Fracture modeling of bolted connections in wood and composites

Journal of Materials in Civil Engineering

Volumn 11, Issue 4, 1999, Pages 345-352

  Kharouf, N ^a   McClure, G ^a   Smith, I ^b  

^a MCGILL UNIVERSITY   (Canada)

^b UNIVERSITY OF NEW BRUNSWICK   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

BRITTLENESS; CRACK INITIATION; FAILURE ANALYSIS; FIBER REINFORCED MATERIALS; FRACTURE MECHANICS; MATHEMATICAL MODELS; STRESS ANALYSIS; STRESS CONCENTRATION; STRUCTURAL ANALYSIS; WOODEN CONSTRUCTION;

BOLTED CONNECTIONS; BRITTLE FAILURES;

BOLTED JOINTS;

EID: 0033360496     PISSN: 08991561     EISSN: None     Source Type: Journal    
DOI: 10.1061/(ASCE)0899-1561(1999)11:4(345)     Document Type: Article

References (77)

1. Agarwal, B. L. (1980). "Static strength prediction of bolted joints in composite materials." AIAA J., 18(11), 1371-1375.
2. Arnold, W. S., Marshall, I. H., and Wood, J. (1990). "Optimum design considerations for mechanically fastened composite joints." Compos. Struct., 16, 85-101.
3. Ashby, M. F., Easterling, K. E., Harrysson, R., and Maiti, S. K. (1985). "The fracture and toughness of woods." Proc., Royal Soc., London, A398, 261-280.
4. "Australian timber engineering code." (1982). AS 1720-1975, Standards Association of Australia, Sydney, New South Wales.
5. Backlund, J. (1981). "Fracture analysis of notched composites." Comp. and Struct., 13, 145-153.
6. Barrett, J. D. (1981). "Fracture mechanics and the design of wood structures." Philosophical Trans. Royal Soc., London, A299, 217-226.
7. Boatright, S. W., and Garret, G. G. (1983). "The effect of microstructure and stress state on the fracture behavior of wood." J. Mat. Sci., 18, 2181-2199.
8. Borjen, Y., and Schniewind, A. P. (1992). "Elasto-plastic fracture mechanics of wood using the J-integral method." Wood and Fiber Sci., 24(3), 364-376.
9. Bostrom, L. (1994a). "The stress-displacement relation of wood perpendicular to the grain - Part I: Experimental determination of the stress-displacement relation." Wood Sci. and Technol., 28, 309-317.
10. Bostrom L. (1994b). "The stress-displacement relation of wood perpendicular to the grain - Part II: Application of the fictitious crack model to the compact tension specimen." Wood Sci. and Technol., 28, 319-327.
11. Bouchair, A., and Vergne, A. (1995). "An application of the Tsai criterion as a plastic flow law for timber bolted joint modelling." Wood Sci. and Technol., 30, 3-19.
12. Chang, F. K., and Chang, K. Y. (1987). "Post failure analysis of bolted composite joints in tension and shear-out mode of failure." J. Composite Mat., 21, 809-833.
13. Chang, F. K., Scott, R. A., and Springer, G. S. (1984). "Failure of composite laminates containing pin-loaded holes - Method of solution." J. Composite Mat., 18, 255-277.
14. Chiang, Y. J. (1983). "Design of mechanical joints in composites," PhD thesis, Dept. of Mech. Engrg., University of Wisconsin, Madison, Wis.
15. Cote, W. A., and Hanna, R. B. (1983). "Ultrastructural characteristics of wood fracture surfaces." Wood and Fiber Sci., 15(2), 135-163.
16. Daudeville, L., Davenne, L., and Yasumara, M. (1996). "Experimental and numerical analysis of failure in bolted joints." Proc., Int. Wood Engrg. Conf, K. A. Gopu, ed., New Orleans, La., 153-159.
17. De Jong, T. (1977). "Stresses around pin-loaded holes in elastically orthotropic or isotropic plates." J. Composite Mat., 2, 313-331.
18. Eisenmann, J. R. (1975). "Bolted joint static strength model for composite materials." Proc., 3rd Conf. on Fibrous Compos, in Flight Vehicle. Design, Part II, NASA TMX-3377, Williamsburg, Va., 563-602.
19. "Engineering design in wood (limit states design)." (1994). National Standard of Canada CAN/CSA-O86.1-M94, Canadian Standards Association, Rexdale, ON, Canada.
20. Eriksson, I., and Aronsson, C. G. (1990). "Strength of tensile loaded graphite/epoxy laminates containing cracks, open and filled holes." J. Composite Mat., 24, 456-483.
21. Friedrich, K. (1989). "Application of fracture mechanics to composite materials." Composite materials, Elsevier Science, Amsterdam.
22. Gibson, L. J., and Ashby, M. F. (1988). Cellular solids - Structure and properties, Pergamon, Tarrytown, New York.
23. Green, A. E. (1945). "Stresses in aelotropic plates." Proc., Royal Soc., London, A184, 288-301.
