Relationships between stress corrosion cracking tests and utility operating experience

Proceedings of the Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors -

Volumn , Issue , 1999, Pages 611-617

  Baum, Allen ^a  

^a BECHTEL BETTIS INC   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ACTIVATION ENERGY; CRACK PROPAGATION; DEGRADATION; EDDY CURRENT TESTING; MATERIALS TESTING; STEAM GENERATORS; TUBES (COMPONENTS);

EDDY CURRENT DISTRIBUTIONS; OUTSIDE DIAMETER STRESS CORROSION CRACKING; STRESS CORROSION CRACKING TESTS;

STRESS CORROSION CRACKING;

EID: 0033489131     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1002/9781118787618.ch63     Document Type: Conference Paper

References (20)

1. Steam Generator Reference Book, Chapter 8, Electric Power Research Institute, 1985.
2. W. H. Cullen, "Review of IGA, IGSCC and Wastage of Alloys 600 and 690 in High-Temperature Acidified Solutions," Control of Corrosion on the Secondary Side of Steam Generators, NACE, 1996, pp. 273-304.
3. R. Staehle and Z. Fang, "SCC of Alloys 600 and 690 in the Mid-Range of pH, Fontevraud IV, pp. 369-380.
4. B. Sala, S. Chevalier, M. Organista, "The Roles of Silica Compounds in the Corrosion Process of the Secondary Side of Steam Generators: An Electrochemical Study," Proc. Eighth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, American Nuclear Society, 1997, pp. 80-90.
5. P. M. Scott and P. Combrade, "On the Mechanisms of Secondary Side PWR Steam Generator Tube Cracking," Proc. Eighth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, American Nuclear Society, 1997, pp. 65-73.
6. E. Pierson and C. Laire, "The Influence of Copper on the SCC of Alloy 600 and Alloy 690 Steam Generator Tubes," Fontevraud IV, pp. 381-90.
7. B. P. Miglin, et al., "Lead Assisted Stress Corrosion Cracking of Nuclear Steam Generator Tubing Materials," Control of Corrosion on the Secondary Side of Steam Generators, NACE, 1996, pp. 305-20.
8. A. J. Baum, "Research Priorities in Thermal-Hydraulics," Control of Corrosion on the Secondary Side of Steam Generators, NACE, 1996, pp. 35-40.
9. A. J. Baum, "Temperature and Superheat Effects on Steam Generator Tube Outer Diameter Stress Corrosion Cracking," Seminar on Crevice Chemistry, Studsvik, Sweden, September 1998.
10. "Corrosion Evaluation of Thermally Treated Alloy 600 Tubing in Primary and Faulted Secondary Water Environments," EPRI NP-6721-SD, June 1990.
11. "PWR Secondary Water Chemistry Guidelines - Revision 4," EPRI TR-102134-R4, November 1996.
12. F. Vaillant, et al., "Effects of Microstructure and Mechanical Properties of Alloys 600 and 690 on Secondary Side SCC," Control of Corrosion on the Secondary Side of Steam Generators, NACE, 1996, pp. 321-36.
13. "Statistical Analysis of Steam Generator Tube Degradation: Additional Topics," EPRI TR-103566, July 1994.
14. "Steam Generator Tubing Outside Diameter Stress Corrosion Cracking at Tube Support Plates - Database for Alternate Repair Limits, Volume 1: 7/8 Inch Diameter Tubing," EPRI NP-7480-L, August 1996.
15. T. Saario and J. P. N. Paine, "Effect of the Surface Film Electric Resistance on Eddy Current Detectability of Surface Cracks in Alloy 600 Tubes," Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, 1995, pp. 327-36.
16. A. Baum, "Toward a Lagrangian Formulation of Crevice Chemistry," Seminar on Crevice Chemistry, Studsvik, Sweden, October 1996.
17. R. Hermer, "Boric Acid Inhibition of Steam Generator Materials Corrosion," Twelfth Biennial Topical Meeting on Reactor Operating Experience, Williamsburg Virginia, August 4-7, 1985.
18. "PWR Molar Ratio Control Application Guidelines, vol. 5," EPRI TR-104811-V5, December 1996.
19. L. Albertin et al., "Characterization of Deposits in Dampierre-1 Steam Generator Tube Support Plate Crevices," Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, 1995, pp. 399-410.
20. A. M. Lancha, et al, "Characterization of Ringhals 3 TSP Crevice and Tube Deposits," Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, NACE, 1995, pp. 27-34.