Mechanism of embrittlement of Al alloy by liquid metal (Ga)

Canadian Metallurgical Quarterly

Volumn 38, Issue 2, 1999, Pages 127-132

  Chu, W Y ^a   Liu, X M ^a   Luo, J L ^b   Qiao, L J ^b  

^a UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

^b UNIVERSITY OF ALBERTA   (Canada)

Author keywords

[No Author keywords available]

Indexed keywords

ADSORPTION; ALUMINUM ALLOYS; COMPRESSIVE STRESS; CRACK INITIATION; CRACK PROPAGATION; EMBRITTLEMENT; FRACTURE; GALLIUM; LIQUID METALS; MICROCRACKING; PLASTIC DEFORMATION; TENSILE STRESS;

LIQUID METAL-INDUCED EMBRITTLEMENT (LME);

ALUMINUM METALLURGY;

EID: 0032636058     PISSN: 00084433     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0008-4433(99)00002-6     Document Type: Article

References (25)

1. Zhong, P. and Yan, H., Engineering Failure Analysis, 1996, 3, 241.
2. Fernandes, P. J. L. and Jones, D. R. H., Engineering Failure Analysis, 1996, 3, 299.
3. Reynolds, A. P. and Stoner, G. E., Metall Trans, 1991, 22A, 1849.
4. Stoloff, N. S., In Environment sensitive fracture of engineering materials, ed. Z. A. Foroulis, Metall. Soc. AIME, Warrendale, PA, 1979, p. 358.
5. Kargol, J. A. and Albright, D. L., Metall Trans, 1977, 8A, 27.
6. Lynch, S. P., Acta Metall, 1988, 36, 2639.
7. Anderson, T. L., Fracture mechanics, 2nd ed., CRC Press, London, 1995.
8. Chu, W. Y., Hsiao, C. M. and Wang, J. W., Metall Trans, 1985, 16A, 1663.
9. Beachem, C. D., Metall Trans, 1972, 3, 437.
10. Licher, B. D., Flanagan, W. F., Kim, J-S., Elkenbracht, J. C. and Van Hunen, M., Corrosion, 1996, 52, 453.
11. Cox, B. and Wong, Y-M., J Nucl Mater, 1997, 245, 34.
12. Lynch, S. P., Acta Metall, 1988, 32, 79.
13. Lynch, S. P., A comparitive study of stress - corrosion cracking, hydrogen-assisted cracking and liquid - metal embrittlement in A1, Ni, Ti and Fe-baaaaased alloys, In Hydrogen effects in metals, ed. I. M. Bernstein and A. W. Thompson, Metall. Soc. AIME, Warrendale, PA, 1981, p. 863.
14. Su, Y. J., Wang, Y. B. and Chu, W. Y., Scripta Metall, 1997, 36, 1239.
15. Chu, W. Y., Hsiao, C. M., Li, W. X. and Zhang, Y. G., Metall Trans, 1984, 15A, 2087.
16. Chu, W. Y., Liu, T. H. and Hsiao, C. M., Corrosion, 1981, 37, 320.
17. Benson, B. A. and Hoagland, R. G., Scripta Metall, 1989, 23, 1943.
18. Lawn, B., In Fracture of brittle solids, 2nd ed., Cambridge University Press, Cambridge, 1993, p. 20.
19. Chu, W. Y., Gao, K. W. and Wang, Y. B., Science in China, 1995, 38A, 233.
20. Lu, H., Li, M. D., Zhang, T. C. and Chu, W. Y., Science in China, 1997, 40E, 562.
21. Chu, W. Y., Gu, B., Gao, K. W. and Huang, Y. Z., Science in China, 1997, 40E, 235.
22. Belz, G. E., Rice, J. R., Shih, C. F. and Xia, L., Acta Mater, 1995, 44, 3943.
23. Orowan, E., Prog Phys, 1949, 12, 185.
24. MacMillan, N. H., The ideal strength of solids, In Atomistics of fracture, ed. R. M. Latanision and J. R. Pickens, Plenum Press, New York, 1981, p. 95.
25. Knott, J. F., In Fundamentals of fracture mechanics, Butterworths, London, 1973, p. 39.