Preparation of self-assembled cobalt nanocrystal arrays

Nanostructured Materials

Volumn 11, Issue 7, 1999, Pages 845-852

  Yin, J S ^a   Wang, Z L ^a  

^a Georgia Institute of Technology   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

COBALT; CRYSTAL WHISKERS; DRYING; MAGNETIC FIELD EFFECTS; NANOSTRUCTURED MATERIALS; PARTICLE SIZE ANALYSIS; PYROLYSIS; TOLUENE;

SELF-ASSEMBLED COBALT NANOCRYSTAL ARRAYS;

MAGNETIC MATERIALS;

EID: 0033340927     PISSN: 09659773     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0965-9773(99)00375-X     Document Type: Article

References (27)

1. Brus L. Appl. Phys. A. 53:1991;465.
2. Alivisatos A.P. Science. 271:1996;933.
3. Stupp S.I., LeBonheur V., Walker K., Li L.S., Huggins K.E., Keser M., Amstutz A. Science. 276:1997;384.
4. Wang Z.L. Adv. Mater. 10:1998;13.
5. Ahmadi T.S., Wang Z.L., Green T.C., Henglein A., El-Sayed M.A. Science. 28:1996;1924.
6. Luedtke W.D., Landman U. J. Phys. Chem. B. 100:1996;13323.
7. Billas I.M.L., Chatelain A., de Heer W.A. Science. 265:1994;1682.
8. Harfenist S.A., Wang Z.L., Whetten R.L., Vezmar I., Alvarez M.M. J. Phys. Chem. B. 100:1996;13904.
9. Ohara P.C., Heath J.R., Gelbart W.M. Angew. Chem. Int. Ed. Engl. 36:1997;1078.
10. Andres R.P., Bielefeld J.D., Henderson J.I., Janes D.B., Kolagunta V.R., Kubiak C.P., Mahoney W.J., Osifchin R.G. Science. 273:1996;1690.
11. Whetten R.L., Khoury J.T., Alvarez M.M., Murthy S., Vezmar I., Wang Z.L., Cleveland C.C., Luedtke W.D., Landman U. Adv. Mater. 8:1996;429.
12. Bentzon M.D., Van Wonterghem J., Morup S., Thölen A., Koch C.J.W. Phil. Mag. B. 60:1989;169.
13. Yin J.S., Wang Z.L. J. Mater. Res. 14:1999;503.
14. Yin J.S., Wang Z.L. Phys. Rev. Lett. 79:1997;2570.
15. Yin J.S., Wang Z.L. J. Phys. Chem. B. 101:1997;8979.
16. Murray C.B., Kagan C.R., Bawendi M.G. Science. 270:1995;1335.
17. Numazawa J., Ohshima H. J. Magn. Magn. Mater. 176:1997;1.
18. Sun S., Murray C.B. J. Appl, Phys. 85:1999;4325.
19. S. Sun and C. B. Murray, in Abstracts of the MRS Fall Meeting (1997).
20. Thomas J.R. J. Appl. Phys. 37:1966;2914.
21. Jacobs I.S., Bean C.P. Phys. Rev. 100:1955;1060.
22. Griffiths C.H., O'Horo M.P., Smith T.W. J. Appl. Phys. 50:1979;7108.
23. Hayashi T., Hirono S., Tomita M., Umemura S. Nature. 381:1996;772.
24. J. P. Chen, K. M. Lee, C. M. Sorensen, K. J. Klabunde, and G. C. Hadjipanayis, J. Appl. Phys. 75, 5876 (1994); J. P. Chen, C. M. Sorensen, K. J. Klabunde, and G. C. Hadjipanayis, Phys. Rev. B. 51, 11527 (1995).
25. J. P. Chen, K. M. Lee, C. M. Sorensen, K. J. Klabunde, and G. C. Hadjipanayis, J. Appl. Phys. 75, 5876 (1994); J. P. Chen, C. M. Sorensen, K. J. Klabunde, and G. C. Hadjipanayis, Phys. Rev. B. 51, 11527 (1995).
26. Papiper E., Horny P., Balard H., Anthore R., Petipas C., Martinet A. J. Colloid Interface Sci. 94:1983;207.
27. The alternating magnetic field was generated by a magnetic stirrer during the synthesis. The strength and frequency of the field is equivalent to the rotating speed of the stirrer of ~ 120 rpm.