Relations between cavitation erosion resistance of materials and their fatigue strength under random loading

Wear

Volumn 230, Issue 2, 1999, Pages 201-209

  Bedkowski, W ^a   Gasiak, G ^a   Lachowicz, C ^a   Lichtarowicz, A ^b   Lagoda T ^a   Macha, E ^a  

^a OPOLE UNIVERSITY OF TECHNOLOGY   (Poland)

^b UNIVERSITY OF NOTTINGHAM   (United Kingdom)

Author keywords

Cavitation erosion; Erosion by liquid; Fatigue; Random loading; Structural steels

Indexed keywords

COMPRESSION TESTING; CORROSION RESISTANCE; FATIGUE OF MATERIALS; MATHEMATICAL MODELS; STEEL CORROSION; STRUCTURAL LOADS; STRUCTURAL METALS; TENSILE TESTING;

RANDOM LOADING; STRUCTURAL STEELS;

CAVITATION CORROSION;

CAVITATION DAMAGE; EROSION; FATIGUE; STEEL; STRUCTURAL COMPONENT;

EID: 0032882267     PISSN: 00431648     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0043-1648(99)00105-2     Document Type: Article

References (19)

1. S. Kocańda, Fatigue Failure of Metals, Sijthoff a. Noordhoff Int. Publ., 1978.
2. Ahmed S.M., Hokkirigawa K., Ito Y., Oba R., Matsudaira Y. Scanning electron microscopy observation on the incubation period of vibratory cavitation erosion. Wear. 142:1991;303.
3. S.M. Ahmed, K. Hokkirigawa, K. Kikuchi, Y. Matsudaira, R. Oshima, R. Oba, Marked surface-roughness effects on the development of microfracture during the incubation period of vibratory cavitation erosion, Proc. 3rd Japan-China Joint Conf. Osaka, Japan, I, 1990, p. 331.
4. Ahmed S.M., Hokkirigawa K., Oba R., Kikuchi K. Jpn. Soc. Mech. Eng. Int. J., Ser. II. 34(3):1992;298.
5. Vaidya S., Preece C.M. Cavitation erosion of age-hardenable aluminium. Metall. Trans. A. 9:1978;299.
6. Ahmed S.M., Hokkirigawa K., Oba R. Fatigue failure of SUS 304 caused by vibratory cavitation erosion. Wear. 177:1994;129.
7. G. Echavez, Cavitation damage and determination of tension and fatigue resistance in concrete surfaces, in: H.P. Rossmanith (Ed.), Fracture on Damage of Concrete and Rock-FDCR-2, 1993, p. 445.
8. Okada T., Iwai Y. JSME J., Ser. I. 33(2):1990;128.
9. Okada T., Awazu K., Kawasaki H. Influence of cavitation erosion on corrosion fatigue and the effect of surface coatings on resistance. Wear. 63:1980;51-70.
10. Okada T., Iwai Y., Hattori S. Corrosion fatigue of steel under cavitation erosion generated intermittently in 3% salt water (results of two-stage tests with and without cavitation erosion). Wear. 96:1984;85-98.
11. Richman R.H., McNaughton W.P. Correlation of cavitation erosion behaviour with mechanical properties of metals. Wear. 149:1990;63-82.
12. Lachowicz C.T., Łagoda T., Macha E., Dragon A., Petit J. Selections of algorithms for fatigue life calculation of elements of 10HNAP steel under uniaxial random loadings. Stud. Geotech. Mech. XVIII(1-2):1996;19-43.
13. ASTM E 739-80. Standard practice for statistical analysis of linearized stress-life (S-N) and strain-life (ε- N) fatigue data, Annual Book of ASTM Standards, Vol. 03.01. Philadelphia, 1989, pp. 667-673.
14. R.T. Knapp, J. Daily, F.G. Hammit, Cavitation, McGraw-Hill, New York, 1970, p. 369.
15. Lichtarowicz A. Nature. Phys. Sci. (London). 239(91):1972;63.
16. A. Lichtarowicz, Cavitating jet apparatus for cavitation erosion testing, ASTM Philadelphia, PA, 1977, 518.
17. A. Lichtarowicz, R.J. Scot, Erosion testing with a cavitating jet, 5th Int. Conf. on Erosion by Liquid and Solid Impact, Cavendish Laboratory, Cambridge, 1979.
18. A. Lichtarowicz, Erosion testing with cavitating jet in cavitation erosion, Fluid Systems Fluids Engn. Conf. Boulder, CO, ASME, 1981.
19. A. Lichtarowicz, P. Kay, Erosion testing with cavitating jet, 6th Int. Conf. on Erosion by Liquid and Solid Impact, Cavendish Laboratory, Cambridge, 1983.