Volumn 21, Issue 12, 1998, Pages 1435-1446

Corrosion fatigue fracture behaviour of a SiC whisker-aluminium matrix composite under combined tension-torsion loading

Author keywords

Combined stress; Composite material; Environmental effect; Fatigue; Metal matrix composite; Tension torsion loading

Indexed keywords

ALUMINUM ALLOYS; CORROSION FATIGUE; CRACK INITIATION; HYDROGEN EMBRITTLEMENT; PITTING; SILICON CARBIDE; SODIUM CHLORIDE; STRESS ANALYSIS; STRESS INTENSITY FACTORS; TENSILE TESTING;

EID: 0032268993     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1046/j.1460-2695.1998.00127.x     Document Type: Article
Times cited : (7)

References (25)
  • 2
    • 0000745771 scopus 로고
    • Fatigue of discontinuous reinforced metal matrix composites
    • (Edited by R. K. Everett and R. J. Arsenault), Academic Press, San Diego, CA, USA
    • J. K. Shang and R. O. Ritchie (1991) Fatigue of discontinuous reinforced metal matrix composites. In: Metal Matrix Composites: Mechanisms and Properties (Edited by R. K. Everett and R. J. Arsenault), Academic Press, San Diego, CA, USA, pp. 255-288.
    • (1991) Metal Matrix Composites: Mechanisms and Properties , pp. 255-288
    • Shang, J.K.1    Ritchie, R.O.2
  • 3
    • 0028405181 scopus 로고
    • Fracture behaviour of SiC whisker reinforced aluminum alloy under combined tension/torsion loading at room and elevated temperatures
    • K. Komai, K. Minoshima and G. Yoshida (1994) Fracture behaviour of SiC whisker reinforced aluminum alloy under combined tension/torsion loading at room and elevated temperatures. Trans. Japan Soc. Mech. Eng. 60, 1080-1087.
    • (1994) Trans. Japan Soc. Mech. Eng. , vol.60 , pp. 1080-1087
    • Komai, K.1    Minoshima, K.2    Yoshida, G.3
  • 4
    • 0030235151 scopus 로고    scopus 로고
    • Fatigue fracture behaviour of SiC whisker/aluminum matrix composite under out-of-phase tension/torsion combined loading
    • K. Minoshima, S. Satoh and K. Komai (1996) Fatigue fracture behaviour of SiC whisker/aluminum matrix composite under out-of-phase tension/torsion combined loading. Trans. Japan Soc. Mech. Eng. 62, 2001-2007.
    • (1996) Trans. Japan Soc. Mech. Eng. , vol.62 , pp. 2001-2007
    • Minoshima, K.1    Satoh, S.2    Komai, K.3
  • 5
    • 0026394333 scopus 로고
    • Review of corrosion studies on aluminium metal matrix composite
    • A. Turnbull (1992) Review of corrosion studies on aluminium metal matrix composite. Br. Corros. J. 27, 27-35.
    • (1992) Br. Corros. J. , vol.27 , pp. 27-35
    • Turnbull, A.1
  • 6
    • 0026899149 scopus 로고
    • Galvanic corrosion of aluminum-matrix composites
    • L. H. Hihara and R. M. Latanision (1992) Galvanic corrosion of aluminum-matrix composites. Corrosion 48, 546-552.
    • (1992) Corrosion , vol.48 , pp. 546-552
    • Hihara, L.H.1    Latanision, R.M.2
  • 8
    • 0020937872 scopus 로고
    • Corrosion fatigue of SiC/Al metal matrix composite in salt ladened moist air
    • (Edited by R. C. Gifkins), Pergamon, Oxford
    • C. R. Crowe and D. F. Hasson (1982) Corrosion fatigue of SiC/Al metal matrix composite in salt ladened moist air. In: Strength of Metals and Alloys (Edited by R. C. Gifkins), Pergamon, Oxford, pp. 859-865.
