Threshold stress for crack initiation in yellow brass immersed in sodium nitrite solutions

Corrosion Science

Volumn 41, Issue 6, 1999, Pages 1031-1035

  Malki, B ^a   Legris, A ^b   Gorse, D ^a  

^a CNRS   (France)

^b UNIV LILLE   (France)

Author keywords

Crack initiation; Critical stress; Sodium nitrite

Indexed keywords

CHEMICAL BONDS; COLD WORKING; CRACK INITIATION; ELECTROLYTES; INTERFACES (MATERIALS); LOAD TESTING; OXIDES; SODIUM COMPOUNDS; STRAIN RATE; STRESS ANALYSIS;

SODIUM NITRITE;

BRASS;

BRASS; EMBRITTLEMENT; STRESS CORROSION CRACKING;

EID: 0032817271     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(98)00136-X     Document Type: Article

References (10)

1. J. Yu, N.J. Holroyd, R.N. Parkins, in: S.W. Dean, E.N. Pugh, G.M. Ugiansky (Eds.), Environment Sensitive Fracture, vol. 821. ASTM STP, 1984, p. 288.
2. J. Yu, R.N. Parkins, Y. Xu, G. Thomson, G.C. Wood, Corrosion Sci. 27 (1987) 141.
3. J. Yu, R.N. Parkins, Corrosion Sci. 27 (1987) 159.
4. F. Mackay, J.T. Evans, R.N. Parkins, Corrosion Sci. 33 (1992) 699.
5. X. Luo, J. Yu, Corrosion Sci. 33 (1996) 767.
6. N. Sato, Corrosion 45 (5) (1989).
7. B. Baroux, D. Gorse, in: F. Dabosi, G. Béranger, B. Baroux (Eds.), La Corrosion Localisée. 1994, p. 91.
8. R.B. Rebak, R.M. Carranza, J.R. Galvele, Corrosion Sci. 28 (1988) 1089.
9. S.R. Bubar, D.A. Vermilyea, J. Electrochem. Soc. 113 (1966) 892.
10. G. Alvarez, C. Manfredi, M. Giordano, J.R. Galvele, Corrosion Sci. 24 (1984) 769.