Mechanical interactions between fiber and cracked coating layer and their influences on fiber strength

Composites Part A: Applied Science and Manufacturing

Volumn 30, Issue 4, 1999, Pages 451-461

  Ochiai, Shojiro ^a   Hojo, Masaki ^a   Tanaka, Mototsugu ^a  

^a KYOTO UNIVERSITY   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

BOND STRENGTH (MATERIALS); COATINGS; CRACK PROPAGATION; CRACKS; ELASTIC MODULI; ELASTICITY; INTERFACES (MATERIALS); INTERFACIAL ENERGY; STRENGTH OF MATERIALS;

COATED FIBER; INTERFACIAL DEBONDING; MECHANICAL INTERACTIONS;

FIBERS;

EID: 0032690729     PISSN: 1359835X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1359-835X(98)00134-1     Document Type: Article

References (21)

1. Metcalfe AG, Klein MJ. Effects of the interface on longitudinal tensile properties. In: Metcalfe AG, editor. Interface in metal matrix composites. New York: Academic Press, 1974:125-168.
2. Dicarlo JA. Factors influencing the thermally induced strength degradation of B/A1 composites. In: Hack JE, Amateau MF, editor. Proc Mechanical Behavior of Metal Matrix Composites. PA: The Metallurgical Society of AIME, 1983:1-14.
3. Ochiai S. Strength of unnotched composites. In: Ochiai S, editor. Mechanical properties of metallic composites. New York: Marcel Dekker, 1993:473-510.
4. Ochiai S., Hojo M. Mesomechanical modeling approach to interface-related tensile behavior of FRM. Composite Interfaces. 5:1995;365-388.
5. Honjo K., Shindo A. Influence of carbide formation on the strength of carbon fibers on which silicon and titanium have been deposited. J Mater Sci. 21:1986;2043-2048.
6. Himbeault D.D., Varin R.A., Piekarski K. Carbon fibers coated with titanium carbide using the liquid metal transfer agent technique. J Mater Sci. 24:1989;2746-2750.
7. Ochiai S., Murakami Y. Theoretical prediction of tensile strength of fibers as a function of thickness of brittle zones on fiber surfaces. Metall Trans. 12A:1981;1155-1162.
8. Murakami Y, Nakao K, Imatani T, Shindo A, Honjo K, Ochiai S. Effect of interfacial condition on the tensile strength of carbon fiber-6061 aluminum alloy composites. In: Kawata K, Umekawa S, Kobayashi A, editors. Proc 3rd Japan-US Conference on Composite Materials. Tokyo: Japan Soc Comp Mater, 1986:761-766.
9. Shorshorov M.Kh., Ustinov L.M., Zirlin A.M., Olefilenko V.I., Vinogradov L.V. Brittle interface layers and the tensile strength of metal matrix-fibre composites. J Mater Sci. 14:1979;1850-1861.
10. Hunt WH Jr. Interfacial zones and mechanical properties in continuous fiber FP/Al-Li metal matrix composites. In: Dhingra AK, Fishman SG, editors. Interfaces in metal-matrix composites. PA: The Metallurgical Society of AIME, 1986:3-25.
11. Ochiai S., Inoue T., Hojo M., Dudek H.-J., Leucht R. Role of weak interface to retain high strength of fiber in monofilamentary SiC fiber/titanium-aluminide composite. Composite Interfaces. 4:1996;157-168.
12. Shinoda T., Liu H., Mishima Y., Suzuki T. Interfacial compatibility in ceramic-fibre-reinforced metal composites. Mater Sci Engng. A146:1991;91-104.
13. Ochiai S., Osamura K., Honjo K. Influence of fracture of coating layer on fiber strength. Mater Sci Engng. A154:1992;149-154.
14. Ochiai S., Hojo M. Interfacial debonding between fiber and pre-cracked coating layer. Mater Trans, JIM. 34:1993;563-568.
15. Ochiai S., Hojo M. Effects of preexistent crack in double- and gradient coatings on the crack-extension into fiber and interfacial debonding. J Mater Sci. 33:1998;347-355. in press.
16. Ochiai S., Hojo M. Multiple cracking of a coating layer and its influence on fiber strength - part II: Monte Carlo simulation. J Mater Sci. 30:1995;509-513.
17. Ochiai S., Osamura K. Influence of multiple cracking of coating layer on fiber strength. Z Metallkd. 84:1993;690-698.
18. Ochiai S., Hojo M. Multiple cracking of a coating layer and its influence on fiber strength - part I: Calculation of the energy release rate of the fiber at cracks for non-uniform crack spacing. J Mater Sci. 30:1995;274-279.
19. Weibull W. A statistical theory of the strength of materials. Proc R Swedish Inst Engng Res. 151:1939;1-45.
20. Evans A.G. The mechanical performance of fiber-reinforced ceramic matrix composites. Mater Sci Engng. A107:1989;227-241.
21. Evans A.G. The mechanical properties of reinforced ceramic, metal and intermetallic matrix composites. Mater Sci Engng. A143:1991;63-76.