Corrosion of Alloy 625 in Aqueous Solutions Containing Chloride and Oxygen

Corrosion

Volumn 54, Issue 10, 1998, Pages 824-834

  Kritzer, P ^a   Boukis, N ^a   Dinjus, E ^a  

^a KARLSRUHE INSTITUTE OF TECHNOLOGY   (Germany)

Author keywords

Alloy 625; Hydrochloric acid; Intergranular corrosion; Oxygen; Pitting; Pressure; Supercritical water; Temperature; Transgranular stress corrosion cracking; Transpassive dissolution

Indexed keywords

CHLORINE COMPOUNDS; DISSOLUTION; HYDROCHLORIC ACID; NICKEL ALLOYS; OXIDATION; OXYGEN; PITTING; PRESSURE; SOLUTIONS; STRESS CORROSION CRACKING;

CHLORIDES; INTERGRANULAR CORROSION; SUPERCRITICAL WATER; TEST REACTORS; TRANSGRANULAR STRESS CORROSION CRACKING; TRANSPASSIVE DISSOLUTION;

CORROSION RESISTANT ALLOYS;

EID: 0032173596     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3284802     Document Type: Article

References (72)

1. N. Boukis, N. Claussen, K. Ebert, R. Janssen, M. Schacht, J. Eur. Ceram. Soc. 17 (1997): p. 71.
2. M. Schacht, N. Boukis, E. Dinjus, K. Ebert, K. Janssen, F. Mescnke, N. Claussen, Key Eng. Mater. 132-136 (1997): p. 1,677.
3. N. Boukis, R. Landvatter, W. Habicht, G. Franz, S. Leistikow, R. Kraft, O. Jacobi, "First Experimental SCWO Corrosion Results of Ni-Based Alloys Fabricated as Pressure Tubes and Exposed to Oxygen-Containing Diluted Hydrochloric Acid at T ≤ 450°C, P = 24 MPa," Proc. 1st Int. Workshop Supercritical Water Oxidation (Lake Bluff, IL: WCM Forums, 1995).
4. N. Boukis, G. Franz, C. Friedrich, W. Habicht, K. Ebert, "Corrosion Screening Tests with Ni-Based Alloys in Supercritical Water Containing Hydrochloric Acid and Oxygen," HTD 335, Proc. ASME Heat Transfer Division, vol. 4 (Metals Park, OH: ASME, 1996), p. 159.
5. N. Boukis, P. Kritzer, "Corrosion Phenomena on Alloy 625 in Aqueous Solutions Containing Hydrochloric Acid and Oxygen Under Subcritical and Supercritical Conditions," CORROSION/ 97, paper no. 10 (Houston, TX: NACE, 1997).
6. H.E. Barner, C.Y. Huang, T. Johnson, G. Jacobs, M.A. Martch, W.R. Killilea, J. Hazardous Mater. 31 (1992): p. 1.
7. S. Huang, K. Daehling, T.E. Carleson, P. Taylor, C. Wai, A. Propp, "Thermodynamic Analysis of Corrosion of Iron Alloys in Supercritical Water," in Supercritical Science and Technology, ACS Symposium Series 406 (Washington, DC: ACS, 1989), p. 276.
8. T.T. Bramlette, B.E. Mills, K.R. Hencken, M.E. Brynildson, S.C. Johnston, J.M. Hruby, H.C. Feemster, B.C. Odegard, M. Modell, "Destruction of DOE/DP Surrogate Wastes with Supercritical Water Oxidation Technology," Sandia National Laboratories SAND90-8229 (1991).
9. D.B. Mitton, J.C. Orzalli, R.M. Latanision, "Corrosion Phenomena Associated with SCWO Systems," Proc. 3rd Int. Symp. Supercritical Fluids, vol. 3 (Vandoeuvre-les-Nancy Cedex, France: Int. Soc. Advancement Supercritical Fluids, 1994), p. 43.
