Microstructures and fatigue crack growth of EH36 TMCP steel weldments

International Journal of Fatigue

Volumn 21, Issue 8, 1999, Pages 857-864

  Tsay, L W ^a   Chern, T S ^a   Gau, C Y ^b   Yang, J R ^b  

^a NATIONAL TAIWAN OCEAN UNIVERSITY   (Taiwan)

^b NATIONAL TAIWAN UNIVERSITY   (Taiwan)

Author keywords

[No Author keywords available]

Indexed keywords

BAINITE; CRACK PROPAGATION; FERRITE; HARDNESS; HEAT AFFECTED ZONE; METALLOGRAPHIC MICROSTRUCTURE; TEMPERING; THERMOMECHANICAL TREATMENT; TOUGHNESS; WELDED STEEL STRUCTURES;

CARBON EQUIVALENT; FATIGUE CRACK GROWTH RATES; INTERLATH MICROPHASES; POSTWELD HEAT TREATMENT; THERMOMECHANICAL CONTROL PROCESS;

FATIGUE OF MATERIALS;

EID: 0033363361     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0142-1123(99)00021-3     Document Type: Article

References (15)

1. Tsukada K, Ohkita T, Ouchi C, Nagamine T, Hirabe K, Yako K. Application of on-line accelerated cooling (OLAC) to steel plates - development of OLAC Part 1. Nippon Kokan Tech. Report, Overseas, 1982;No. 35:24-34.
2. Ohno Y, Okamura Y, Uchino K, Yamamoto K, Matsuda S, Ikeda K, Saton T. Development of low-temperature steel for welding with high heat input. Nippon Steel Tech. Report, 1988;No. 36:49-59.
3. 2 steel with low carbon equivalent using on-line accelerated cooling (OLAC) - development of OLAC - Part 2. Nippon Kokan Tech. Report, Overseas, 1982;No. 35:35-46.
4. Tamehiro H., Yamada N., Matsuda H. Effect of the thermo-mechanical control process on the properties of high strength low alloy steel. Transactions ISIJ. 25(1):1985;54-61.
5. Yurioka N. TMCP steels and their welding. Weld in the World. 35(6):1996;375-390.
6. Kusuhara Y, Kobayashi E, Ohnishi F, Hirai I, Amano K, Tarui R. Structural steel plates for arctic use produced by multipurpose accelerated cooling system. Kawasaki Steel Tech. Report, 1985;No. 13:77-82.
7. Tanigawa O, Ishii H, Itakura N, Amano K, Nakao Y, Kawabata F. 420 MPa and 500 MPa yield strength steel plates with high HAZ toughness produced by TMCP for offshore structures. Kawasaki Steel Tech. Report, 1993;No. 29:54-63.
8. Wang SC, Chiu FJ. The establishment of TMCP process in the plate mill of CSC. China Steel Tech. Report, 1995;No. 9:1-13.
9. Watanabe I, Suzuki M, Tagawa H, Kunisada Y, Yamazaki Y, Iwasaki N. Weld - HAZ, toughness and line heated properties of TMCP steel. Nippon Kokan Tech. Report, Overseas, 1986;No. 47:52-7.
10. Bhadeshia H.K.D.H., Svensson L.E., Gretoft B. A model for the development of microstructure in low-alloy steel weld deposits. Acta Metall. 33(7):1985;1271-1283.
11. Yang J.R., Lion S.H. Microstructural evolution of simulated heat affected zone in ASTM A533 Type B steel plates. Sci. and Tech. of Weld and Join. 2(3):1997;119-12712.
12. Bhadeshia H.K.D.H. Bainite in Steel. 1992;The Institute of Materials, London. 304-14.
13. Beghini M., Bertini L., Vitale E. Fatigue crack growth in residual stress fields: experimental results and modelling. Fatigue Fract. Engng Mater. Struct. 17(12):1994;1433-1444.
14. Shi Y.W., Chen B.Y., Zhang J.X. Effects of welding residual stresses on fatigue crack growth behaviour in butt welds of a pipeline steel. Engng Fract. Mech. 36(6):1990;893-902.
15. Kang K.J., Song J.H., Earmme Y.Y. Fatigue crack growth and closure behavior through a compressive residual stress field. Fatigue Fract. Engng Mater. Struct. 13(1):1990;1-13.