A damage zone model for the failure analysis of adhesively bonded joints

International Journal of Adhesion and Adhesives

Volumn 18, Issue 6, 1998, Pages 385-400

  Sheppard, Andrew ^a,b   Kelly, Don ^a,b   Tong, Liyong ^a,c  

^a Coop Res Ctr Adv Compos S ^*  (Australia)

^b UNIVERSITY OF NEW SOUTH WALES   (Australia)

^c UNIVERSITY OF SYDNEY   (Australia)

Author keywords

B. composites; C. finite element stress analysis; C. joint design; Strength of bonded joints

Indexed keywords

ADHESIVELY BONDED JOINTS; DAMAGE ZONE MODEL;

ADHESIVE JOINTS; COMPOSITE STRUCTURES; FAILURE ANALYSIS; FINITE ELEMENT METHOD; LOADS (FORCES); MATHEMATICAL MODELS; STRESS ANALYSIS;

BOND STRENGTH (MATERIALS);

EID: 0032275825     PISSN: 01437496     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0143-7496(98)00024-4     Document Type: Article

References (59)

1. Grant P, Lewington JA. Some important considerations in the design of composite bonded joints in aerospace structures. Can Aeronautics Space J 1987;33(2):91-8.
2. Hart-Smith LJ. Adhesive-bonded double lap joints. NASA, CR-112235, January 1973.
3. Harris J, Adams R. Strength prediction of bonded single lap joints by non-linear finite element methods. Int J Adhesion Adhesives 1984;4(2):65-78.
4. Adams RD, Atkins RW, Harris JA, Kinloch, AJ. Stress analysis and failure properties of carbon-fibre-reinforced-plastic/steel double-lap joints. J Adhesion 1986;20:29-53.
5. Adams RD, Harris JA. The influence of local geometry on the strength of adhesive joints. Int J Adhesion Adhesives, 1987;7(2): 69-80.
6. Adams RD, Strength predictions for lap joints, especialy with composite adherends. A review, J Adhesion, 1989;30:219-242.
7. Czarnocki P, Piekarski K. Fracture strength of an adhesive-bonded joint', Int J Adhesion Adhesives 1986;6(2):93-5.
8. Hollaway L, Romhi A, Gunn M. Optimisation of adhesive bonded composite tubular sections. Composite Struct 1990; 16:125-170.
9. Lee Su Jeong, Lee Dai Gil. Development of a failure model for the adhesively bonded tubular single lap joint. J Adhesion 1992; 40:1-14.
10. Mori K, Sugibayashi T. Predicting the strength of stepped-lap bonded joint with adhesive resin under tensile shear load. JSME Int J Ser I 1990;33(3):349-55.
11. Long R, Static strength of adhesively bonded ARALL-1 joints. J Composite Mater 1991;25:391-415.
12. Sato C, Ikegami K. Tensile strength of single lap joint and scarf joint between CFRP and carbon steel. J Adhesion 1992;39:29-41.
13. Ikegami K, Takeshita T, Matsuo K, Sugibayashi T. Strength of adhesively bonded scarf joints between glass fibre-reinforced plastics and metals. Int J Adhesion Adhesives 1990;10(3):199-206.
14. Hachenberg D, Kossira H. Stringer peeling effects at stiffened composite panels in the postbuckling range. J Aircraft 1993;30(5): 769-776.
15. Delale, F. Stress singularities in bonded anisotropic materials. Int J Solids Struct 1984;20(1):31-40.
16. Hein VL, Erdogan F. Stress singularities in a two-material wedge. Int J Fracture Mech 1971;7(3):317-30.
17. Hattori T. A stress-singularity-parameter approach for evaluating the adhesive strength of single-lap joints. JSME Int J Ser I 1991;34(3):326-31.
18. Haruna K, Hamada H, Maekawa Z. Mechanical behavior of CFRP adhesive joints with thin adherends. In: Hui D, editor. Proc of Int Conf on Composites Engineering, 1994;739-40.
19. Groth HL. Stress singularities and fracture at interface corners in bonded joints., Int J Adhesion Adhesives 1988;8(2):107-13.
20. Crocombe A. Global yielding as a failure criterion for bonded joints. Int J Adhesion Adhesives 1989:9(3).
21. Suo Z. Failure of brittle adhesive joints. Appl Mech Rev 1990; 5(Part 2):s276-9.
22. Anandarajah A, Vardy AE. Mode I and II fracture of Adhesive joints. J Strain Anal 1984;19(3):173-83.
23. Anderson GP, Brinton DH, Ninow KJ, DeVries KL. A fracture mechanics approach to predicting bond strength. Proc American Society of Mechanical Engineers, Materials Division, MD Vol. 6, New York: ASME, pp. 93-9.
24. Lee SM. An in-situ failure model for adhesive joints. J Adhesion 1985;18:1-15.
25. Fernlund G, Papini M, McCammond D, Spelt JK. fracture load predictions for adhesive joints. Composites Sci Technol 1994;51: 587-600.
26. Fernlund G, Spelt JK. Mixed-mode fracture characterization of adhesive joints. Composites Sci Technol 1994;50:441-9.
27. Fernlund G, Spelt JK. Mixed mode energy release rates for adhesively bonded beam specimens. J Composites Technol Res 1994;16(3):234-43.
28. Papini M, Fernlund G, Spelt JK. Effect of crack-growth mechanism on the prediction of fracture load of adhesive joints. Composites Sci Technol 1994;52:561-70.
29. Xiao J, Bathias C. Damage and fracture of notched non-woven and woven composite laminates. Composites Sci Technol 1994; 52:99-108.
30. Wisnom MR. Shear fracture of unidirectional composites without initial cracks. Composites Sci Technology 1994;52:9-17.