10. R.M. Latanision, R.W. Shaw, "Corrosion in Supercritical Water Oxidation Systems," Workshop Summary, The Energy Laboratory, MIT-EL 93-006 (Cambridge, MA: Massachusetts Institute of Technology, 1993).
11. G. Hong, D.W. Ordway, V.A. Zilberstein, "Materials Testing in Supercritical Water Oxidation Systems," Proc. 1st Int. Workshop Supercritical Water Oxidation (Lake Bluff, IL: WCM Forums, 1995).
12. R.W. Bach, H.A. Friedrichs, H. Rau, High Temp.-High Press. 9 (1977): p. 305.
13. M.L. Japas, E.U. Franck, Ber. Bunsenges. Phys. Chem. 89 (1985): p. 1,268.
14. R. Molins, E. Andrieu, J. Phys. 4 3 (C9) (1993): p. 469.
15. T. Shibata, Corrosion 52 (1996): p. 813.
16. G.T. Burstein, P.C. Pistorius, Corros. Sci. 51 (1995): p. 380.
17. G. Okamoto, Corros. Sci. 13 (1973): p. 471.
18. C.L. McBee, J. Kruger, Electrochim. Acta 17 (1972): p. 1,337.
19. T.P. Moffat, R.M. Lantanision, J. Electrochem. Soc. 139 (1992): p. 1,869.
20. L. Wegrelius, I. Olefjord, Mater. Sci. Forum 185-188 (1995): p. 347.
21. W.J. Plieth, K.J. Vetter, Ber. Bunsenges. Phys. Chem. 73 (1969): p. 1,077.
22. M. Ürgen, U. Stolz, R. Kirchheim, Corros. Sci. 30 (1990). p. 377.
23. M. Keddam, H. Takenouti, N. Yu, J. Electrochem. Soc. 132 (1985): p. 2,561.
24. L.J. Oblonsky, T.M. Devine, J. Electrochem. Soc. 142 (1995): p. 3,677.
25. M. Datta, H.J. Mathieu, D. Landolt, Electrochim. Acta 24 (1979): p. 843.
26. K. Ohashi, T. Hirai, New Mat. New Proc. 3 (1985): p. 173.
27. F. Schneider, M. Herrich, A. John, J. Engelmann, K. Mummert, Mater. Sci. Forum 185, 188 (1995): p. 275.
28. P. Schmuki, S. Virtanen, A.J. Davenport, C.M. Vitus, J. Electrochem. Soc. 143 (1996): p. 3,997.
29. T. Fujii, Trans. Nat. Res. Inst. Met. 18 (1976): p. 101.
30. A.M. Olmedo, M. Villegas, M.G. Alvarez, J. Nucl. Mat. 229 (1996): p. 102.
31. R.M. Carranza, M.G. Alvarez, Corros. Sci. 38 (1996): p. 909.
32. H.J. Choi, Y.H. Hu, M. K.-Ranjbar, J. Mankowski, F.H. Beck, S. Smialowska, D.D. Macdonald, "Effect of Flow Velocity on Pitting Corrosion and Stress Corrosion Cracking of Reactor Materials," Proc. Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 1984), p. 532.
33. 2- on the Corrosion of Fe-Cr-Ni Alloys in Hot Water Systems," Proc. 8th Int. Cong. Metallic Corrosion (Frankfurt, Germany: DECHEMA, 1981), p. 1,887.
34. L.F. Lin, G. Gragnolino, Z.S.-Smialowska, D.D. Macdonald, Corrosion 37 (1981): p. 616.
35. G. Gragnolino, L.F. Lin, Z.S.-Smialowska, Corrosion 37 (1981): p. 312.
36. R.D. Grimm, D. Landolt, Corros. Sci. 36 (1994): p. 1,847.
37. N. Sato, Corros. Sci. 37 (1995): p. 1,947.
38. D. Landolt, "Transpassivity," in Passivity of Metals, eds. R.P. Frankenthal, J. Kruger, Proc. 4th Int. Symp. Passivity (Pennington, NJ: Electrochemical Society, 1977), p. 484.
39. H.U. Borgstedt, Werkst. Korros. 17 (1966): p. 1,027.
40. H. Coriou, J. Hure, G. Plante, Electrochim. Acta 5 (1961): p. 105.
41. J.S. Armijo, Corrosion 21 (1965): p. 235.
42. J.S. Armijo. Corrosion 24 (1968): p. 24.
43. A.E. Pickett, W.L. Pearl, M.C. Rowland, Nucl. Appl. 1 (1965): p. 453.
