Use of forces from instrumented Charpy V-notch testing to determine crack-arrest toughness

ASTM Special Technical Publication

Volumn , Issue 1325, 1999, Pages 204-222

  Iskander, S K ^a   Nanstad, R K ^a   Sokolov, M A ^a   McCabe, D E ^a   Hutton, J T ^b   Thomas, D L ^b  

^a OAK RIDGE NATIONAL LABORATORY   (United States)

^b NONE

Author keywords

[No Author keywords available]

Indexed keywords

BRITTLE FRACTURE; BRITTLENESS; CRACKS; EMBRITTLEMENT; FRACTURE TOUGHNESS; MECHANICAL VARIABLES MEASUREMENT; PRESSURE VESSELS; RADIATION EFFECTS; STEEL STRUCTURES; TEMPERATURE;

CHARPY V NOTCH TESTING; CRACK ARREST TOUGHNESS; IRRADIATION EMBRITTLEMENT; NIL DUCTILITY TRANSITION TEMPERATURE; REACTOR PRESSURE VESSEL STEELS;

MECHANICAL TESTING;

EID: 0033331083     PISSN: 10403094     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1520/stp13865s     Document Type: Conference Paper

References (13)

1. Ic curves for High-Copper Welds," pp. 214-233 in Effects of Radiation on Materials, 14th International Symposium, (Volume II), ASTM STP 1046, N. H. Packan, R. E. Stoller, and A. S. Kumar, Eds., American Society for Testing and Materials, Philadelphia, 1990.
2. Iskander, S. K., Corwin, W. R., and Nanstad, R. K., Nanstad, "Effects of Irradiation on Crack-Arrest Toughness of Two High-Copper Welds," pp. 251-269 in Effects of Radiation on Materials: 15th International Symposium, ASTM STP 1125, R. E. Stoller, A. S. Kumar, and D. S. Gelles, Eds., American Society for Testing and Materials, Philadelphia, 1992.
3. Iskander, S. K., Corwin, W. R., and Nanstad, R. K., "Effects of Irradiation on Crack-Arrest Toughness of Two High-Copper Welds," pp. 251-269 in Effects of Radiation on Materials: 15th International Symposium, ASTM STP 1125, R. E. Stoller, A. S. Kumar, and D. S. Gelles, Eds., American Society for Testing and Materials, Philadelphia, 1992.
4. NDT Determinations for Midland Weld WF-70, NUREG/CR-5914 (ORNL-6740), Oak Ridge National Laboratory, Oak Ridge, Tenn., December 1992.
5. Vasoukis, G. "Fraktographie und Analyse der Kerbschlagbiegeversuchs" (Doctoral Dissertation), Universität Stuttgart, 1971.
6. Schoch, F-W, "Eigenschaften formgeschweisster Grossgauteile: Werkstoffuntersuchungen an einem 72 t Versuchskörper aus Schweissgut 10MnMoNi55" (Doctoral Dissertation), Universität Stuttgart, 1984.
7. Ia, VTT-MET B-221, Metals Laboratory, Technical Research Centre of Finland, Espoo, Finland, January 1993.
8. McCabe, D. E., Nanstad, R. K., Iskander, S. K., and Swain, R. L., Unirradiated Material Properties of Midland Weld WF-70, NUREG/CR-6249 (ORNL/TM-12777), Oak Ridge National Laboratory, Oak Ridge, Tenn., October 1994.
9. Berggren, R. G., Stelzman, W. J., and Jones, T. N., "Studies of Impact and Slow-Bend Charpy-Type Specimens," pp. 20-30 in Heavy-Section Steel Technology Program Semiann. Prog. Rep. for Period Ending February 28, 1970, ORNL-4590, Oak Ridge National Laboratory, Oak Ridge, Tenn., October 1970.
10. Stelzman, W. J., and Berggren, R. G., Fig. 14 in Radiation Strengthening and Embrittlement in Heavy-Section Steel Plates and Welds, ORNL-4871, Oak Ridge National Laboratory, Oak Ridge, Tenn., June 1973.
11. Iskander, S. K., Corwin, W. R., and Nanstad, R. K., Crack-Arrest Tests on Two Irradiated High-Copper Welds. Phase II: Results of Duplex-Type Specimens, NUREG/CR-6139 (ORNL/TM-12513), Oak Ridge National Laboratory, Oak Ridge, Tenn., March 1994.
12. McCabe, D. E., Nanstad, R. K., Iskander, S. K., and Swain, R. L., Unirradiated Material Properties of Midland Weld WF-70, NUREG/CR-6249 (ORNL/TM-12777), Oak Ridge National Laboratory, Oak Ridge, Tenn., October 1994.
13. Naus, D. J., Keeney-Walker, J., Bass, B. R., Robinson, Jr., G. C., Jr., Iskander, S. K., Fields, R. J., deWit, R., Low, S. R., Schwartz, C. W., Alexander, D. J., and Johansson, I.-B., Crack-Arrest Behavior in SEN Wide-Plates of Low-Upper-Shelf Base Metal Tested Under Nonisothermal Conditions: WP-2 Series, NUREG/CR-5451 (ORNL-6584), Oak Ridge National Laboratory, Oak Ridge, Tenn., August 1990.