Effect of residual stress on brittle fracture testing

ASTM Special Technical Publication

Volumn , Issue 1332, 1999, Pages 154-175

  Hill, Michael R ^a   Panontin, Tina L ^b  

^a University of California   (United States)

^b NASA AMES RESEARCH CENTER   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

BRITTLE FRACTURE; COMPOSITE MICROMECHANICS; FINITE ELEMENT METHOD; FRACTURE MECHANICS; FRACTURE TESTING; FRACTURE TOUGHNESS; LOADS (FORCES); MATHEMATICAL MODELS; WELDS;

CRACK TIP CONSTRAINT; HOMOGENIZATION; MICROMECHANICAL FAILURE THEORY;

RESIDUAL STRESSES;

EID: 0032632439     PISSN: 10403094     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1520/stp14948s     Document Type: Article

References (23)

1. T. L. Panontin and M. R. Hill, "The effect of residual stresses on brittle and ductile fracture initiation predicted by micromechanical models," International Journal of Fracture 82 (1996) pp. 317-333.
2. T. Mura, Micromechanics of Defects in Solids, Dordrecht, Netherlands, M. Nijhoff (1987)
3. M. R. Hill, Ph.d. Dissertation, Stanford University (1996).
4. J. A. Goldak, et al., "Computational Weld Mechanics," Advanced Joining of Materials (AGARD CP-398), AGARD (1985) pp. 1-1-1-32.
5. Y. Ueda, K. Nakacho, and M. Yuan, "Application of FEM to theoretical analysis, measurement and prediction of welding residual stresses," Transactions of the Japanese Welding Research Institute 20(1) (1991) pp. 97-107
6. M. R. Hill and D. V. Nelson, "The Inherent Strain Method for Residual Stress Determination and Its Application to a Long Welded Joint," ASME Pressure Vessels and Piping 318 (1995) pp. 343-352.
7. R. Gunnert, "Residual Stresses," Proceedings of the Special Symposium on the Behavior of Welded Structures, Urbana, IL, University of Illinois Engineering Experiment Station (1961) pp. 164-201.
8. V. Kumar, M. D. German, and C. F. Shih, "An Engineering Approach for Elastic-Plastic Fracture Analysis," EPRI Report NP-1931, Electric Power Research Institute, Palo Alto (1981).
9. W. A. Sorem, S. T. Rolfe, and R. H. Dodds, Jr., "The Effects of Crack Depth on Elastic-Plastic CTOD Fracture Toughness." Welding Research Council Bulletin 351 (1990) pp. 12-23.
10. R. O. Ritchie, W. L. Server, and R. A. Wullarert, "Critical Fracture Stress and Fracture Strain Models for the Prediction of Lower and Upper Shelf Toughness in Nuclear Pressure Vessel Steels," Metallurgical Transactions 10A (1979) pp. 1557-1570.
11. A. C. Mackenzie, J. W. Hancock, and D. K. Brown, "On the Influence of State of Stress on Ductile Failure Initiation in High Strength Steels," Engineering Fracture Mechanics 9 (1977) pp. 167-188.
12. N. P. O'Dowd and C. F. Shih, "Family of Crack-Tip Fields Characterized by a Triaxiality Parameter: Part I-Structure of Fields," Journal of the Mechanics and Physics of Solids 39 (1991) pp. 989-1015.
13. N. P. O'Dowd and C. F. Shih, "Family of Crack-Tip Fields Characterized by a Triaxiality Parameter: Part II-Fracture Applications," Journal of the Mechanics and Physics of Solids, 40 (1992) pp. 939-963.
14. M. Nevalainen and R. H. Dodds, Jr., "Numerical Investigation of 3-D Constraint Effects on Brittle Fracture in SE(B) an C(T) Specimens," Report UIUC-ENG-95-2001, University of Illinois at Urbana-Champaign (1995).
15. P3/PATRAN, User Manual, Release 1.3, PDA Engineering, Inc., Los Angeles, CA (1994).
16. ABAQUS/Standard, User's Manual, Version 5.5, Hibbitt, Karlsson, and Sorenson, Inc., Providence, RI (1995).
17. P. W. Bridgman, Studies in Large Flow and Fracture, McGraw-Hill, New York (1952).
18. G. Glinka and G. Shen, "Universal Features of Weight Functions for Cracks in Mode I," Engineering Fracture Mechanics 40 (1991) pp. 1135-1146.
19. T. L. Panontin and S. D. Sheppard, "An Experimentally-Verified Finite Element Study of the Stress-Strain Response of Crack Geometries Experiencing Large Scale Yielding," Fatigue and Fracture Mechanics, 27th Volume, ASTM STP 1296, Robert S. Piascik, James C. Newman, Jr. and Norman E. Dowling, Eds., American Society for Testing and Materials (1997) pp. 216-242.
20. T. L. Panontin, Ph.d. Dissertation, Stanford University (1994).
21. E .F. Rybicki and J. R. Shadley, "A Three-dimensional Finite Element Evaluation of a Destructive Experimental Method of Determining Through-thickness Residual Stresses in Girth Welded Pipes," Journal of Engineering Materials and Technology 108(2) (1986) pp. 99-106.
22. O. L. Towers and M. G. Dawes, "Welding Institute Research on the Fatigue Precracking of Fracture Toughness Specimens," Elastic-Plastic Fracture Test Methods: The Users' Experience, ASTM STP 856, E. T. Wessel and F. J. Loss Eds., American Society for Testing and Materials (1985) pp. 23-46.
23. R. H. Leggatt and M. S. Kamath, Residual Stresses in 25mm Thick Weld Metal COD Specimens in the As-welded and Locally Compressed States, The Welding Institute (1981).