Microchemistry of proton-irradiated austenitic alloys under conditions relevant to LWR core components

Materials Research Society Symposium - Proceedings

Volumn 540, Issue , 1999, Pages 421-432

  Was, G S ^a   Allen, T R ^a   Busby, J T ^a   Gan, J ^b   Damcott, D ^b   Carter, D ^b   Atzmon, M ^a   Kenik, E A ^b  

^a UNIVERSITY OF MICHIGAN   (United States)

^b OAK RIDGE NATIONAL LABORATORY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

AUSTENITE; CHROMIUM; DOSIMETRY; GRAIN BOUNDARIES; LIGHT WATER REACTORS; METALLOGRAPHIC MICROSTRUCTURE; NICKEL; PROTON IRRADIATION; TEMPERATURE;

IRON COPPER NICKEL ALLOYS; MICROCHEMISTRY;

IRON ALLOYS;

EID: 0032591964     PISSN: 02729172     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Article

References (22)

1. D. Damcott, J. Cookson, V. Rotberg and G. S. Was, Nucl. Instr. Meth. B 99, p.780, (1995).
2. T. R. Allen, Ph.D. Thesis, University of Michigan, 1997
3. D. Damcott, T. Alien and G. S. Was, J. Nucl. Mater. 225, p. 97, (1995).
4. L. E. Davis, N. C. MacDonald, P. W. Palmberg, G. E. Riach, and R. E. Weber, Handbook of Auger Electron Spectroscopy, 2nd Edition, Perkin-EImer Corporation, Eden Prairie, MN.
5. E. A. Kenik, Scripta Metall. 21, p. 811, ( 1987).
6. G. Cliff and G. W. Lorimer: Proc. Fifth European Congress on Electron Microscopy, p. 140, Institute of Physics, Bristol, 1972.
7. G. S. Was, T. R. Alien, J. T. Busby, J. Gan, D. Damcott, D. Carter, M. Atzmon and E. A. Kenik, J. Nucl. Mater., in press.
8. R.D. Carter, D.L. Damcott, M. Atzmon, G.S. Was, S.M. Bruemmer, and E. A. Kenik, J. Nucl. Mater. 211, p. 70, (1994).
9. J. M. Perks, A.D. Marwick, and C.A. English, Harwell Laboratory, Oxfordshire, UK, AERE R 12121, June 1986.
10. T. Allen, J. T. Busby, G. S. Was and E. A. Kenik, J. Nucl. Mater. 255, p. 44-58, (1998).
11. T. Allen, G. S. Was and E. A. Kenik, J. Nucl. Mater. 244, p. 278, (1997).
12. T. R. Allen and G. S. Was, Proc. Mater. Res. Soc., Materials Research Society, Pittsburgh, vol. 373, p. 101, 1995.
13. S.J. Rothman, L.J. Nowicki, and G.E. Murch, Journal of Physics F: Metal Physics 10, p. 383 (1980).
14. B. Million, J. Ruzickova, and J. Vrestal, Mated. Sci. Engin. 72, p. 85, (1985).
15. P. Cenedese, F. Bley, and S. Lefebvre, Acta Crystall. A40, p. 228, (1984).
16. A. D. Marwick, R. C. Piller, and T. E. Cranshaw, J. Phys F. Met. Phys. 17, p. 37, (1987).
17. A. Marucco, Mat. Sci. Eng., A189, p. 267, (1994).
18. C. Dimitrov, D. Huguenin, P. Moser, and O. Dimitrov, J. Nucl. Mater. 174, p. 22-34, (1990).
19. H. Wiedersich, P. R. Okamoto, and N. Q. Lam, J. Nucl.. Mater. 83, p. 98, (1979).
20. S. Watanabe and H. Takahashi, J. Nucl. Mater. 208, p. 191, (1994).
21. S. Dumbill, Ph.D. Thesis, University of Birmingham (1992).
22. F. A. Garner and A. S. Kumar, ASTM STP 955, Eds., F. A. Garner, N. H. Packan, and A. S. Kumar, American Society for Testing and Materials, Philadelphia 1987, p.289.