Stress corrosion cracking behaviour of 8090 Al-Li alloy at 313 K. The effect of grain structure

Corrosion Science

Volumn 41, Issue 6, 1999, Pages 1079-1088

  Conde, A ^a   De Damborenea, J J ^a  

^a DEPARTMENT OF PHYSICAL METALLURGY   (Spain)

Author keywords

Aluminium; Slow strain rate; Stress corrosion

Indexed keywords

CRACK PROPAGATION; CRYSTAL MICROSTRUCTURE; FRACTURE; HYDROGEN PEROXIDE; SODIUM CHLORIDE; STRAIN RATE; STRESS CORROSION CRACKING; THERMAL EFFECTS;

SLOW STRAIN RATE TESTS (SSRT);

ALUMINUM ALLOYS;

ALUMINUM ALLOY; STRESS CORROSION CRACKING;

EID: 0032876046     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(98)00152-8     Document Type: Article

References (15)

1. T.D. Burleigh, Corrosion 47 (1991) 89.
2. J.R. Galvele, Corrosion Science 27 (1987) 1-33.
3. J.R. Galvele, Corrosion Science 35 (1993) 419-434.
4. J.R. Galvele, J. of Nucl. Mat. 229 (1996) 139-148.
5. H. Vogt, M.O. Speidel, The effect of temperature on crack growth rates of stress corrosion cracks in metal alloys exposed to water. In: Corrosion '96 (Paper No. 265). NACE, Houston, 1966.
6. N.J.H. Holroyd, G.M. Scamans, In: S.W. Dean, E.N. Pugh, G.M. Ugiansky (Eds.), Environment-Sensitive fracture: Evaluation and Comparison of Test Methods, ASTM STP821. American Society for Testing and Materials, Philadelphia, 1984, pp. 202.
7. A. Conde, J. de Damborenea, Corrosion Science 40 (1) (1998) 91-102.
8. M.G. Alvarez, M. Giordano, C. Manfredi, J.R. Galvele, Corrosion 46 (1990) 717-726.
9. A. Sedkris, Stress Corrosion Cracking Test Methods. NACE, Houston, 1990.
10. J.R. Galvele, In: R.E. White (Ed.), Modern Aspects of Electrochemistry, No. 27. Plenum Press, NY, 1995, pp. 233-358.
11. H. Vogt, M. Speidel, Corrosion Science 40 (1998) 251-270.
12. N.J.H. Holroyd, A. Gray, G.M. Scamans, R. Herman, In: C. Baker, P.J. Gregson, S.J. Harris, C.J. Peel (Eds.), Proceedings 3rd Aluminium-Lithium Conference. The Institute of Metals of London, 1986, pp. 310-320.
13. A. Buis, J. Schijve, Corrosion 48 (1992) 898-909.
14. J.R. Galvele, J. of Electrochem. Soc. 133 (1986) 953-954.
15. J.B. Lumsden, A.T. Allen, Corrosion 44 (1988) 527-532.