The mode of stress corrosion cracking in Ni-base alloys in high temperature water containing lead

Journal of Nuclear Materials

Volumn 275, Issue 1, 1999, Pages 28-36

  Hwang, Seong Sik ^a   Kim, Hong Pyo ^a   Lee Hyun, Deok ^a   Kim, Uh Chul ^a   Kim, Joung Soo ^a  

^a Korea Atomic Energy Research Institute   (South Korea)

Author keywords

[No Author keywords available]

Indexed keywords

CORROSION RESISTANCE; CRACKS; DISLOCATIONS (CRYSTALS); GRAIN BOUNDARIES; HEAT TREATMENT; HIGH TEMPERATURE OPERATIONS; LEAD; PH EFFECTS; SOLUTIONS; STRAIN RATE; STRESS CORROSION CRACKING; STRESS RELAXATION;

C-RINGS; CRACK LENGTH; INTERGRANULAR STRESS CORROSION CRACKING; SLOW STRAIN RATE TESTING; TRANSGRANULAR STRESS CORROSION CRACKING;

NICKEL ALLOYS;

EID: 0033204342     PISSN: 00223115     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0022-3115(99)00111-7     Document Type: Article

References (15)

1. A.K. Agrawal, J.P.N. Paine, Lead cracking of Alloy 600-A review, in: Proceedings of the Fourth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Jekyll Island, Georgia, USA, 6-10 August, 1989, p. 71.
2. S.S. Hwang, J.S. Kim, U.C. Kim, Failure analysis report of the steam generator tubings pulled out from Kori unit 2, Korea Atomic Energy Research Institute, 1990.
3. H.R. Copson, S.W. Dean, Corrosion 21 (1965) 1.
4. T. Sakai, S. Okabayashi, K. Aoki, K. Matsumoto, Y. Kishi, A study of oxide thin film of Alloy 600 in high temperature water containing lead, CORROSION/90, paper no. 520.
5. M. Helie, Lead assisted stress corrosion cracking of Alloys 600, 690 and 800, in: Proceedings of the Sixth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, Sandiego, California, USA, 1-5 August, 1993, p. 179.
6. F. Vaillant, Comparative behavior of Alloys 600, 690 and 800, in: Proceedings of the Seventh International Symposium Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Breckenridge, Colorado, USA, 7-10 August, 1995, p. 219.
7. B.P. Miglin, J.M. Sarver, M.J. Psaila-Dombrowski, P.E. Doherty, Lead assisted stress corrosion cracking of nuclear steam generator tubing materials, Proceedings of a conference jointly sponsored by the EPRI and ANL, Airlie, Virginia, USA, 9-13 October, 1995, p. 305.
8. S.S. Hwang, U.C. Kirn, Y.S. Park, J. Nucl. Mater. 246 (1997) 77.
9. R.J. Jacko, Corrosion evaluation of thermally treated Alloy 600 tubing in primary and faulted secondary water environments, EPRI NP-6721-SD, June 1990, pp. 3-103.
10. R.J. Jacko, Stress corrosion testing of candidate steam generator tubing materials, in: Proceedings of Workshop on Thermally Treated Alloy 690 Tubes for Nuclear Steam Generators, EPRI NP-4665S-SR, July 1986, pp. 1-15.
11. J.P.N. Paine, R.S. Pathania, C.E. Shoemaker, Effect of caustic environment on intergranular attack and stress corrosion cracking of Alloy 600, in: Proceedings of the Third International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Traverse City, Michigan, USA, 30 August-3 Septemper, 1987, p. 501.
12. S.M. Bruemmer, Corrosion 44 (1988) 782.
13. S.S. Hwang, U.C. Kim, Y.S. Park, J. Corros. Science Society of Korea 25 (1996) 170.
14. T. Sakai, T. Senjuh, K. Aoki, T. Shigemitsu, Y. Kishi, Lead induced stress corrosion cracking of Alloy 600 and 690 in high temperature water, in: Proceedings of the Fifth International Symposium on Environmental Degradation of Materials in Nuclear Power System - Water Reactors, Monterey, California, USA, 25-29 August, 1991, p. 764.
15. M.D. Wright, G. Goszczynski, F. Peca, Embrittlement of Alloy 400 by lead in secondary side steam generator environments, in: Proceedings of the Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, Breckenridge, Colorado, USA, 7-10 August, 1995, p. 209.