Polymer interdiffusion vs cross-linking in carboxylic acid-carbodiimide latex films

Macromolecules

Volumn 32, Issue 22, 1999, Pages 7692-7695

  Pham, Hung H ^a   Winnik, Mitchell A ^a  

^a UNIVERSITY OF TORONTO   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

CARBOXYLIC ACIDS; COPOLYMERS; CROSSLINKING; DISPERSIONS; FOURIER TRANSFORM INFRARED SPECTROSCOPY; INTERDIFFUSION (SOLIDS); LATEXES; PLASTIC FILMS;

CARBODIIMIDE; POLYETHYLHEXYL METHACRYLATE;

ORGANIC POLYMERS;

EID: 0033228340     PISSN: 00249297     EISSN: None     Source Type: Journal    
DOI: 10.1021/ma990677a     Document Type: Article

References (36)

1. (a) Winnik, M. A.; Feng, J. J. Coat. Technol. 1996, 68 (852), 39.
2. (b) Feng, J.; Winnik, M. A.; Shivers, T.; Clubb, B. Macromolecules 1995, 28, 7671.
3. Eckersley, S. T.; Helmer, B. J. J. Coat. Technol. 1997, 69 (864), 97.
4. Winnik, M. A. Curr. Opin. Colloid In. 1997, 2 (2), 192.
5. Keddie, J. L. Mater. Sei. Eng. 1997, 21, 101.
6. Taylor, J. W. PMSE publication, 1999.
7. Wicks, Z. W., Jr. Film Formation; Federation Series on Coatings Technology: Blue Bell, PA, 1986.
8. Buffkin, B. G.; Grawe, J. R. J. Coat. Technol. 1978,50 (641), 41.
9. Pichot, C. Makromol. Chem., Macromol. Sym. 1990,35/36, 327
10. Park, Y. J.; Kim, J. H. Polym. Eng. Sei. 1998, 35 (6), 884.
11. Mohammed, S.; Daniels, E. S.; Sperling, L. H.; Klein, A.; El-Aasser, M. S. J. Appl. Polym. Sei. 1997, 66, 1869.
12. Xu, J.; Dimonie, V. L.; Sudol, D. E.; Shaffer, O. L.; El-Aasser, M. S. J. Appl. Polym. Sei. 1998, 69, 977.
13. Yoo, S.; Harelle, L.; Daniels, E. S.; El-Aasser, M. S.; Klein, A. J. Appl. Polym. Sei. 1995, 58, 367.
14. Hill, L. W. Mechanical Properties of Coatings; Federation Series on Coatings Technology: Blue Bell, PA, 1987.
15. Winnik, M. A.; Pinenq, P.; Krüger, C.; Zhang, J.; YanefT, P. J. Coat. Technol. 1997, 71 (892), 47.
16. Feng, J. R.; Pham, H. H.; Macdonald, P.; Winnik, M. A.; Guerts, J. M.; Zirkzee, H.; van Es, J. J. G. S.; German, A. L. J. Coat. Technol. 1998, 70 (881), 57.
17. Zosel, A.; Ley, G. Macromolecules 1993, 26, 2222.
18. Geurts, J. M.; van Es, J. J. G. S.; German, A. L. Prog. Org. Coat. 1996, 29 (1-4), 107.
19. Mohammed, S.; Daniels, E. S.; Sperling, L. H.; Klein, A.; El-Aasser, M. S. J. Appl. Polym. Sei. 1997, 66, 1869.
20. Dolphin, D.; Wick, A. Tabulation of Infrared Spectral Data; A Wiley-Interscience Publication: New York, 1977.
21. (a) Feng, J. R.; Pham, H. H.; Macdonald, P.; Winnik, M. A.; Geurts, J. M.; Zirkzee, H.; van Es, J. J. G. S.; German, A. L. J. Coat. Technol. 1998, 70 (881), 57.
22. (b) Odrobina, E.; Feng, J. R.; Kawaguchi, S.; Winnik, M. A.; Neag, M.; Meyer, E. F. Macromolecules 1998, 31, 7239.
23. Feng, J. R.; Odrobina, E.; Winnik, M. A. Macromolecules 1998,31,5290.
24. Feng, J. R.; Winnik, M. A. Macromolecules 1997, 30, 4324.
25. (e) Kawaguchi, S.; Odrobina, E.; Winnik, M. A. Macromol. Rapid Commun. 1995, 16, 861.
26. Brandrup, J., Immergnt, E. H., Eds. Polymer Handbook, 3rd ed.; John Wiley & Sons: New York, 1989.
27. Feng, J. R.; Pham, H. H.; Stoeva, V.; Winnik, M. A. J. Polym. Sei., Part B: Polym. Phys. 1998, 36, 1129.
28. Pham, H. H.; Winnik, M. A. J. Polym. Sei., Part A: Polym. Chem., in press.
29. Xu, Z.; Lu, G.; Cheng, S.; Li, L. J. Appl. Polym. Sei. 1995, 56, 575.
30. Versiegen, J. M. G. Ph.D. Thesis, University of Eindhoven, 1998.
31. When the dry latex film is annealed at 60 °C, no significant loss of the -N = C = N- group can be detected over a period of 30 h. We do see the loss of 4% in 40 h if the film is annealed at 80 °C.
32. Taylor, J. W.; Collins, M. J.; Bassett, D. R. Prog. Org. Coat. 1999. 35, 215.
33. -1.
34. Taylor, J. W.; Bassett, D. R. ACS Symp. Ser. 1997,663,137.
35. We find that 14% of the -N = C = N- is lost during solvent casting and drying of the film. This process takes about 10 min.
36. Pham, H. H.; Farinha, J. P. S.; Winnik, M. A., to be submitted for publication.