Damage development in woven fabric composites during tension-tension fatigue

Journal of Composite Materials

Volumn 33, Issue 7, 1999, Pages 614-639

  Hansen, Ulrich ^a,b  

^a TECHNICAL UNIVERSITY OF DENMARK   (Denmark)

^b UNIVERSITY OF READING   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

COMPUTER SIMULATION; DEGRADATION; FAILURE (MECHANICAL); FATIGUE OF MATERIALS; IMPACT RESISTANCE; INSPECTION; MATHEMATICAL MODELS; NONDESTRUCTIVE EXAMINATION; NUMERICAL ANALYSIS; STRESS CONCENTRATION; TENSILE TESTING; THERMOGRAPHY (IMAGING);

DAMAGE DEVELOPMENT; DAMAGE GROWTH; DAMAGE INITIATION; TENSION-TENSION FATIGUE; WOVEN FABRIC COMPOSITES;

FABRICS;

EID: 0032677021     PISSN: 00219983     EISSN: None     Source Type: Journal    
DOI: 10.1177/002199839903300702     Document Type: Article

References (27)

1. Joshi, S. P. and Sun, C. T. "Impact Induced Fracture in a Laminated Composite," Journal of Composite Materials, Vol. 19, 1985, pp. 51-66.
2. Mandell, J. F., Huang, D. D. and McGarry, F. J. "Tensile Fatigue Performance of Glass Fiber Dominated Composites," Composites Technology Review, Vol. 3, No. 3, Fall 1981, pp. 96-102.
3. Hansen, U., Brøndsted, P. and Andersen, S.-I. "Fatigue Testing of Damaged FRP Sandwich Specimens," DAMTOS Report, No DAMTOS-TR-301/Risø, 1996.
4. Karger-Hocsis, J. and Fejes-Kozma, Z. "Failure Mode and Damage Zone Development in a GMT-PP by Acoustic Emission and Thermography," Journal of Reinforced Plastics and Composites, Vol. 13, September 1994, pp. 786-792.
5. Sakagami, T. and Ogura, K. "New Flaw Inspection Technique Based on Infrared Thermal Images under Joule Effect Heating," JSME International Journal, Series A, Vol. 37, No. 4, 1994, pp. 380-388.
6. Shiratori, M., Takahashi, Y. and Qiang, Y. "Application of Infrared Thermography to Detection of Cracks," JSME International Journal, Series A, Vol. 37, No. 3, 1994, pp. 296-302.
7. Fujii, T., Shiina, T. and Okubo, K. "FatigueNotch Sensitivity of Glass Woven Fabric Composites Having a Circular Hole under Tension/Torsion Biaxial Loading," Journal of Composite Materials, Vol. 28, No. 3, 1994, pp. 234-251.
8. Kellas, S., Morton, J. and Bishop, S. M. "Damage Development in Notched Carbon Fibre Composites Subjected to Fatigue Loading," Composite Structures, Vol. 3, 1985, pp. 56-68.
9. Stinchcomb, W. W. and Reifsnider, K. L. "Fatigue Damage Mechanisms in Composite Materials: A Review," Fatigue Mechanisms, Proceedings of an ASTM-NBS-NSF Symposium, Kansas City, Mo., 1978, J. T. Fong, Ed., ASTM STP 675, American Society for Testing and Materials, 1979, pp. 762-787.
10. Broutman, L. J. and Sahu, S. "Progressive Damage of a Glass Reinforced Plastic during Fatigue," Paper 11D in Proceedings of the 24th Annual Conference of the RP/C Institute, Society of the Plastics Industry, Feb. 1969, pp. 1-12.
11. O'Brien, T. K. and Reifsneider, K. L. "Fatigue Damage: Stiffness/Strength Comparisons for Composite Materials," Journal of Testing and Evaluation, Vol. 5, No. 5, 1977, pp. 384-393.
12. Reifsnider, K. L., Schulte, K. and Duke, J. C. "Long-Term Fatigue Behavior of Composite Materials," Long-Term Behavior of Composites, ASTM STP 813, T. K. O'Brien, Ed., American Society for Testing and Materials, Philadelphia, 1983, pp. 136-159.
13. Hahn, H. T. and Kim, R. Y. "Fatigue Behavior of Composite Laminate," Journal of Composite Materials, Vol. 10, April 1976, pp. 156-180.
14. Kachanov, L. M. "On the Creep Fracture Time," Izv. AN SSR, Otd. Tekhn, Nauk, No. 8, 1958, pp. 26-31 (in Russian).
15. Talreja, R., "A Continuum Mechanics Characterization of Damage in Composite Materials," in Proceedings of the Royal Society of London, 399A, 1985, pp. 195-216.
16. Harris, C. E., Allen, D. H. and Nottorf, E. W. "Modeling Stiffness Loss in Quasi-Isotropic Laminates Due to Microstructural Damage," Transactions of the ASME, Vol. 110, April 1988, pp. 128-133.
17. Lemaitre, J. "How to Use Damage Mechanics," Nuclear Engineering and Design, 80, 1984, pp. 233-245.
18. Burr, A., Hild, F. and Leckie, F. A. "Micro-Mechanics and Continuum Damage Mechanics," Archive of Applied Mechanics, Springer Verlag, 1995, pp. 1-20.
19. Pyrz, R. "A Constitutive Model for Creep and Damage in Composite Materials," Creep in Structures, Zyczkowski, M., Ed., IUTAM Symposium Cracow/Poland, 1990, pp. 451-458.
20. Blackketter, D. M., Walrath, D. E. and Hansen, A. C. "Modelling Damage in a Plain Weave Fabric-Reinforced Composite Material," Journal of Composites Technology & Research, JCTRER, Vol. 15, No. 2, Summer 1993, pp. 136-142.
21. Naik, N. K. and Ganesh, V. K. "Failure Behavior of Plain Weave Fabric Laminates under In-Plane Shear Loading," Journal of Composites Technology & Research, JCTRER, Vol. 16, No. 1, 1994, pp. 3-20.
22. Ishikawa, T. and Chou, T.-W., "Stiffness and Strength Behavior of Woven Fabric Composites," Journal of Materials Science, Vol. 17, 1982, pp. 3211-3220.
23. Whitcomb, J., Woo, K. and Gundapaneni, S. "Macro Finite Element for Analysis of Textile Composites," Journal of Composite Materials, Vol. 28, No. 7, 1994, pp. 607-618.
24. Shan, H.-Z., Pluvinage, P., Parvizi-Majidi, A. and Chou, T.-W., "Damage Mechanics of Two-Dimensional Woven SiC/SiC Composites," Journal of Engineering Materials and Technology, Vol. 116, 1994, pp. 403-407.
25. Ladeveze, P. and Le Dantec, E. "Damage Modelling of the Elementary Ply for Laminated Composites," Composites Science and Technology, Vol. 43, 1992, pp. 257-267.
26. Brockenbrough, J. R. and Suresh, S. "Constitutive Behavior of a Microcracking Brittle Solid in Cyclic Compression," Journal of the Mechanics and Physics of Solids, Vol. 35, No. 6, 1987, pp. 721-742.
27. ABAQUS User's Manual, Version 5, Hibbitt, Karlsson and Sorensen, Inc., Providence, RI 02906.