Decomposition kinetics, arrhenius parameters, and bond dissociation energies for alkoxyamines of relevance in "living" free radical polymerization

Macromolecules

Volumn 31, Issue 25, 1998, Pages 9103-9105

  Skene, W G ^a   Belt, S T ^b   Connolly, T J ^a   Hahn, Peter ^a   Scaiano, J C ^a  

^a UNIVERSITY OF OTTAWA   (Canada)

^b UNIVERSITY OF PLYMOUTH   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

ACTIVATION ENERGY; ALCOHOLS; AMINES; CHEMICAL BONDS; DISSOCIATION; ENTROPY; FREE RADICAL POLYMERIZATION; GROUND STATE; ORGANIC SOLVENTS; PHOTOLYSIS; POLYESTERS; RATE CONSTANTS;

ALKOXYAMINES; ARRHENIUS PLOTS; THERMOLYSIS;

INITIATORS (CHEMICAL);

EID: 0032291931     PISSN: 00249297     EISSN: None     Source Type: Journal    
DOI: 10.1021/ma9812229     Document Type: Article

References (32)

1. Rizzardo, E.; Solomon, D. H. Polym. Bull. 1979, 1, 529. Moad, G.; Rizzardo, E.; Solomon, D. H. Tetrahedron Lett. 1981, 22, 1165. Moad, G.; Rizzardo, E.; Solomon, D. H. Macromolecules 1982, 15, 909. Moad, G.; Rizzardo, E.; Solomon, D. H. Polym. Bull. 1982, 6, 589. Beckwith, A. L. J.; Bowry, V. W.; O'Leary, M.; Moad, G.; Rizzardo, E.; Solomon, D. H. J. Chem. Soc., Chem. Commun. 1986, 1003.
2. Rizzardo, E.; Solomon, D. H. Polym. Bull. 1979, 1, 529. Moad, G.; Rizzardo, E.; Solomon, D. H. Tetrahedron Lett. 1981, 22, 1165. Moad, G.; Rizzardo, E.; Solomon, D. H. Macromolecules 1982, 15, 909. Moad, G.; Rizzardo, E.; Solomon, D. H. Polym. Bull. 1982, 6, 589. Beckwith, A. L. J.; Bowry, V. W.; O'Leary, M.; Moad, G.; Rizzardo, E.; Solomon, D. H. J. Chem. Soc., Chem. Commun. 1986, 1003.
3. Rizzardo, E.; Solomon, D. H. Polym. Bull. 1979, 1, 529. Moad, G.; Rizzardo, E.; Solomon, D. H. Tetrahedron Lett. 1981, 22, 1165. Moad, G.; Rizzardo, E.; Solomon, D. H. Macromolecules 1982, 15, 909. Moad, G.; Rizzardo, E.; Solomon, D. H. Polym. Bull. 1982, 6, 589. Beckwith, A. L. J.; Bowry, V. W.; O'Leary, M.; Moad, G.; Rizzardo, E.; Solomon, D. H. J. Chem. Soc., Chem. Commun. 1986, 1003.
4. Rizzardo, E.; Solomon, D. H. Polym. Bull. 1979, 1, 529. Moad, G.; Rizzardo, E.; Solomon, D. H. Tetrahedron Lett. 1981, 22, 1165. Moad, G.; Rizzardo, E.; Solomon, D. H. Macromolecules 1982, 15, 909. Moad, G.; Rizzardo, E.; Solomon, D. H. Polym. Bull. 1982, 6, 589. Beckwith, A. L. J.; Bowry, V. W.; O'Leary, M.; Moad, G.; Rizzardo, E.; Solomon, D. H. J. Chem. Soc., Chem. Commun. 1986, 1003.
5. Rizzardo, E.; Solomon, D. H. Polym. Bull. 1979, 1, 529. Moad, G.; Rizzardo, E.; Solomon, D. H. Tetrahedron Lett. 1981, 22, 1165. Moad, G.; Rizzardo, E.; Solomon, D. H. Macromolecules 1982, 15, 909. Moad, G.; Rizzardo, E.; Solomon, D. H. Polym. Bull. 1982, 6, 589. Beckwith, A. L. J.; Bowry, V. W.; O'Leary, M.; Moad, G.; Rizzardo, E.; Solomon, D. H. J. Chem. Soc., Chem. Commun. 1986, 1003.
