Lead-induced SCC propagation rates in alloy 600

Proceedings of the Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors -

Volumn , Issue , 1999, Pages 657-665

  Wright, M D ^a   Mirzai, M ^b  

^a CANADIAN NUCLEAR LABORATORIES   (Canada)

^b ONTARIO POWER GENERATION   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

ALLOYS; CRACK PROPAGATION; FRACTURE MECHANICS; FRACTURE TESTING; LEAD; PH EFFECTS; STEAM GENERATORS; TUBES (COMPONENTS);

ALL-VOLATILE TREATMENT; LEAD-INDUCED STRESS CORROSION CRACKING;

STRESS CORROSION CRACKING;

EID: 0033489132     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1002/9781118787618.ch68     Document Type: Conference Paper

References (22)

1. Scarth, et al. "CANDU® Steam Generator Fitness-for-Service Guidelines" Third International Steam Generator and Heat Exchanger Conference, Toronto (1998) CNS 149-162.
2. M. Mirzai, et al. "Stress Corrosion Cracking/Corrosion Fatigue in Alloy 600" Eighth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems Amelia Island, Florida, TMS, (1997), 11-18.
3. Curicio and M.M. Shanahan, "Steam Generator Tube Peformance in Ontario Hydro CANDU PHWRS" 3RD International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, Traverse City, MI, TMS, (1987) 409-418.
4. King, F. Gonzalez and J. Brown "Stress Corrosion Cracking Experience in Steam Generators at Bruce NGS", Sixth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, San Diego CA., TMS, (1993) 233-240.
5. Agrawal and J.P.N. Paine, "Lead Cracking of Alloy 600 - A Review" Fourth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, Jekyll Island, Georgia, NACE, (1986) 7.1-7.17.
6. Rocher, F. Nordman and D. Feron, "Transport of Lead in Secondary Systems of PWR Plants", Water Chemistry of Nuclear Reactor Systems, Bournemouth, UK, BNES 2 (1992) 249-255.
7. Stubbe, et al., "Corrosion Secondaire Des GV De Doel: Le Plomb et Le Cuivre Sont-ils Impliques" Fontevraud III, SFEN, September (1994) 356-364.
8. Clark and O.E. Lepik, private communication, OHT Report No. A-NGS-96-160-P: "Bruce A SG Tubing - Summary Report #3 of Metallurgical Examinations (as of September, 1995)", November 1996.
9. M.A. Clark, O.E. Lepik and S.M. Pagan, "Investigation of Bruce A Steam Generator Crevice Environment: Results and Comparison of Hideout Return, Deposit and Crack Analysis Evaluations", Proceedings of EPRI Surface Chemistry Workshop, (1996).
10. Takamatsu, et al., "Study on Lead-Induced Srtess Corrosion Cracking of Steam Generator Tubing Under AVT Water Chemistry Conditions" Eighth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, Amelia Island, FL, TMS, (1997) 216-223.
11. Wright, A. Manolescu and M. Mirzai, "Lead Induced SCC of Alloy 600 in Plausible Steam Generator Crevice Environments" Third International Steam Generator and Heat Exchanger Conference, Toronto, ON (1998) CNS 438-451.
12. Castano-Marin, D. Gomez-Briceno and F. Hernandez-Arroyo "Influence of Lead Contamination on the Stress Corrosion Resistance of Nickel Alloys", Sixth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, San Diego, CA., TMS (1993) 189-196.
13. Rocher, et al., "Effect of Lead on the OD Degradation of Steam Generator Tubes", Fontevraud III, SFEN (1994) 538-547.
14. Vaillant, D. Buisine and B. Prieux, "Comparative Behaviour of Alloys 600, 690 and 800 in Caustic Environments" Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, Breckenridge, CO,. NACE, (1995), 219-225.
15. Gomez-Briceno, M.L. Castano and M.S. Garcia "Stress Corrosion Cracking Susceptibility of Steam Generator Tube Materials in AVT (all volatile treatment) Chemistry Contaminated with Lead" Nuc. Eng. Design 165 (1996) 161-169.
16. Helie, I Lambert and G. Santarini, "Some Considerations about the Possible Mechanism of Lead Assisted Stress Corrosion Cracking of Steam Generator Tubing" Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, Breckenridge, CO, NACE (1995) 247-256.
17. Sakai, et al., "Effect of Lead Water Chemistry on Oxide Thin Film of Alloy 600", Corrosion, NACE, Vol. 48, 9, (1992) 745-750.
18. Costa, H. Talah, P. Marcus "Interaction of Lead with Nickel-Base Alloys 600 and 690" Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, Breckenridge, CO, NACE (1995), 199-208.
19. Wright, "Establishing Thresholds for Lead Induced Cracking Cracking of Steam Generator TubeAlloys" 7th Int. Conf. Water Chemistry of Nuclear Reactor Systems, Bournemouth, UK, BNES (1996), 435-441.
20. "PWR Molar Ratio Control Application Guidelines", EPRI TR-104811-V1 (1995) 2-13.
21. Hwang and U.C. Kim, "Effects of Pb on the Stress Corrosion Cracking of Alloy 600 in Weak Caustic Water" J. Corr. Sci. Soc. Korea, 25 (1996) 327-339.
22. Chung and I.H. Kuk "A Discussion on Caustic IGA/SCC and Pb SCC of Alloys 600 and 690" J. Corr. Sci. Soc. Korea, 25 (1996) 391-406.