Mechanical properties and fracture behavior of interfacial alumina scales on plasma-sprayed thermal barrier coatings

Materials at High Temperatures

Volumn 16, Issue 2, 1999, Pages 49-69

  Haynes, J A ^a,b   Ferber, M K ^a   Porter, W D ^a   Rigney, E D ^b  

^a OAK RIDGE NATIONAL LABORATORY   (United States)

^b University of Alabama at Birmingham   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

COATINGS; ELASTIC MODULI; FRACTURE MECHANICS; GRAIN BOUNDARIES; HARDNESS; PLASMA SPRAYING; THERMAL CYCLING;

AIR PLASMA SPRAYED; ALUMINA FRACTURE; ALUMINA SCALES; PLASMA SPRAYED COATING; THERMAL BARRIER COATINGS; VACUUM PLASMA SPRAYED;

ALUMINA;

EID: 0032690278     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1179/mht.1999.006     Document Type: Article

References (51)

1. R. Prescott and M. J. Graham, The formation of aluminum oxide scales on high-temperature alloys. Oxidation of Metals. 38[3/4], 233-253 (1992).
2. G. H. Meier, A review of advances in high-temperature corrosion. Materials Science and Engineering, A120, 1-11 (1989).
3. 3 oxide scales. Materials Science and Engineering, A201, 211-228 (1995).
4. D. M. Lipkin and D. R. Clarke, Measurement of the stress in oxide scales formed by oxidation of alumina-forming alloys. Oxidation of Metals, 45[3/4], 267-280 (1996).
5. A. G. Evans, G. B. Crumley and R. E. Demaray, On the mechanical behavior of brittle coatings and layers. Oxidation of Metals, 20[5/6], 193-216 (1983).
6. H. E. Evans, Cracking and spalling of protective oxide layers. Materials Science and Engineering, A120, 239-146 (1989).
7. M. M. Nagl, W. T. Evans, Review: The mechanical failure of oxide scales under tensile or compressive load. Journal of Materials Science, 28, 6247-6260 (1993).
8. M. Schütze, Mechanical properties of oxide scales. Oxidation of Metals, 44[1/2], 29-61 (1995).
9. P. F. Tortorelli and J. R. Keiser, The use of depth-sensing submicron indentation testing to characterize the mechanical behavior of thin oxide scales. Scripta Metallurgica et Materiala, 25, 2339-2344 (1991).
10. J. R. Nicholls, D. J. Hall and P. F. Tortorelli, Hardness and modulus measurements on oxide scales, Materials at High Temperatures, 12[2-3], 141-150 (1994).
11. J. C. Schaeffer, W. H. Murphy and J. L. Smialek, The effect of surface condition and sulfur on the environmental resistance of airfoils. Oxidation of Metals, 43[1/2], 1-23 (1996).
12. B. A. Pint, Experimental observations in support of the dynamic-segregation theory to explain the reactive-element effect. Oxidation of Metals, 45[1/2], 1-37 (1996).
13. A. Funkenbusch, J. G. Smeggil, N. S. Bornstein, Reactive element-sulfur interaction and oxide scale adherence. Metallurgical Transactions A16, 1164-1166 (1985).
14. J. G. Smeggil, A. W. Funkenbusch and N.S. Bornstein, A relationship between indigenous impurity elements and protective oxide scale adherence characteristics. Metallurgical Transactions A17, 923-932 (1986).
15. J. L. Smialek, D. T. Jayne, J. C. Schaeffer, W. H. Murphy, Effects of hydrogen annealing, sulfur segregation and diffusion on the cyclic oxidation resistance of superalloys: a review. Thin Solid Films, 253, 285-292 (1994).
16. 3Al containing yttrium. Oxidation of Metals, 8[3], 139-177 (1974).
17. 3, scales. Oxidation of Metals, 48, 303 (1997).
18. T. A. Ramanarayanan, M. Raghavan and R. Petkovic-Luton, The characteristics of alumina scales formed on Fe-based Yttria-dispersed alloys. J. Electrochem. Soc.: Solid-State Science and Technology, 923-931 (1984).
19. F. A. Golightly, F. H. Stott, G. C. Wood, The influence of yttrium additions on the oxide-scale adhesion to an iron-chromium-aluminum alloy. Oxidation of Metals, 10[3], 163-187 (1976).
20. B. A. Pint, P. F. Tortorelli and I. G. Wright, The oxidation behavior of ODS iron aluminides. Submitted to Werkst. Korros. (1997).
21. J. Stringer, The reactive element effect in High-Temperature Corrosion. Materials Science and Engineering, A120, 129-137 (1989).
22. T. A. Ramanarayanan, R. Ayer, R. Petkovic-Luton and D. P. Leta, The influence of yttrium on oxide scale growth and adherence. Oxidation of Metals, 29[5/6], 445-472 (1988).
23. S. M. Meier, D. M. Nissley, K. D. Sheffler, Thermal barrier coating life prediction model development: Phase II final report. NASA Contractor Report 189111 (1991).
24. S. M. Meier and D. K. Gupta, The evolution of thermal barrier coatings in gas turbine engine applications. Journal of Engineering for Gas Turbines and Power, 116, 250-257 (1994).
