Comparison of stress corrosion cracking susceptibility of thermally-sensitized and proton-irradiated 304 stainless steel using electrochemical noise techniques

Journal of Nuclear Materials

Volumn 258-263, Issue PART 2 B, 1998, Pages 2046-2053

  Wang, L H ^a   Kai, J J ^b   Tsai, C H ^b   Fong, C ^a  

^a INDUSTRIAL TECHNOLOGY RESEARCH INSTITUTE   (Taiwan)

^b NATIONAL TSING HUA UNIVERSITY   (Taiwan)

Author keywords

[No Author keywords available]

Indexed keywords

ELECTROCHEMISTRY; GRAIN BOUNDARIES; PROTON IRRADIATION; RADIATION HARDENING; SCANNING ELECTRON MICROSCOPY; SEGREGATION (METALLOGRAPHY); STRESS CORROSION CRACKING;

ELECTROCHEMICAL NOISE TECHNIQUES;

STAINLESS STEEL;

EID: 0032181906     PISSN: 00223115     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0022-3115(98)00420-6     Document Type: Article

References (9)

1. W.J. Liu, C.H. Tsai, J.J. Kai, Proceedings of the Sixth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, 1993, p. 591.
2. A.J. Jacobs, R.E. Clausing, L. Heatherly, R.M. Kruger, Proceedings of the 14th International Symposium on Effects of Radiation on Materials, ASTM, Philadelphia, PA, 1988.
3. K. Fukuya et al., Proceedings of the Fifth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, 1991, p. 821.
4. M. Kodama et al., Proceedings of the 14th International Symposium on Effects of Radiation of Materials, ASTM, Philadelphia, PA, 1992.
5. J.R. Kearns et al. (Eds.), Electrochemical Noise Measurement for Corrosion Measurement, ASTM, Philadelphia, PA, 1994, STP-1277.
6. J. Stewart, D.B. Wells, P.M. Scott, D.E. Williams, Corrosion Science 33 (1992) 73.
7. G.S. Was, T. Allen, J. Nucl. Mater. 205 (1993) 332.
8. J.J. Kai et al., Proceedings of the Eighth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems (in press).
9. S.M. Bruemmer et al., Proceedings of the Sixth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, 1993, p. 537.