Effects of a single tensile overload on fatigue crack growth in a 316L steel

Fatigue and Fracture of Engineering Materials and Structures

Volumn 22, Issue 12, 1999, Pages 1041-1051

  Wheatley, G ^a   Hu, X Z ^a   Estrin, Y ^a  

^a UNIVERSITY OF WESTERN AUSTRALIA   (Australia)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK PROPAGATION; FATIGUE TESTING; PLASTIC DEFORMATION; SCANNING ELECTRON MICROSCOPY; STRAIN HARDENING; TENSILE STRESS;

FIELD EMISSION SCANNING ELECTRON MICROSCOPY (FESEM); SINGLE TENSILE OVERLOAD;

STAINLESS STEEL;

EID: 0033310824     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1046/j.1460-2695.1999.00225.x     Document Type: Article

References (23)

1. D. Damri and J. F. Knott (1993) Fracture modes encountered following the application of a major tensile overload. Int. J. Fatigue 15, 53-60.
2. Y. Lu and K. Li (1993) A new model for fatigue crack growth after a single overload. Engng Fracture Mech. 46, 849-856.
3. D. M. Shuter and W. Geary (1996) Some aspects of fatigue crack retardation behaviour following tensile overloads in a structural steel. Fatigue Fract. Engng Mater. Struct. 19, 185-199.
4. C. M. Ward-Close, A. F. Blom and R. O. Ritchie (1989) Mechanisms associated with transient fatigue growth under variable-amplitude loading: an experimental and numerical study. Engng Fracture Mech. 32, 613-638.
5. R. H. Dauskardt, B. J. Dalgleish, D. Yao, R. O. Ritchie and P. F. Becher (1993) Cyclic fatigue-crack propagation in a silicon carbide whisker-reinforced alumina composite: role of load ratio. J. Mater. Sci. 28, 3258-3266.
6. S. Suresh and R. O. Ritchie (1984) Propagation of short fatigue cracks. Int. Metall. Rev. 29, 445-476.
7. R. H. Dauskardt, R. O. Ritchie and B. N. Cox (1993) Fatigue of advanced materials: Part I. Adv. Mater. Processes 7, 26-30.
8. R. O. Ritchie (1988) Mechanisms of fatigue crack propagation in metals, ceramics and composites: role of crack tip shielding. Mater. Sci. Engng A103, 15-28.
9. J. K. Shang, J.-L. Tzou and R. O. Ritchie (1987) Role of crack tip shielding in the initiation and growth of long and small fatigue cracks in composite microstructures. Metall. Trans. 18A, 1613-1626.
10. C.-Y. Hou and J.-J. Charng (1996) Estimation of plasticity-induced crack closure in a pre-existing plastic zone. Int. J. Fatigue 18, 463-474.
11. H. Tsukuda, H. Ogiyama and T. Shiraishi (1996) Transient fatigue crack growth behaviour following single overloads at high stress ratios. Fatigue Fract. Engng Mater. Struct. 19, 879-891.∼.
12. G. Wheatley, R. Niefanger, Y. Estrin and X. Z. Hu (1998) Fatigue crack growth in 316L stainless steel. Key Engng Mater. 145-149, 631-636.
13. W. Elber (1971) The significance of fatigue crack closure in damage tolerance in aircraft structures. ASTM STP 486, 230-242.
14. O. E. Wheeler (1972) Spectrum loading and crack growth. J Bas. Engng 4, 181-186.
15. S. Suresh (1998) Fatigue of Materials, Cambridge University Press, Cambridge.
16. C. S. Shin and S. H. Hsu (1993) On the mechanisms and behaviour of overload retardation in AISI 304 stainless steel. Int. J. Fatigue. 15, 181-192.
17. J. D. Dougherty, T. S. Srivatsan and J. Padovan (1997) Fatigue crack propagation and closure behaviour of modified 1070 steel: experimental results. Engng Fracture Mech. 56, 167-187.
18. X. Z. Hu and Y. W. Mai (1992) A general method for determination of crack-interface bridging stresses. J. Mater. Sci. 27, 3502-3510.
19. X. Z. Hu and Y. W. Mai (1992) Crack-bridging analysis for alumina ceramics under monotonic and cyclic loading. J. Amer. Ceram. Soc. 75, 848-853.
20. X. Z. Hu (1992) Influence of crack-tip shielding on fatigue crack growth in ceramic materials. In: Proceedings of the International Ceramic Conference (AUSTCERAM 92) (Edited by M. J. Bannister), Melbourne, Vol. 2, pp. 870-875.
21. R. Kumar, A. Kumar and K. Singh (1996) Effect of rest time after application of single overload cycle on fatigue life. Engng Fracture Mech. 54, 147-153.
22. G. Wheatley, Y. Estrin, X. Z. Hu and Y. Bréchet (1998) Effect of low cycle fatigue on subsequent high cycle fatigue life of 316L stainless steel. Mater. Sci. Engng 254, 315-316.
23. G. Wheatley, Y. Estrin, X. Z. Hu and Y. Bréchet (1998) Interaction between low cycle fatigue and high cycle fatigue in 3161 stainless steel. In: Proceedings of the Fourth International Conference on Low Cycle Fatigue and Elasto-Plastic Behaviour of Materials, Garmisch-Partenkirchen, Germany, pp. 567-572. Elsevier Science, The Netherlands.