Effect of heat treatment on the stress corrosion resistance of a microalloyed pipeline steel

Corrosion Science

Volumn 41, Issue 6, 1999, Pages 1037-1049

  Albarran, J L ^a   Martinez, L ^a   Lopez, H F ^b  

^a INSTITUTO DE CIENCIAS FÍSICAS   (Mexico)

^b University of Wisconsin Milwaukee   (United States)

Author keywords

Hydrogen embrittlement; Microalloyed steels; Pipeline steels; Sulfide stress corrosion cracking

Indexed keywords

CORROSION RESISTANCE; CRACK PROPAGATION; GRAIN BOUNDARIES; HYDROGEN EMBRITTLEMENT; HYDROGEN SULFIDE; METALLOGRAPHIC MICROSTRUCTURE; MICROCRACKS; QUENCHING; STRESS INTENSITY FACTORS; SULFIDE CORROSION CRACKING; TEMPERING;

SULFIDE STRESS CRACKING;

STEEL PIPE;

CRACK PROPAGATION; HEAT TREATMENT; HYDROGEN SULFIDE; STEEL PIPE; STRESS CORROSION CRACKING;

EID: 0032839526     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(98)00139-5     Document Type: Article

References (24)

1. R.S. Tresseder, in: R.W. Staehle et al. (Eds.), Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys. NACE, Houston, TX, 1977, p. 147.
2. Y. Nakai, H. Kurahashi, T. Emi, O. Haida, ISIJ Trans. 19 (1979) 401.
3. H. Huang, W.J.D. Shaw, Corrosion Sci. 34 (1993) 61.
4. H. Margot-Marette, G. Bardou, J.C. Charbonnier, Corrosion Sci. 27 (1987) 1009.
5. R.N. Parkins, J. of Min. Met. and Mat. 44 (1992) 12.
6. D.B. Kasul, L.A. Heldt, MRS Bulletin 37 (1989) 000-000.
7. J.M. Sykes, J. of Min. Met. and Mat. 45 (1993) 31.
8. R.N. Parkins, in: R.W. Staehle, A.J. Forty, D. Van Rooyen (Eds.), Fundamentals Aspects of Stress Corrosion Cracking. NACE, Houston, TX, 1969, p. 361.
9. R.N. Parkins, in: L.L. Shreir (Ed.), Mechanisms of SCC, Corrosion. Newnes-Butterworth, London, 1970.
10. J. Avila Mendoza, J.M. Sykes, Corrosion Sci. 23 (1983) 547.
11. R.N. Parkins, Corrosion Sci. 29 (1989) 1019.
12. R.M. Pedrazzoli, M.O. Speidel, Stress Corrosion Cracking of High Strength Steels, in: S.M. Bruemmer et al. (Eds.), Parkins Symposium on Fundamental Aspects of Stress Corrosion Cracking, TMS, Warrendale, PA, 1992, p. 341.
13. A. Ciszewski, T. Radomski, M. Smialowski, in: R.W. Staehle, J. Hochman, R.D. McCrigth, J.E. Slater (Eds.), Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys. NACE, Houston TX, 1977, p. 671.
14. S.R. Novak, S.T. Rolfe, J. Mats. 4 (1969) 701.
15. W.F. Deans, C.E. Richards, J. Test. Eval. 7 (1979) 147.
16. H. Buist, E. Feldhusen, B. Fatseas, (Eds.), NACE 1992 Book of Standards. Houston, NACE, TX, 1992.
17. R.N. Parkins, P.W. Slattery, W.R. Middleton, M.J. Humphries, British Corr. J. 8 (1973) 117.
18. N. Bandyopadhyay, A mechanistic interpretation of the relationship between temper embrittlement and the SCC susceptibility of Ni-Cr steels, in: MiCon'82L, ASTM, Philadelphia, PA, 1993, p. 104.
19. R.T. Hill, in: J.M. Gray, T. Ko, Z. Shouhua, Baorong, X. Xishan (Eds.), Proceedings of the International Conference on HSLA Steels. ASM International, 1985, p. 735.
20. Y. Nakai, H. Kurahashi, T. Emi, O. Haida, ISIJ Trans. 19 (1979) 401.
21. H.F. Lopez, R. Raghunath, J.L. Albarran, L. Martinez, Met. and Mat. Trans. A 27A (1996) 3601.
22. D. Bhattacharjee, J.F. Knott, Acta Metall, and Mater. 42 (1994) 1747.
23. Y. Kobayashi, in: K. Kawakami (Ed.), Proceedings of VIII Seminar Mexico-Japan, JICA'94, 1994, p. 9.1.
24. J.L. Albarran, L. Martinez, H.F. Lopez, Scripta Mater. 38 (1997) 749.