24. Griffith, A. A. (1921). "The phenomenon of rupture and flow in solids." Philosophical Trans. Royal Soc., London, A221, 163-197.
25. Guan, Z. G., and Rodd, P. D. (1996). "A simplified FE model for double shear joints made with a hollow dowel fastener." Proc., Int. Wood Engrg. Conf., K. A. Gopu, ed., New Orleans, La., 164-171.
26. Harding, N., and Fawkes, A. H. R. (1984). "Bolted timber joints." Proc., Pacific Timber Engrg. Conf., Pacific TEC New Zealand, 3, 872-882.
27. Irwin, G. R. (1957). "Analysis of stresses and strains near the end of a crack traversing a plate." J. Appl. Mech., 24, 361-364.
28. Jurf, R. A., and Vinson, J. R. (1990). "Failure analysis of bolted joints in composite laminates." Composite materials: Testing and design, ASTM-STP 1059, 165-190.
29. Kanninen, M. F., and Popelar, C. H. (1985). Advanced fracture mechanics. Oxford University Press, New York.
30. Kedward, K. T., and Whitney, J. M. (1990). "Design of joints." Delaware composite design encyclopedia. Vol. 5, Technomic Publishing Co., Lancaster, Pa., 21-43.
31. Kharouf, N., McClure, G., and Smith, I. (1998a). "Stress analysis of single and double-bolt timber connections." Proc., World Conf. on Timber Engrg., J. Natterer and J. L. Sandoz, eds., Montreux, Switzerland, 329-336.
32. Kharouf, N., Tan, D., Smith, I., and McClure, G. (1998b). "Application of fracture theories to predict the strength of bolted timber connections." Proc., World Conf. on Timber Engrg., J. Natterer and J. L. Sandoz, eds., Montreux, Switzerland, 814-816.
33. Lekhnitskii, S. G. (1968). Theory of elasticity of an anisotropic elastic body, Holden-Day, San Francisco.
34. Lessard, L. B., and Shokrieh, M. M. (1995). "Two-dimensional modelling of composite pinned-joint failure." J. Composite Mat., 29, 671-697.
35. Mangalgiri, P. D., and Dattaguru, B. (1986). "A large orthotropic plate with misfit pin under arbitrary oriented biaxial loading." Comp. and Struct., 6, 271-281.
36. Marshall, I. H., Arnold, W. S., Wood, J., and Mously, R. F. (1989). "Observations on bolted connections in composite structures." Compos. Struct., 13, 316-322.
37. Masuda, M. (1998). "Fracture analysis of bolted joints using the finite small area criterion." Proc., World Conf. on Timber Engrg., J. Natterer and J. L. Sandoz, eds., Montreux, Switzerland, 321-328.
38. Matthews, F. L., Wong, C. M., and Chryssafitis, S. (1982). "Stress distribution around a single bolt in fiber-reinforced plastic." Composites, 13, 316-322.
39. Meguid, S. A. (1989). Engineering fracture mechanics. Elsevier Science, New York.
40. Mohammadien, A., Hassan, N. K., and Rizkalla, H. (1996). "Finite element analysis of bolted connections for PFRP composites." Composites, Part B, 27B, 339-349.
41. Moss, P. J. (1984). "Plane stress analysis of a bolted joint in wood." Proc., Pacific Timber Engrg. Conf., Pacific TEC New Zealand, 3, 864-871.
42. Nahas, M. N. (1986). "Survey of failure and post-failure theories of laminated fiber-reinforced composites." J. Compos. Technol. and Res., 8, 138-153.
43. Naik, R. A., and Cruse, J. H. (1986). "Stress analysis method for a clearance fit bolt under bearing loads." AIAA J., 24, 1348-1353.
44. Nuismer, R. J., and Brown, G. E. (1976). "Progressive failure of notched composite laminates using finite elements." Proc., 13th Annu. Meeting of the Soc. of Engrg. Sci., NASA CP 2001, 1, 183-192.
45. Nuismer, R. J., and Tan, S. C. (1989). "A theory for progressive matrix cracking in composite laminates." J. Composite Mat., 23, 1029-1047.
46. Nuismer, R. J., and Whitney, J. M. (1975). "Uniaxial failure of composite laminates containing stress concentrations." Fracture of Compos. Mat., ASTM STP 593, 117-142.
47. Owen, D. R. J., and Fawkes, A. J. (1983). Engineering fracture mechanics: Numerical methods and applications, Pineridge, Swansea, U.K.
48. Papaspyropoulos, V., Ahmad, J., and Kanninen, M. F. (1984). "A micro-mechanical fracture mechanics analysis of a fiber composite laminate containing a defect." Effect of Defects in Composite Materials, ASTM STP 836, 237-249.
49. Parhizgar, S., Zachary, L. W., and Sun, C. T. (1982). "Applications of the principles of linear fracture mechanics to the composite materials." Int. J. Fracture, 20, 3-15.
50. Patton-Mallory, M., Pellicane, P. J., and Smith I. W. (1997a). "Modelling bolted connections in wood: Review." J. Struct. Engrg., ASCE, 123(8), 1054-1062.
