Residual strength predictions for multiple site damage cracking using a three-dimensional finite element analysis and a CTOA criterion

ASTM Special Technical Publication

Volumn , Issue 1332, 1999, Pages 815-829

  Dawicke, D S ^a   Newman Jr , J C ^a  

^a NASA LANGLEY RESEARCH CENTER   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ALUMINUM ALLOYS; CRACK INITIATION; CRACK PROPAGATION; ELASTOPLASTICITY; FAILURE (MECHANICAL); FINITE ELEMENT METHOD; FRACTURE; STRESSES;

COMPACT TENSION; CTOA; MIDDLE CRACK TENSION; MULTIPLE SITE DAMAGE;

STRENGTH OF MATERIALS;

EID: 0032651304     PISSN: 10403094     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Article

References (20)

1. Rice, J. R., "A Path Independent Integral and the Approximate Analysis of Strain Concentrations by Notches and Cracks," ASME Journal of Applied Mechanics, Vol. 35, 1968, pp. 379-386.
2. IC," Fracture Toughness, ASTM STP 514, American Society for Testing and Materials, Philadelphia, 1972, pp. 24-39.
3. R-Curves for Four Aluminum Alloys," Fracture Mechanics: Twenty-Second Symposium (Volume II). ASTM STP 1131, S. N. Atluri, J. C. Newman, Jr., I. S. Raju, and J. S. Epstein, Eds., American Society for Testing and Materials, Philadelphia, 1992, pp. 135-153.
4. Wells, A. A., "Unstable Crack Propagation in Metals: Cleavage and Fast Fracture," Proceedings of the Cranfield Crack Propagation Symposium, Vol. 1, 1961, pp. 210-230.
5. Wells, A. A., "Application of Fracture Mechanics at and Beyond General Yielding," British Welding Journal, Vol. 11, 1961, pp. 563-570.
6. Wells, A. A., "Notched Bar Tests, Fracture Mechanics and Brittle Strengths of Welded Structures," British Welding Journal, Vol. 12, 1963, pp. 2-13.
7. Anderson, H., "Finite Element Representation of Stable Crack Growth," Journal of Mechanics and Physics of Solids, Vol. 21, 1973, pp. 337-356.
8. de Koning, A. U., "A Contribution to the Analysis of Quasi Static Crack Growth in Steel Materials," Fracture 1977, Proceedings of the 4th International Conference on Fracture, Vol. 3. 1977, pp. 25-31.
9. Kanninen, M. F., "The Analysis of Stable Crack Growth in Type 304 Stainless Steel," Proceedings of the International Conference of Fracture, 1980, pp. 1759-1768.
10. Kanninen, M. F., Popelar, C. H., and Broek, D., "A Critical Survey on the Application of Plastic Fracture Mechanics to Nuclear Pressure Vessels and Piping," Nuclear Engineering and Design, 1981, Vol. 67, pp. 27-55.
11. Newman, J. C., Jr., "An Elastic-Plastic Finite Element Analysis of Crack Initiation, Stable Crack Growth, and Instability, " Fracture Mechanics - Fifteenth Symposium, ASTM STP 833, American Society for Testing and Materials, Philadelphia, 1984, pp. 93-117.
12. Newman, J. C., Jr., Shivakumar, K. N., and McCabe, D. E., "Finite Element Fracture Simulation of A533B Steel Sheet Specimens," ESIS Pub. 9, 1991, pp. 117-126.
13. Newman, J. C., Jr., Dawicke, D. S., and Bigelow, C. A., "Finite-Element Analyses and Fracture Simulation in Thin-Sheet Aluminum Alloy," Durability of Metal Aircraft Structures, Proceedings of the International Workshop on Structural Integrity of Aging Airplanes, 1992, pp. 167-186.
14. Newman, J. C., Jr., Dawicke, D. S., Sutton, M. A., and Bigelow, C. A., "A Fracture Criterion for Widespread Cracking in Thin-Sheet Aluminum Alloys," ICAF 17, International Committee on Aeronautical Fatigue, 1993, pp. 443-468.
15. Dawicke, D. S., Newman, J. C., Jr., Sutton, M. A., and Amstutz, B. E., "Influence of Crack History on the Stable Tearing Behavior of a Thin-Sheet Material with Multiple Cracks," NASA CP 3274, Part 1, Proceedings from the FAA/NASA International Symposium on Advanced Structural Integrity Methods for Airframe Durability and Damage Tolerance, 1994, pp. 193-212.
16. Dawicke, D. S., "Residual Strength Predictions Using a CTOA Criterion," DOT/FAA/AR-97/2, Proceedings of the FAA-NASA Symposium on Continued Airworthiness of Aircraft Structures, July 1997, pp. 555-566.
17. Dawicke, D.S. and Sutton, M. A., "CTOA and Crack Tunneling in Thin Sheet 2024-T3 Aluminum Alloy," Experimental Mechanics, Vol. 34, No. 4, 1994, pp. 357-368.
18. Dawicke, D. S., Newman, J. C., Jr., and Bigelow, C. A., "Three-Dimensional CTOA And Constraint Effects During Stable Tearing In A Thin-Sheet Material," Fracture Mechanics: 26th Volume, ASTM STP 1256, W. G. Reuter, J. H. Underwood, and J. C. Newman, Jr., Eds., American Society for Testing and Materials, Philadelphia, 1995.
19. Shivakumar, K. N. and Newman, J. C., Jr., "ZIP3D - An Elastic-Plastic Finite-Element Analysis Program for Cracked Bodies," NASA TM-102753, Hampton, VA, 1990.
20. Sutton, M. A., Dawicke, D. S., and Newman, J. C., Jr., "Orientation Effects on the Measurement and Analysis of Critical CTOA in an Aluminum Alloy Sheet," Fracture Mechanics: 26th Volume, ASTM STP 1256, W. G. Reuter, J. H. Underwood, and J. C. Newman, Jr., Eds., American Society for Testing and Materials, Philadelphia, 1995.