Ferromagnetism in LaFeO3-LaCrO3 superlattices

Science

Volumn 280, Issue 5366, 1998, Pages 1064-1066

  Ueda, Kenji ^a   Tabata, Hitoshi ^a   Kawai, Tomoji ^a  

^a OSAKA UNIVERSITY   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

CHROMIUM; FERRIC ION; FERROMAGNETIC MATERIAL; OXYGEN;

ARTICLE; ION EXCHANGE; MAGNETIC FIELD; MAGNETISM; MATHEMATICAL ANALYSIS; METAL BINDING; PRIORITY JOURNAL; REACTION ANALYSIS; X RAY DIFFRACTION;

EID: 0032524429     PISSN: 00368075     EISSN: None     Source Type: Journal    
DOI: 10.1126/science.280.5366.1064     Document Type: Article

References (14)

1. H. A. Kramers, Physical, 182 (1934).
2. P. W. Anderson, Phys. Rev. 79, 350 (1950).
3. J. B. Goodenough, ibid. 100, 564 (1955).
4. J. Kanamori, J. Phys. Chem. Solids 10, 87 (1959).
5. 4+, FM ordering was reported in the bulk sample [G. Blasse, J. Phys. Chem. Solids 26, 1969 (1965)].
6. A. Wold and W. Croft, J. Phys. Chem. 63, 447 (1959).
7. A. Belayachi, M. Nogues, J.-L. Dormann, M. Taibi, Eur. J. Solid State Inorg. Chem. 33, 1039 (1996).
8. K. P. Belov et al., Sov. Phys. Solid State 14, 813 (1972).
9. R. Aleorard, R. Pauthenet, J. P. Rebouillat, C. Veyret, J. Appl. Phys. 39, 379 (1968).
10. W. C. Koehler, E. O. Wollan, M. K. Wilkinson, Phys. Rev. 118, 58 (1960).
11. D. Treves, J. Appl. Phys. 36, 1033 (1965).
12. T. Kawai, M. Kanai, H. Tabata, Mater. Sci. Eng. 41, 123 (1996).
13. H. Tabata, T. Kawai, S. Kawai, Phys. Rev. Lett. 70, 2633 (1993).
14. 3, respectively, at a molar ratio of 1:1 and sintering them at 1000°C. The films were formed at 580°C in an oxygen/ozone (8%) ambient pressure of 1 mtorr. The deposition rate was 10 Å/min. All magnetic measurements were performed with a SQUID magnetometer (Quantum design MPMS-5S).