Mild steel corrosion in saline solutions. Comparison between bulk solutions and steel-coating interfacial solutions

Journal of Coatings Technology

Volumn 70, Issue 882, 1998, Pages 61-66

  Bastidas, J M ^a   Morcillo, M ^a   Rodriguez F J ^b  

^a DEPARTMENT OF PHYSICAL METALLURGY   (Spain)

^b UNIVERSIDAD NACIONAL AUTÓNOMA DE MÉXICO   (Mexico)

Author keywords

[No Author keywords available]

Indexed keywords

CARBON STEEL; CHLORINE COMPOUNDS; COATINGS; GRAVIMETRIC ANALYSIS; NITRATES; SOLUTIONS; SULFUR COMPOUNDS;

AQUEOUS ELECTROLYTE SOLUTIONS; HUMIDITY TEST;

STEEL CORROSION;

EID: 0032114997     PISSN: 03618773     EISSN: None     Source Type: Journal    
DOI: 10.1007/bf02720516     Document Type: Article

References (12)

1. Morcillo, M., Hernández, L.S., Otero, E., and Feliu, S., "Corrosion of Varnished Steel Induced by Sulphur Dioxide and Sodium Chloride in the Atmosphere," J. Oil & Colour Chemists' Assoc., 72, 402 (1989).
2. Morcillo, M., Hernández, L.S., Simancas, J., Feliu Jr., S., and Gimenez, S., "Underfilm Corrosion of Steel Induced by Saline Contaminants at the Metal/Paint Interface," J. Oil & Colour Chemists' Assoc., 73, 24 (1990).
3. Morcillo, M., "Minimum Film Thickness for Protection of HotRolled Steel: Results after 23 Yeats of Exposure at Kure Beach, North Carolina," in ASTM STP 841, Berger, D.M. and Wint, R F. (Eds.), American Society for Testing and Materials, p. 95-112, 1984.
4. Johnson, W.C., "Corrosion Failure from Water-Soluble Contaminants on Abrasives," J. Prot. Coat. Linings, 7, 54 (1990).
5. Howlett Jr., J.J. and Dupuy, R., "Ultrahigh-Pressure Water Jetting for Deposit Removal and Surface Preparation," Mater. Performance, 32, 38 (1993).
6. Haagen, H., "Einflüsse verschiedener Salzlösungen auf die Stahlkorrosion anhand von tauchversuchen mit unbeschichteten musterblechen," Forschungsinstitut für Pigmente und Lacke E.V., Stuttgart, 1988.
7. Munger, C.G., in Corrosion Prevention by Protective Coatings, NACE, Houston, 1991.
8. Johnson, W.C., "Detrimental Materials at the Steel/Paint Interface," in ASTM STP 841, Berger, D.M. and Wint, R.F. (Eds.), American Society for Testing and Materials, p. 28-43,1984.
9. Morcillo, M., Rodríguez, F.J., and Bastidas, J.M., "The Influence of Chlorides, Sulphates and Nitrates at the Coating-Steel Interface on Underfilm Corrosion," Prog. Org. Coat., 31, 245 (1997).
10. Kittelberger, W.W. and Elm, A.C., "Water Immersion Testing of Metal Protective Paints. Role os osmosis in Water Absorption and Blistering," Ind. Eng. Chem., 38, 695 (1946); "Water Immersion Testing of Metal Protective Paints. Role of Electroendosmosis in Water Absorption and Blistering," Ind. Eng. Chem., 39, 879 (1947).
11. Kittelberger, W.W. and Elm, A.C., "Water Immersion Testing of Metal Protective Paints. Role os osmosis in Water Absorption and Blistering," Ind. Eng. Chem., 38, 695 (1946); "Water Immersion Testing of Metal Protective Paints. Role of Electroendosmosis in Water Absorption and Blistering," Ind. Eng. Chem., 39, 879 (1947).
12. Leidheiser Jr., H. and Wang, W., "Some Substrate and Environmental Influences on the Cathodic Delamination of Organic Coatings," JOURNAL OF COATINGS TECHNOLOGY, 53, No. 672, 77 (1981).