25. Y. H. Sohn, R. R. Biederman, R. D. Sisson, Jr., Isothermal oxidation of physical vapor deposited partially stabilized zirconia thermal barrier coatings. Journal of Materials Engineering and Performance, 3[1], 55-60 (1994).
26. J. A. Haynes, Oxidation and Degradation of Thermal Barrier Coating Systems. PhD Thesis, University of Alabama at Birmingham (1997).
27. R. A. Miller, C. E. Lowell, Failure mechanisms of thermal barrier coatings exposed to elevated temperatures. Thin Solid Films, 95, 265-273 (1982).
28. R. V. Hillery, B. H. Pilsner, R. L. McKnight, T. S. Cook, M. S. Hartle, Thermal barrier coating life prediction model development. NASA Contractor Report 180807 (1988).
29. J. T. DeMasi, K. D. Sheffler, M. Ortiz, Thermal barrier coating life prediction model development: Phase I Final Report. NASA Contractor Report 182230 (1989).
30. 3/Ni-22Cr-10Al-1Y thermal barrier coatings. J. Am. Ceram. Soc., 72[2], 212-218 (1989).
31. A. H. Bartlett, R. Dal Maschio, Failure mechanisms of a zirconia-8wt% yttria thermal barrier coating. J. Am. Ceram. Soc., 78[4], 1018-1024 (1995).
32. 3 thermal barrier system. Advanced Ceramic Materials, 1[1], 68-76 (1986).
33. J. T. DeMasi-Marcin, K. D. Sheffler, S. Bose, Mechanisms of degradation and failure in a plasma-deposited thermal barrier coating. Journal of Engineering for Gas Turbines and Power, 112, 521-526 (1990).
34. D. J. Wortman, B. A. Nagaraj and E. C. Duderstadt, Thermal barrier coatings for gas turbine use. Materials Science and Engineering, A121, 433-440 (1989).
35. R. A. Miller, Life modeling of thermal barrier coatings for aircraft gas turbine engines. Journal of Engineering for Gas Turbines and Power, 111, 301-305 (1989).
36. J. A. Haynes, E. D. Rigney, M.K. Ferber, W. D. Porter, Isothermal and cyclic oxidation of an air plasma-sprayed thermal barrier coating system. ASME Paper 96-GT-286 (1996).
37. J. A. Haynes, E. D. Rigney, M. K. Ferber, W. D. Porter, Oxidation and degradation of a plasma-sprayed thermal barrier coating system. Surface and Coatings Technology, 86-87, 102-108 (1996).
38. 2 electron beam-physical vapor deposition coatings on Ni-base superalloy. Journal of the American Ceramic Society, 77[4], 984-992 (1994).
39. L. Lelait, S. Alperine, R. Mevrel, Alumina scale growth at zirconia-MCrAlY interface: a microstructural study. Journal of Materials Science, 27, 5-12 (1992).
40. S. Alperine, Microstructural investigations of plasma-sprayed yttria partially stabilized zirconia TBC (in relation to thermomechanical resistance and high-temperature oxidation mechanisms) Journal of Engineering for Gas Turbines and Power, 116, 259-265 (1994).
41. W. J. Brindley and R. A. Miller, Thermal barrier coating life and isothermal oxidation of low-pressure plasma-sprayed bond coat alloys. Surface and Coatings Technology, 43/44, 446-457 (1990).
42. B. A. Pint, Characterization of the high temperature oxidation of a TBC-coated oxide-dispersed β-NiAl substrate. Materials at High Temperatures, 14(4), 403-412 (1997).
43. M. M. Mora, R. R. Biederman and R. D. Sisson, Jr., Microstructural characterization of metallic overlay coatings by high resolution analytical electron microscopy. Thin Solid Films, 119, 383-394 (1984).
44. P. Choquet, C. Indrigo, R. Mevrel, Microstructure of oxide scales formed on cyclically oxidized M-Cr-Al-Y coatings. Materials Science and Engineering, 88, 97-101 (1987).
45. R. A. Miller and W. J. Brindley, Plasma-sprayed thermal barrier coatings on smooth surfaces. Proceedings of the International Thermal Spray Conference & Exposition, 493-498 (1992).
46. P. F. Tortorelli, S. R. J. Saunders, G. Shafirstein and D. J. Hall, Use of the mechanical properties microprobe for characterization of oxide scales. Materials at High Temperatures, 12[2-3], 95-101 (1994).
47. M. P. Borom, C. A. Johnson, Thermomechanical behavior and phase relationships of plasma-sprayed zirconia coatings. Surface and Coatings Technology, 54/55, 45-52 (1992).
48. W. Phucharoen, Development of an analytical-experimental methodology for predicting the life and mechanical behavior of thermal barrier coatings. PhD Thesis, Cleveland State University, (1990).
49. M. Ferrari and L. Lutterotti, Thermal stresses in bi-coated structures. ASCE Journal of Engineering Mechanics, 118, 1928-38 (1992).
50. E. P. Popov, Mechanics of Materials, 2nd Edition, Prentice-Hall, Inc. Englewood Cliffs, New Jersey, p. 291 (1976).
51. B. A. Pint, I. G. Wright, W. Y. Lee, Y. Zhang, K. Prußner and K. B. Alexander, Substrate and Bond Coat Compositions: Factors affecting alumina scale adhesion. Materials Science and Engineering, A245, 201-211 (1997).