Influences of thermal cycling and low-energy impact on the fatigue behavior of carbon/PEEK laminates

Composites Part B: Engineering

Volumn 30, Issue 8, 1999, Pages 849-865

  Tai, Nyan Hwa ^a   Yip, Ming Chuen ^a   Tseng, Chih Ming ^a  

^a NATIONAL TSING HUA UNIVERSITY   (Taiwan)

Author keywords

[No Author keywords available]

Indexed keywords

CARBON FIBER REINFORCED PLASTICS; FATIGUE TESTING; MORPHOLOGY; PLASTIC LAMINATES; POLYETHER ETHER KETONES; RESIDUAL STRESSES; SCANNING ELECTRON MICROSCOPY; STIFFNESS; TENSILE STRENGTH; THERMAL CYCLING; THERMAL STRESS; WEIBULL DISTRIBUTION;

LOW ENERGY IMPACT LOADING;

LAMINATED COMPOSITES;

EID: 0033329032     PISSN: 13598368     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1359-8368(99)00048-7     Document Type: Article

References (29)

1. Curtis P.T. The fatigue behavior of fibrous composite materials. J Strain Anal. 24:(4):1989;235-244.
2. Lee L.J., Yang J.N., Sheu D.Y. Prediction of fatigue life for matrix-dominated composite laminates. Compos Sci Technol. 46:1993;21-28.
3. Rotem A. Load frequency effect on the fatigue strength of isotropic laminates. 1993;46:129-138.
4. Harris B., Reiter H., Adam T., Dickson R.F., Fernando G. Fatigue behavior of carbon fiber reinforced plastics. Composites. 21:(3):1990;232-242.
5. Hahn H.T., Hwang D.G. Failure characterization of a graphite/epoxy laminate through proof testing. Daniel I.M. Composite materials: testing and design. ASTM STP 787. 1982;247-273 American Society for Testing and Materials.
6. Spearing S.M., Beaumont P.W.R. Fatigue damage mechanics of composite materials. Part III. Prediction of post-fatigue strength. Composite Science and Technology. 44:1992;299-307.
7. Curtis D.C., Moore D.R., Slater B., Zahlan N. Fatigue testing of multi-angle laminates of CF/PEEK. Composite. 19:(6):1988;446-452.
8. Buggy M., Dillon G. Flexural fatigue of carbon fiber-reinforced PEEK laminates. Composites. 22:(3):1991;191-198.
9. Henaff-Gardin C., Lafarie-Frenot M.C. Fatigue behaviour of thermoset and thermoplastic cross-ply laminates. Composites. 23:(2):1992;109-116.
10. Newaz G.M., Lustiger A., Yang J.N. Delamination growth under cyclic loading at elevated temperature in thermoplastic composites. Newaz G.M. Advances in thermoplastic matrix composite materials. ASTM STP 1044. 1989;264-278 American Society for Testing and Materials.
11. Tai N.H., Ma C.C.M., Wu S.H. Fatigue behaviour of carbon fibre/PEEK laminate composites. Composites. 26:(8):1995;551-559.
12. Diao X., Ye L., Mai Y.W. Fatigue behaviour of CF/PEEK composite laminates made from commingled prepreg. Part I: Experimental studies. Composites A. 28:1997;739-747.
13. Finn S.R., He Y.F., Springer G.S. Delaminations in composite plates under transverse impact loads - experimental results. Compos Struct. 23:1993;191-204.
14. Strait L.H., Karasek M.L., Amateau M.F. Effects of stacking sequence on the impact resistance of carbon fiber reinforced thermoplastic toughened epoxy laminates. J Compos Mater. 26:(12):1992;1725-1740.
15. Delfosse D., Poursartip A. Energy-based approach to impact damage in CFRP laminates. Composites A. 28:1997;647-655.
16. Caprino G., Visconti I.G., Ilio A.D. Composite materials response under low-velocity impact. Compos Struct. 2:1984;261-271.
17. Wu E., Shyu K. Response of composite laminates to contact loads and relationship to low-velocity impact. J Compos Mater. 27:(15):1993;1443-1464.
18. Razi H., Kobayashi A.S. Delamination in cross-ply laminated composite subjected to low-velocity impact. AIAA J. 31:(8):1993;1498-1502.
19. Choi H.Y., Chang F.K. A model for predicting damage in graphite/epoxy laminated composites resulting from low-velocity point impact. J Compos Mater. 26:(14):1992;2134-2169.
20. Ramkumar R.L. Effect of low-velocity impact damage on the fatigue behavior of graphite/epoxy laminates. O'Brien T.K. Long-term behavior of composite. ASTM STP 813. 1983;116-135 American Society for Testing and Materials.
21. Tai N.H., Yip M.C., Lin J.L. Effects of low-energy impact on fatigue behavior of the carbon/epoxy composites. Compos Sci Technol. 58:(1):1998;1-9.
22. Spera D.A. What is thermal fatigue. Spera D.A., Mowbray D.F. Thermal fatigue of materials and composites. ASTM STP 612. 1976;3-9 American Society for Testing and Materials.
23. Hasselman D.P., Badaliance R., Chen E.P. Spera D.A., Mowbray D.F. Thermal fatigue of materials and composites. ASTM STP 612. 1976;55-68 American Society for Testing and Materials.
24. Wetherhold R.C., Westfall L.J. Thermal cycling on tungsten-fiber-reinforced superalloy composites. J Mater Sci. 23:1988;713-717.
25. Mall S., Ermer P.G. Thermal fatigue behavior of a unidirectional SCS/Ti-15-3 metal matrix composite. J Compos Mater. 25:1991;1668-1686.
26. Walker G., Crow W., Taya M. Long term thermal cycling of SCS-6/Ti-15-3 metal matrix composite. Proc ICCM-10. 2:1995;711-718.
27. Herakovich C.T., Hyer M.W. Damage-induced property changes in composites subjected to cyclic thermal loading. Engng Fracture Mech. 25:(5/6):1986;779-791.
28. Whitney J.M. Fatigue characterization of composite materials, ASTM STP 723. 1981;American Society for Testing and Materials. p. 131-151.
29. Kline R.A., Chang F.H. Composite failure surface analysis. J Compos Mater. 14:1980;315-324.