila-Dombrowski, and P.E. Doherty, "Lead Assisted Stress Corrosion Cracking of Nuclear Steam Generator Tubing Materials", Proceeding of Improving the Understanding and Control of Corrosion on the Secondary Side of Steam Generators, Airlie Center, October 1995.
2. A. Rocher, F. Cattant, D. Buisine, B Prieux, M. Helie, "Effect of Lead on the OD Degradation of Steam generator Tubes", proceedings of the Int. Syp. Fontevraud III, Fontevraud, France, Sept. 12-16, 1994, 538.
3. M. Helie, I. Lambert and Santarini, "Some Considerations About the Possible Mechanisms of Lead Assisted Stress Corrosion Cracking of Steam Generator Tubing", Seventh Int. Syp. On Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Breckenridge, CO August 7-10, 1995, 247-258.
4. K.K. Chung, et al, "Lead Induced Stress Corrosion Cracking of Alloy 690 in High Temperature Water", Seventh Int. Syp. On Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Breckenridge, CO August 7-10, 1995, 233-246.
5. R.D. McCright, "Effects of Environmental Species and Metallurgical Structure on the Hydrogen Entry into Steel", Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, Unieux-Firminy, France, June 1973.
6. P. E. Doherty, et al. "On the Influence of Manufacturing Practices on the SCC Behavior of Alloy 690 Steam Generator Tubing" Proceedings of Improving the Understanding and Control of Corrosion on the Secondary Side of Steam Generators, Airley, VA, Oct. 9-13, 1995.
7. J.M. Sarver, et al. "The Influence of Manufacturing Processes on the Microstructure, Grain Boundary Characteristics and SCC Behavior of Alloy 690 Steam Generator Tubing", Proceedings of the Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE; Breckenridge, CO., August 7 - 10, 1995.