    • (1982) Strength of Metals and Alloys , pp. 859-865
    • Crowe, C.R.1    Hasson, D.F.2
  • 9
    • 0025767544 scopus 로고
    • Environmental and frequency effects on fatigue crack growth rates in aluminum-silicon carbide composites
    • (Edited by R. H. Jones and R. E. Ricker), The Minerals, Metals & Materials Society, Warrendale, PA, USA
    • R. F. Buck and A. W. Thompson (1991) Environmental and frequency effects on fatigue crack growth rates in aluminum-silicon carbide composites. In: Environmental Effects on Advanced Materials (Edited by R. H. Jones and R. E. Ricker), The Minerals, Metals & Materials Society, Warrendale, PA, USA, pp. 297-313.
    • (1991) Environmental Effects on Advanced Materials , pp. 297-313
    • Buck, R.F.1    Thompson, A.W.2
  • 10
    • 0027269191 scopus 로고
    • Tensile and fatigue fracture behaviour and water-environment effects in SiC-whisker/7075-aluminum composite
    • K. Komai, K. Minoshima and H. Ryoson (1993) Tensile and fatigue fracture behaviour and water-environment effects in SiC-whisker/7075-aluminum composite. Composites Sci. Technol. 46, 59-66.
    • (1993) Composites Sci. Technol. , vol.46 , pp. 59-66
    • Komai, K.1    Minoshima, K.2    Ryoson, H.3
  • 11
    • 0028429309 scopus 로고
    • Corrosion fatigue of SiC whisker or SiC particulate reinforced 6061 aluminum alloy
    • S. Y. Yu, H. Ishii and K. Tohgo (1994) Corrosion fatigue of SiC whisker or SiC particulate reinforced 6061 aluminum alloy. Fatigue Fract. Engng Mater. Struct. 17, 571-578.
    • (1994) Fatigue Fract. Engng Mater. Struct. , vol.17 , pp. 571-578
    • Yu, S.Y.1    Ishii, H.2    Tohgo, K.3
  • 12
    • 0023307159 scopus 로고
    • The influence of small vibratory stresses and anisotropy of grains on SCC strength in aluminum alloys
    • K. Komai, K. Minoshima and Y. Nishide (1987) The influence of small vibratory stresses and anisotropy of grains on SCC strength in aluminum alloys. JSME Int. J. 30, 401-407.
    • (1987) JSME Int. J. , vol.30 , pp. 401-407
    • Komai, K.1    Minoshima, K.2    Nishide, Y.3
  • 13
    • 0024771366 scopus 로고
    • Mechanical conditions dominating cyclic stress corrosion cracks of high-strength steel under combined cyclic/static multiaxial loads
    • K. Minoshima, T. Kiuchi and K. Komai (1989) Mechanical conditions dominating cyclic stress corrosion cracks of high-strength steel under combined cyclic/static multiaxial loads. Trans. Japan Soc. Mech. Eng. 55, 2277-2284.
    • (1989) Trans. Japan Soc. Mech. Eng. , vol.55 , pp. 2277-2284
    • Minoshima, K.1    Kiuchi, T.2    Komai, K.3
  • 14
    • 0024032966 scopus 로고
    • Crack initiation behaviour of cyclic SCC under bending and torsional loads in high-strength steel
    • K. Minoshima, A. Ohkubo and K. Komai (1988) Crack initiation behaviour of cyclic SCC under bending and torsional loads in high-strength steel. J. Soc. Mater. Sci., Japan 33, 670-675.
    • (1988) J. Soc. Mater. Sci., Japan , vol.33 , pp. 670-675
    • Minoshima, K.1    Ohkubo, A.2    Komai, K.3
  • 15
    • 0019030518 scopus 로고
    • Hydrogen-induced slow crack growth in Ti-6Al-6V-2Sn
    • N. R. Moody and W. W. Gerberich (1980) Hydrogen-induced slow crack growth in Ti-6Al-6V-2Sn. Metallurg. Trans. 11A, 973-981.