44. N. Kaneko, S. Abe, "Mechanism of the End Grain Corrosion in Stainless Steels and its Preventive Method," Proc. Int. Conf. Stainless Steels (Chiba, Japan: ISIJ, 1991), p. 280.
45. S.N.V.K. Aki. Z.Y. Ding. M.A. Abraham, AIChE J. 42 (1996): p. 1,995.
46. T.W. Swaddle, J.H. Lipton, G. Guastalla, Can. J. Chem. 49 (1971): p. 2,433.
47. J.W. Cobble, R.C. Murray, Jr., P.J. Turner, K. Chen, "High-Temperature Thermodynamic Data for Species in Aqueous Solution," EPRI Report NP-2400 (Palo Alto, CA: EPRI, 1982).
48. D.D. Macdonald, B.C. Syrett, S.S. Wing, Corrosion 35 (1979): p. 1.
49. J.B. Lee, Corrosion 37 (1981): p. 467.
50. H. Hirano, H. Takaku, T. Kurosawa, Corros. Sci. 31 (1990): p. 557.
51. P. Radhakrishnamurty, P. Adaikkalam, Corros. Sci. 8 (1982): p. 753.
52. P.R. Tremaine, J.C. Leblanc, J. Chem. Thermodyn. 12 (1980): p. 521.
53. K. Dinov, C. Matsuura, D. Hiroishi, K. Ishigure, Nucl. Sci. Eng. 113 (1993): p. 207.
54. D.D. Macdonald, "Thermodynamics of Metal-Water Systems at Elevated Temperatures, part 4: Nickel-Water System," AECL-4139 (Pinawa, Man., Canada: Atomic Energy of Canada, Ltd., 1972).
55. R.L. Cowan, R.W. Staehle, J. Electrochem. Soc. 118 (1971): p. 557.
56. P.C. Ho, D.A. Palmer, J. Solut. Chem. 25 (1996): p. 711.
57. D.B. Mitton, P.A. Marrone, R.M. Latanision, J. Electrochem. Soc. 143 (1996): p. L59.
58. D.B. Mitton, S.-H. Zhang, K.E. Hautanen, J.A. Cline, E.-H. Han, R.M. Latanision, "Evaluating Stress Corrosion and Corrosion Aspects in Supercritical Water Oxidation Systems for the Destruction of Hazardous Waste," CORROSION/97, paper no. 203 (Houston, TX: NACE, 1997).
59. W.E. Berry, "Corrosion Behavior of Fe-Cr-Ni Alloys in High-Temperature Water," in High-Temperature, High-Pressure Electrochemistry, eds. D. de G. Jones, J. Slater, R.W. Staehle (Houston, TX: NACE, 1973), p. 48.
60. R.H. Jones, Stress Corrosion Cracking (Materials Park, OH: ASM, 1992).
61. T.K. Christmann, Corrosion 46 (1990): p. 450.
62. A. Miyasaka, K. Denpo, H. Ogawa, "Environmental Aspects SCC of High Alloys in Sour Environments," CORROSION/88, paper no. 70 (Houston, TX: NACE, 1988).
63. R.N. Parkins, W.K. Blanchard, Jr., B.S. Delanty, Corrosion 50 (1994): p. 394.
64. E.U. Franck, Z. Phys. Chem. N.F. 8 (1956): p. 192.
65. J.D. Frantz, W.L. Marshall, Amer. J. Sci. 284 (1984): p. 651.
66. K.P. Johnston, G.E. Bennett, P.B. Balbuena, P.J. Rossky, J. Amer. Chem. Soc. 118 (1996): p. 6,746.
67. L. Oscarson, S.E. Gillespie, J.J. Christensen, R.M. Izatt, P.R. Brown, J. Solut. Chem. 17 (1988): p. 865.
68. H.C. Helgeson, Amer. J. Sci. 267 (1969): p. 729.
69. L.B. Kriksunov, D.D. Macdonald, J. Electrochem. Soc. 142 (1995): p. 4,069.
70. S. Lin, R.K. Popp, Geochim. Cosmochim. Acta 48 (1984): p. 2,713.
71. F.J. Armellini, J.W. Tester, J. Supercrit. Fluids 4 (1991): p. 245.
72. B.N. Ryzhenko, O.V. Bryzgalln, Geokhlmiya 1 (1987): p. 122 (in English).