Effect of biaxial strain ratio and periodic compressive overstrains on fatigue crack growth mode and crack growth rate

ASTM Special Technical Publication

Volumn , Issue 1360, 1999, Pages 299-312

  Varvani Farahani, A ^a   Topper, T H ^b  

^a RYERSON UNIVERSITY   (Canada)

^b UNIVERSITY OF WATERLOO   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

COMPRESSIVE STRENGTH; CRACK PROPAGATION; FATIGUE TESTING; MICROSCOPIC EXAMINATION; STEEL TESTING;

BIAXIAL STRAIN RATIO; COMPRESSIVE OVERSTRAIN; CONFOCAL SCANNING LASER MICROSCOPY;

FATIGUE OF MATERIALS;

EID: 0033331804     PISSN: 10403094     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (14)

1. Parson, M. W. and Pascoe, K. J., "Observations of Surface Deformation, Crack Initiation and Crack Growth in Low-cycle Fatigue under Biaxial Stress," Material Science Engineering, Vol. 22, 1976, pp. 31-50.
2. Brown, M. W. and Miller, K. J., "A Theory for Fatigue Failure under Multiaxial Stress-Strain Conditions," Proceedings of the Institution Mechanical Engineering, Vol. 187, 1973, pp. 745-755.
3. Socie, D., "Critical Plane Approaches for Multiaxial Fatigue Damage Assessment," Advances in Multiaxial Fatigue, ASTM STP 1191, D. L. McDowell, and R. Ellis, Eds., American Society for Testing and Materials, Philadelphia, PA, 1993, pp. 7-63.
4. Varvani-Farahani, A. and Topper, T. H., "The Effect of Periodic Compressive Overstrain Excursions on Crack Closure and Crack Growth Rates of Short Fatigue Cracks-Measurements and Modelling," Advances in Fatigue Crack Closure Measurements and Analysis, ASTM STP 1343, accepted for publication, 1999.
5. Varvani-Farahani, A. and Topper, T. H., "Crack Growth and Closure Mechanisms of Shear Cracks under Constant Amplitude Biaxial Straining and Periodic Compressive Overstraining in 1045 Steel," International Journal of Fatigue, Vol. 19, No. 7, 1997, pp. 589-596.
6. Varvani-Farahani, A., Topper, T. H., and Plumtree, A., "Confocal Scanning Laser Microscopy Measurements of the Growth and Morphology of Microstructurally Short Fatigue Cracks in Al 2024-T351 Alloy," Fatigue and Fracture of Engineering Materials and Structure, Vol. 19, No. 9, 1996, pp. 1153-1159.
7. Varvani-Farahani, A. and Topper, T. H., "Short Fatigue Crack Characterization and Detection using Confocal Scanning Laser Microscopy (CSLM)," Nontraditional Methods of Sensing Stress, Strain and Damage in Materials and Structures, ASTM STP 1318, G. F. Lucas and D. A. Stubbs, Eds., American Society for Testing and Materials, West Conshohocken, PA, 1997, pp. 43-55.
8. Marco, S. M. and Starkey, W. L., "A Concept of Fatigue Damage," Transactions of ASME, Vol. 76, 1954, pp. 627-632.
9. Henkener, J. A., Scheumann, T. D., and Grandt, A. F., "Fatigue Crack Growth Behaviour of Peakaged Al-2.6Li-0.09Zr Alloy," Proceedings, Fourth International Conference on Fatigue and Fracture Threshold, 1990, pp. 957-962.
10. Herman, W. A., Hertzberg, R. W., and Jaccard, R., "Prediction and Simulation of Fatigue Crack Growth under Conditions of Low Cycle Closure," Proceedings, Advance Fracture Research, 7th International Conference on Fracture, 1989, p. 1417.
11. maxΔK-decreasing Fatigue Crack Growth Procedures" Small-Crack Test Methods, ASTM STP 1149, American Society for Testing and Materials, Philadelphia, PA, 1992, pp. 197-220.
12. Kemper, H., Weiss, B., and Stickler, R., "An Alternative Prediction of the Effect of the Stress-Ratio on the Fatigue Threshold," Engineering and Fracture Mechanics, Vol. 4, 1989, pp. 591-600.
13. Tack, A. J. and Beevers, C. J., "The Influence of Compressive Loading on Fatigue Crack Propagation in three Aerospace Bearing Steels," Proceedings, Fourth International Conference on Fracture and Fatigue Thresholds, 1990, pp. 1179-1184.
14. Varvani-Farahani, A., "Biaxial Fatigue Crack Growth and Crack Closure under Constant Amplitude and Periodic Compressive Overload Histories in 1045 Steel," A Ph.D. thesis, University of Waterloo, Canada, 1998.