51. Patton-Mallory, M., Pellicane, P. J., and Smith, I. W. (1997b). "Nonlinear material models for analysis of bolted wood connections." J. Struct. Engrg., ASCE, 123(8), 1063-1070.
52. Patton-Mallory, M., and Cramer, S. M. (1984). "Fracture mechanics: A tool for predicting wood component strength." Forest Products J., 37(7/8), 39-47.
53. Petterson, R. W., and Bodig, J. (1983). "Prediction of fracture toughness of conifers." Wood and Fiber Sci., 15(4), 302-316.
54. Porter, A. W. (1964). "On the mechanics of fracture in wood." Forest Products J., 14(8), 325-331.
55. Rahman, M. U. (1981). "Stress and strength analysis of double-bolted mechanical joints in orthotropic materials," PhD thesis, Dept. of Mech. Engrg., University of Wisconsin, Madison, Wis.
56. Rahman, M. U., Chiang, Y. J., and Rowlands, R. E. (1991). "Stress and failure analysis of double bolted joints in Douglas-fir and Sitkaspruce." Wood and Fiber Sci., 23(4), 567-589.
57. Rahman, M. U., and Rowlands, R. E. (1993). "Finite element analysis of multiple joints in orthotropic plates." Comp. and Struct., 46, 859-867.
58. Ramamurthy, T. S. (1989). "Recent studies of the behavior of interference fit pins in composite plates." Comp. and Struct., 13, 81-99.
59. Rowlands, R. E., Rahman, M. U., Wilkinson, T. L., and Chiang, Y. J. (1982). "Single and multiple-bolted joints in orthotropic materials." Composites, 13, 273-380.
60. Schniewind, A. P., and Lyon, D. E. (1973). "A fracture mechanics approach to the tensile strength perpendicular to grain of dimension lumber." Wood Sci. and Technol., 7, 45-59.
61. Schulz, K. C., Packman, P. F., and Eisenmann, J. R. (1995). "A tension-mode fracture model for bolted joints in laminated composites." J. Composite Mat., 29, 37-59.
62. Shokrieh, M., and Lessard, L. B. (1996). "Effects of material nonlinearity on the three-dimensional stress state of pin-loaded composite laminates." J. Composite Mat., 30(7), 839-861.
63. Smith, I., and Chui, Y. H. (1994). "Factors affecting mode I fracture of plantation grown red pine." Wood Sci. and Technol., 28, 144-157.
64. Smith, I., Chui, Y. H., and Hu, J. (1996). "Reliability analysis for critical reaction forces of lumber members with end notch." Can. J. Civ. Engrg., 23, 202-210.
65. Smith, I., and Hu, L. J. (1994). "Fracture analysis of bolted timber connections." Proc., ASCE Struct. Congr., ASCE, N.Y., 912-917.
66. Soni, S. R. (1981). "Failure analysis of composite laminates with a fastener hole." Joining of composite materials, ASTM STP 749, 145-164.
67. Stanzl-Tschegg, S. E., Tan, D. M., and Tschegg, E. K. (1995). "New splitting method for wood fracture characterization." Wood Sci. and Technol., 29, 31-50.
68. Tan, D. M., Stanzl-Tschegg, S. E., and Tschegg, E. K. (1995). "Models of wood fracture in Mode I and Mode II." Holz als Roh-und Werkstoff, 53, 159-164.
69. Valentin, G., Bostrom, L., Gustafsson, P. G., Ranta-Maunus, A., and Gowda, W. (1991). "Application of fracture mechanics to timber structures RILEM state of the art report." Tech. Rep. Res. Notes 1262, Technical Research Center of Finland, Espoo, Finland.
70. Vasic, S., and Smith, I. (1996). "The brittleness of wood in tension perpendicular to the grain: Micro-mechanical aspects." Proc., Int. COST 508 Wood Mech. Conf, 556-569.
71. Vasic, S., and Smith, I. (1998). "Bridged crack model of wood fracture: Experimental analysis and numerical modeling." Proc., World Conf. on Timber Engrg., COST 508, Stuttgart, Germany, 818-820.
72. Waddoups, M. E., and Kaminski, B. E. (1971). "Macroscopic fracture mechanics of advanced composite materials." J. Compos. Mat., 5, 446-455.
73. Wazczak, J. P., and Cruse, T. A. (1971). "Failure mode and strength prediction of anistropic bolt bearing specimen. J. Comp. Mat., 5, 421-425.
74. Wilkinson, T. L. (1978). "Stresses in the neighborhood of loaded holes in wood with application to bolted joints," PhD thesis, Dept. of Mech. Engrg., University of Wisconsin, Madison, Wis.
75. Wilkinson, T. L., and Rowlands, R. E. (1981). "Analysis of mechanical joints in wood." Experimental Mech., 21, 408-414.
76. Wilkinson, T. L., Rowlands, R. E., and Cook, R. D. (1981). "An incremental finite element determination of stresses around loaded holes in wood plates." Comp. and Struct., 14, 123-128.
77. Wu, E. M. (1967). "Application of fracture mechanics to anisotropic plates." J. Appl. Mech., 34, 967-974.