Ageing and cracking of simulated heat affected zones in 321 stainless steel

Materials at High Temperatures

Volumn 15, Issue 3-4, 1998, Pages 395-401

  Chabaud, M ^a   Allais, L ^a   Dubuisson, P ^a   Hogrel, C ^a   Pineau, A ^b  

^a CEA SACLAY   (France)

^b PSL RESEARCH UNIVERSITY   (France)

Author keywords

321 stainless steel; Heat affected zones

Indexed keywords

AGING OF MATERIALS; CRACK PROPAGATION; CREEP TESTING; EMBRITTLEMENT; FATIGUE OF MATERIALS; FINITE ELEMENT METHOD; HEAT AFFECTED ZONE; MATHEMATICAL MODELS; STRESS RELAXATION; STRESS RELIEF; TENSILE TESTING; WELDS;

STAINLESS STEEL 321; STRESS RELIEF CRACKING; THERMAL AGING;

STAINLESS STEEL;

EID: 0032315304     PISSN: 09603409     EISSN: None     Source Type: Journal    
DOI: 10.1080/09603409.1998.11689628     Document Type: Article

References (17)

1. C.F. Meitzner, Stress relief cracking in steels weldments. Welding Research Council Bulletin 211, 1-17 (1975).
2. C. Picker, Materials and structural integrity experience from PFR. Nucl. En., 31 (3), 207-219 (1992).
3. A. Leclou et al. Soudabilité des aciers austénitiques - détermination de la tendance à divers types de fissuration. Proc Conf journée métallurgie de la soudure. Marseille, pp. 1-32, 8-9 nov 1973.
4. V.V Ardentov et al. Forecasting of local failures in the heat affected zones of welded joints in 18-8 type austenitic steels. Welding production, 24 (1), 23-26 (1977).
5. R.N Younger, D.M Haddrill, and R.G Backer, Post-weld heat treatment of high temperature austenitic steels, JISI 693-698, August (1963).
6. R.J Christoffel, Notch-rupture strength of type 347 HAZ. Welding Res supple 315-320, July (1960).
7. R.J Truman and H.W Kirkby, Some ductility aspects of 18-12-1Nb steel JISI, 180-188, October (1960).
8. N.E Moore and J.A Griffiths, Microstructural causes of HAZ cracking in heavy section 18-12-Nb austenitic stainless steel welded joints, JISI 29-39, January (1961).
9. R.N Younger and R.G Baker, Heat affected zone cracking in welded austenitic steels during treatment. Br Welding J, 579-587, December (1961).
10. M. Yoshida, C. Levaillant, R. Piques, A. Pineau, Quantitative study of intergranular damage in austenitic stainless steel on smooth and notched bars. Proc Conf on high temperature fracture mechanisms and mechanics. Dourdan, pp. 3-21, October (1987).
11. CEA / DMT, Castem 2000, code de calcul par éléments finis. Manuel d'Utilisation, Saclay, France (1997).
12. A. Diboine, Influence de la triaxialité des contraintes sur la cavitation intergranulaire par fluage dans acier inoxydable austénitique. Mém DEA à l'ENSMP (1982).
13. M. Yoshida, Endommagement intergranulaire de fluage dans un acier inoxydable 17Cr-12Ni. Etude quantitative. Rôle de la multiaxialité des contraintes. Thèse à l'ENSMP (1985).
14. R. Piques, Mécanique et mécanisme de l'amorçage et de la propagation des fissures en viscoplasticité dans un acier inoxydable austénitique. Thèse à l'ENSMP (1989).
15. J.M Adamson and J.W Martin, Effect of niobium content on the steady state creep of stabilized 20Cr-25Ni austenitic stainless steels, Proc of conf on creep strength in steels and high temperature alloys, Sheffield. The Metal Society, pp. 99-105 (1972).
16. J.D Cook, D.R Harries, and A.C Roberts, Some factors affecting the creep strength of 20Cr-25-Ni-Nb austenitic sleel at 750°C. Proc Conf on creep strength in steels and high temperature alloys, Sheffield. The Metal Society, pp. 91-98 (1972).
17. J.M Silcock and Willoughby, Low stress creep tests of Nb stabilized austenitic steels. Proc of conf creep strength in steels and high temperature alloys, Sheffield. The Metal Society, pp. 122-133 (1972).