31. Knauss WG, Losi GU. Crack propagation in a nonlinearly viscoelastic solid with relevance to adhesive bond failure. J Appl Mech 1993;60:793-801.
32. Laksimi A, Gong XL, Benzeggagh ML. Analysis of damage mechanisms in a centrally notched glass-fiber/epoxy plate. Composites Sci Technol 1994;52:85-91.
33. Chai H. Observation of deformation and damage at the tip of cracks in adhesive bonds loaded in shear and assessment of a criterion for fracture. Int J Fracture 1993;60:311-26.
34. Chai H. Deformation and failure of adhesive bonds under shear loading. J Mater Sci 1993;28:4944-56.
35. Hibbs MF, Bradley WL. Correlations between micromechanical failure processes and the delamination toughness of graphite/epoxy systems. In: Masters JE, Au JJ, editors. Fractography of modern engineering materials: composites and metals, ASTM STP 948. Philadelphia: American Society for Testing and Materials, 1987:68-97.
36. Purslow D. Matrix fractography of fibre-reinforced epoxy composites. Composites 1986;17(4):289-303.
37. Smith BW, Grove RA. Determination of crack propagation directions in graphite/epoxy structures. In: Master JE, Au JJ, editors. Fractography of modern engineering materials: composites and metals, ASTM STP 948. Philadelphia: American Society for Testing and Materials, 1987:154-73.
38. Whitney J, Nuismer R. Stress fracture criteria for laminated composites containing stress concentrations. J Composite Mater 1974;8:253-65.
39. McClintock FA. Ductile fracture instability in shear. J Appl Mech, Trans ASME, December 1958:582-87.
40. Clark JD, McGregor IJ. Ultimate tensile stress over a zone: a new failure criterion for adhesive joints. J Adhesion 1993; 42:227-45.
41. John SJ. Predicting the strength of bonded carbon fibre/epoxy composite joints. In: Damico DJ, Wilkinson TL, Niks SLF, editors. Composites bonding, ASTM STP 1227. Philadelphia: ASTM, 1994;45-59.
42. John SJ, Kinloch AJ, Matthews FL. Measuring and predicting the durability of bonded carbon fibre/epoxy composite joints. Composites 1991;22(2):121-6.
43. Simo JC, Ju JW. Strain- and stress-based continuum damage models - I. formulation. Int J Solids Struct 1987;23(7):821-40.
44. Edlund U, Klarbring A. A coupled elastic-plastic damage model for rubber-modified epoxy adhesives. Int J Solids Struct 1993; 30(19):2693-708.
45. Edlund U. Surface adhesive joint description with coupled elastic-plastic damage behaviour and numerical applications. Coput Meth Appl Mech Eng 1994;115:253-76.
46. Brewer J, Lagace P. Quadratic stress criterion for initiation of delamination. J of Composite Mater 1988;22:1141-55.
47. Kim R, Soni S. Failure of composite laminates due to combined interlaminar normal and shear stresses. In: Kawata K, Umekawa S, Koyabashi A, editors. Composites '86: recent advances in Japan and the United States. Proc. Japan-U.S. CCM-III, Japan, 1986; 341-50.
48. Kim RY, Soni, SR. Experimental and analytical studies on the onset of delamination in laminated composites. J. Composite Mater 1984;18:70-80.
49. Soni SR, Kim RY. Delamination of composite laminates stimulated by interlaminar shear. In: Whitney JM, editor. Composite materials: testing and design. 7th Conference, ASTM STP 893, Philadelphia: American Society for Testing and Materials, 1986: 286-307.
50. Joo J, Sun C. A failure criterion for laminates governed by free edge interlaminar shear stress. J. Composite Mater 1992;26(10): 1510-22.
51. Fish J, Lee S. Delamination of tapered composite structures. Eng Fracture Mech 1989;34(1):43-54.
52. Dávila C, Johnson E. Analysis of delamination initiation in postbuckled dropped-ply laminates. AIAA J 1993;31(4):721-7.
53. Beaumont PW, Schultz JM. Macroscopic fracture theories. In: Beaumont PW, Schultz JM, Friedrich K. editors. Failure analysis of composite materials, Delaware composites design encyclopedia. Lancaster, U.S.A., Technomic Pub. Co., 1990:83-115.
54. Zhu FY, Kelly DW, Patterson C. An application of a post-yield crack algorithm. In: Valliappan S, Pulmana VA, Tim-Loi F. editors. Computational mechanics. Balkemna Publishers, 1993; 713-7.
55. Copeland E. The importance of peel stress on the fatigue behaviour of adhesively bonded joints. Undergraduate Thesis, School of Materials Science and Engineering, The University of New South Wales, 1994.
56. Lee CC. In-situ and bulk testing of adhesives. PhD Thesis, School of Material Science and Engineering, University of New South Wales, Australia, 1997.
57. MSC/NASTRAN. In: Reymond M, Miller M, editors. Quick reference guide, Version 68. The MacNeal-Schwendler Corporation, 1994.
58. Sheppard A. Failure analysis of adhesively bonded joints. PhD Thesis, School of Mechanical and Manufacturing Engineering, University of New South Wales, Australia, 1996.
59. Tong L, Sheppard A, Kelly D, Chalkley P. Postbuckling induced failure in adhesively bonded composite panel-to-flange joints. Composites B 1998; 29(3):287-98.