6. Georges, M. K.; Veregin, R. P. N.; Kazmaier, P. M.; Hamer, G. K. Macromolecules 1993, 26, 2987.
7. Connolly, T. J.; Baldovi, M. V.; Mohtat, N.; Scaiano, J. C. Tetrahedron Lett. 1996, 37, 4919.
8. Baldovi, M. V.; Mohtat, N.; Scaiano, J. C. Macromolecules 1996, 29, 5497.
9. Moad, G.; Rizzardo, E. Macromolecules 1995, 28, 8722.
10. Hawker, C. J. J. Am. Chem. Soc. 1994, 116, 11185.
11. Veregin, R. P. N.; Georges, M. K.; Hamer, G. K.; Kazmaier, P. M. Macromolecules 1995, 28, 4391.
12. Kazmaier, P. M.; Moffat, K. M.; Georges, M. K.; Veregin, R. P. N.; Hamer, G. K. Macromolecules 1995, 28, 1841.
13. Puts, R. D.; Sogah, D. Y. Macromolecules 1996, 29, 3323.
14. Veregin, R. P. N.; Odell, P. G.; Michalak, L. M.; Georges, M. K. Macromolecules 1996, 29, 2746.
15. Odell, P. G.; Veregin, R. P. N.; Michalak, L. M.; Brousmiche, D.; Georges, M. K. Macromolecules 1995, 28, 8453.
16. Engel, P. S.; Duan, S.; Arhancet, G. B. J. Org. Chem. 1997, 62, 3537.
17. Stipa, P.; Greci, L.; Carloni, P.; Damiani, E. Polym. Degrad. Stab. 1997, 55, 323.
18. Li, I.; Howell, B. A. Macromolecules 1995, 28, 6692.
19. Veregin, R. P. N.; Kazmaier, P. M.; Odell, P. G.; Georges, M. K. Chem. Lett. 1997, 5, 467.
20. Goto, A.; Rerauchi, T.; Fukuda, T.; Miyamoto, T. Macromolecules 1997, 18, 3373.
21. Fukuda, T.; Tsujii, Y.; Miyamoto, T. Polym. Prepr. 1997, 38, 723.
22. Veregin, R. P. N.; Odell, P. G.; Michalak, L. M.; Georges, M. K. Macromolecules 1996, 29, 4161.
23. Fischer, H. Macromolecules 1997, 30, 5666.
24. Typical initial concentrations are 20 mM for the alkoxyamine and 60 mM for the nitroxide trap.
25. Beckwith, A. L. J.; Bowry, V. W.; Ingold, K. U. J. Am. Chem. Soc. 1992, 114, 4983.
26. Bowry, V. W.; Ingold, K. U. J. Am. Chem. Soc. 1992, 114, 4992.
27. Fischer, H. J. Am. Chem. Soc. 1986, 108, 3925.
28. HPLC analyses were carried out using a Zorbax SB-C18 reverse-phase column with 85:15 methanol/water as eluent. The flow rate was 0.5 mL/min for the first 12 min and 1.5 mL/min after that. Results are based on products formed rather than comsumption of starting material, since at the low conversions used the latter is subject to considerable errors. Product concentrations (coupling and traces of disproportionation) were determined against authentic samples.
29. Batt, L.; Christie, K.; Milne, R. T.; Summers, A. Int. J. Chem. Kinet. 1974, 6, 877.
30. Hawker, C. J.; Barclay, G. G.; Orellana, A.; Dao, J.; Devonport, W. Macromolecules 1996, 29, 5245.
31. Chateauneuf, J.; Lusztyk, J.; Ingold, K. U. J. Org. Chem. 1988, 53, 1629.
32. Kothe, T.; Marque, S.; Martschke, R.; Popov, M.; Fischer, H. J. Chem. Soc., Perkin Trans. 2 1998, 1553.