Effect of pre-irradiation grain boundary chemistry on IASCC

Proceedings of the Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors -

Volumn , Issue , 1999, Pages 923-929

  Kodama, M ^a   Ishiyama, Y ^a   Namatame, S ^b   Suzuki, S ^b   Fukuya, K ^c   Sakamoto, H ^c   Nakata, K ^d   Kato, T ^d  

^a NIPPON NUCLEAR FUEL DEVELOPMENT CO LTD   (Japan)

^b TOKYO ELECTRIC POWER COMPANY   (Japan)

^c TOSHIBA CORPORATION   (Japan)

^d HITACHI LTD   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

ANNEALING; CHROMIUM; ENERGY DISPERSIVE SPECTROSCOPY; FIELD EMISSION MICROSCOPES; FRACTURE; GRAIN BOUNDARIES; MOLYBDENUM; NEUTRON IRRADIATION; SCANNING ELECTRON MICROSCOPY; STRAIN RATE; STRESS CORROSION CRACKING; TRANSMISSION ELECTRON MICROSCOPY;

GRAIN BOUNDARY ANALYSIS; RADIATION INDUCED SEGREGATION; STRAIN RATE TEST;

STAINLESS STEEL;

EID: 0033489074     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1002/9781118787618.ch97     Document Type: Conference Paper

References (11)

1. W.L. Clarke and A.J. Jacobs, "Effect of Radiation Environment on SCC of Austenitic Materials," Proc. of 1st Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Myrtle Beach, South Carolina, August 1983, 451-461 (NACE).
2. P.L. Andresen et al., "State of Knowledge of Radiation Effects on Environmental Cracking in Light Water Reactor Core Materials," Proc. of 4th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Jekyll Island, Georgia, August 1989, 83-121 (NACE).
3. M. Kodama et al., "Effects of Fluence and Dissolved Oxygen on IASCC in Austenitic Stainless Steels," Proc. of 5th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Monterey, California, August 1991, 948-954 (ANS).
4. A.J. Jacobs et al., "The Correlation of Grain Boundary Composition in Irradiated Stainless Steel with IASCC Resistance," Proc. of 6th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, San Diego, California, August 1993, 597-606 (TMS).
5. M. Kodama et al., "IASCC Susceptibility of Austenitic Stainless Steels Irradiated to High Neutron Fluence," ibid., 583-590.
6. K. Asano et al., "Changes in Grain Boundary Composition Induced by Neutron Irradiation on Austenitic Stainless Steels," Proc. of 5th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Monterey, California, August 1991, 838-842 (ANS).
7. S.M. Bruemmer, L.A. Charlot and E.P. Simonen, "Irradiation-Induced Chromium Depletion and Its Influence on Intergranular Stress Corrosion Cracking of Stainless Steels," ibid., 821-286.
8. E.P. Simonen and S.M. Bruemmer, "Thermally Induced Grain Boundary Composition and Effects on Radiation-Induced Segregation," Proc. of 8th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Amelia Island, Florida, August 1997, 751-757 (ANS).
9. K. Nakata et al., "Effects of Foil Thickness on Measurement of Grain Boundary Segregation with FEG-TEM/EDS in Austenitic Stainless Steels," J. Electron Microscopy, 47(3) (1998), 193-200.
10. P.R. Okamoto and H. Wiedersich, "Segregation of Alloying Elements to Free Surfaces during Irradiation," J. Nucl. Mater., 53 (1974), 336-345.
11. M. Kaneko and S. Abe, "Effect of Intermetallic Compounds Precipitated at Grain-Boundaries on Intergranular Corrosion of Type 316L Stainless Steel in Nitric Acid Solution," Zairyo-to-Kankyo, 42 (1993), 700-707.