    • (1980) Metallurg. Trans. , vol.11 A , pp. 973-981
    • Moody, N.R.1    Gerberich, W.W.2
  • 16
    • 0015300738 scopus 로고
    • A new model for hydrogen-assisted cracking (hydrogen 'embrittlement')
    • C. D. Beachem (1972) A new model for hydrogen-assisted cracking (hydrogen 'embrittlement'). Metallurg. Trans. 3, 437-451.
    • (1972) Metallurg. Trans. , vol.3 , pp. 437-451
    • Beachem, C.D.1
  • 17
    • 0023422302 scopus 로고
    • The influence of hydrogen on deformation and fracture processes in high-strength aluminum alloys
    • G. M. Bond, I. M. Robertson and H. K. Birnbaum (1987) The influence of hydrogen on deformation and fracture processes in high-strength aluminum alloys. Acta Metall. 35, 2289-2296.
    • (1987) Acta Metall. , vol.35 , pp. 2289-2296
    • Bond, G.M.1    Robertson, I.M.2    Birnbaum, H.K.3
  • 18
    • 0028401434 scopus 로고
    • Hydrogen-enhanced localized plasticity - A mechanism for hydrogen-related fracture
    • H. K. Birnbaum and P. Sofronis (1994) Hydrogen-enhanced localized plasticity - a mechanism for hydrogen-related fracture. Mater. Sci. Engng A176, 191-202.
    • (1994) Mater. Sci. Engng , vol.A176 , pp. 191-202
    • Birnbaum, H.K.1    Sofronis, P.2
  • 20
    • 0023697825 scopus 로고
    • Corrosion fatigue crack initiation of high-tensile-strength steels in synthetic seawater
    • K. Komai, K. Minoshima, S. Kinoshita and G. Kim (1988) Corrosion fatigue crack initiation of high-tensile-strength steels in synthetic seawater. JSME Int. J. 31, 606-612.
    • (1988) JSME Int. J. , vol.31 , pp. 606-612
    • Komai, K.1    Minoshima, K.2    Kinoshita, S.3    Kim, G.4
  • 21
    • 0022488994 scopus 로고
    • Influence of vibratory stresses on initiation of stress corrosion cracking in high-strength steel
    • K. Komai, K. Minoshima and T. Fujito (1986) Influence of vibratory stresses on initiation of stress corrosion cracking in high-strength steel. Trans. Japan Inst. Metals 27, 23-31.
    • (1986) Trans. Japan Inst. Metals , vol.27 , pp. 23-31
    • Komai, K.1    Minoshima, K.2    Fujito, T.3
  • 22
    • 0023457237 scopus 로고
    • Prediction method of corrosion fatigue crack initiation life based on corrosion pit growth
    • Kondo, K. (1983) Prediction method of corrosion fatigue crack initiation life based on corrosion pit growth. Trans. Japan Soc. Mech. Eng. 53, 1983-1987.
    • (1983) Trans. Japan Soc. Mech. Eng. , vol.53 , pp. 1983-1987
    • Kondo, K.1
  • 24
    • 0019658622 scopus 로고
    • An empirical stress intensity factor equation for the surface crack
    • J. C. Newman Jr and I. S. Raju (1981) An empirical stress intensity factor equation for the surface crack. Engng Fracture Mech. 15, 185-192.
    • (1981) Engng Fracture Mech. , vol.15 , pp. 185-192
    • Newman Jr., J.C.1    Raju, I.S.2
  • 25
    • 0001141775 scopus 로고
    • Influence of processing variables on the corrosion susceptibility of metal-matrix composites
    • R. C. Paciej and V. S. Agarwala (1988) Influence of processing variables on the corrosion susceptibility of metal-matrix composites. Corrosion 44, 680-684.
    • (1988) Corrosion , vol.44 , pp. 680-684
    • Paciej, R.C.1    Agarwala, V.S.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.