Tensile behavior of a quasi-isotropic carbon-carbon composite

Journal of the American Ceramic Society

Volumn 81, Issue 1, 1998, Pages 113-120

  Namiki, Fumiharu ^a,c   Chou, Tsu Wei ^b,c  

^a NISSAN MOTOR CO   (Japan)

^b AMERICAN CERAMIC SOCIETY   (United States)

^c UNIVERSITY OF DELAWARE   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK INITIATION; CRACKS; ELASTIC MODULI; FABRICATION; MECHANICAL VARIABLES MEASUREMENT; STACKING FAULTS; STRAIN; TENSILE PROPERTIES; THERMAL STRESS;

ELASTIC MODULI DEGRADATION; MECHANICAL RESPONSE; QUASI-ISOTROPIC STACKING SEQUENCE; RESIDUAL STRAIN; TENSILE LOADING; TENSILE STRAIN; YOUNG'S MODULI;

CARBON CARBON COMPOSITES;

EID: 0031703698     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1151-2916.1998.tb02302.x     Document Type: Article

References (25)

1. H. Weisshaus, S. Keinig, and A. Seigmann, "Effect of Materials and Processing on the Mechanical Properties of C/C Composites," Carbon, 29 [8] 1203-20 (1991).
2. P. D. Copp, J. C. Dendis, and S. Mall, "Failure Analysis and Damage Initiation in Carbon-Carbon Composite Materials under Three-Point Bending," J. Compos. Mater., 25, 593-608 (1991).
3. S.-M. Oh and J.-Y. Lee, "Fracture Behavior of Two-Dimensional Carbon/ Carbon Composites," Carbon. 27 [3] 423-30 (1989).
4. P. B. Pollock, "Tensile Failure in 2-D Carbon-Carbon Composites," Carbon, 28 [5] 717-32 (1990).
5. J. Jortner, "Effect of Crimp Angle on the Tensile Strength of a Carbon-Carbon Laminate"; pp. 243-51 in Proceedings of the Symposium on High Temperature Composites (Dayton, OH). American Society for Composites, Technomic, Lancaster, PA, 1989.
6. J. Takayasu, M. Ikegami, E. Tsusima, and A. Shindo, "Mechanical Properties of Unidirectional C/C Composites Prepared Using Matrix Precursor Containing Green Coke as the Main Component"; pp. 540-47 in ICCM Proceedings of the 1993 International Conference on Composite Materials (Barcelona, Spain, 1993). Woodhead Publishing Ltd., Cambridge, England, 1993.
7. K. W. Garrett and J. E. Bailey, "Multiple Transverse Fracture in 90° Cross-Ply Laminates of a Glass Fibre-Reinforced Polyester," J. Mater. Sci., 12, 157-68 (1977).
8. K. W. Garrett and J. E. Bailey, "The Effect of Resin Failure Strain on the Tensile Properties of Glass Fibre-Reinforced Polyester Cross-Ply Laminates," J. Mater. Sci., 12, 2189-94 (1977).
9. A. Parvizi, K. W. Garrett, and J. E. Bailey, "Constrained Cracking in Glass Fibre-Reinforced Epoxy Cross-Ply Laminates," J. Mater. Sci., 13, 195-201 (1978).
10. J. E. Bailey, P. T. Curtis, and A. Parvizi, "On the Transverse Cracking and Longitudinal Splitting Behavior of Glass and Carbon Fibre Reinforced Epoxy Cross-Ply Laminates and the Effect of Poisson and Thermally Generated Strain," Proc. R. Soc. London, Ser. A, 366, 599-623 (1979).
11. T.-W. Chou and P. Karandikar, "Damage Development and Moduli Reductions in Nicalon-CAS Composites under Static Fatigue and Cyclic Fatigue," J. Am. Ceram. Soc., 76, 1720 (1993).
12. T.-W. Chou and P. Karandikar, "Characterization and Modeling of Microcracking and Elastic Moduli Changes in Nicalon-CAS Composites," Compos. Sci. Technol., 76, 1720 (1993).
13. T.-W. Chou and P. Karandikar, "Commonality in the Damage of Ceramic and Polymer Matrix Composites"; p. 249 in High Performance Composites: Commonality of Phenomena. Edited by K. K. Chawla, P. K. Liaw, and S. G. Fishman. The Minerals, Metals and Materials Society, Warrendale, PA, 1994.
14. T.-W. Chou and P. Karandikar, "Damage Processes and Nonlinearity in Ceramic Matrix Composites"; p. 107 in High Temperature Ceramic Matrix Composites I: Design, Durability, and Performance. Edited by A. G. Evans and R. Naslain. American Ceramic Society, Westerville, OH, 1995.
15. P. Pluvinage, A. Parvizi-Majidi, and T.-W. Chou, "Morphological and Mechanical Characterization of 2D Woven and 3D Braided SiC/SiC Composites," J. Mater. Sci., 30, 232 (1995).
16. P. Gudmundson and S. Östlund, "Prediction of Thermoelastic Properties of Composite Laminates with Matrix Cracks," Compos. Sci. Technol. 44, 95-105 (1992).
17. A. L. Highsmith and K. L. Reifsnider, "Stiffness-Reduction Mechanisms in Composite Laminates"; pp. 103-17 in ASTM Special Technical Publication, Vol. 775, Damage in Composite Materials. American Society for Testing and Materials, Philadelphia, PA, 1982.
18. S. G. Lim and C. S. Hong, "Prediction of Transverse Cracking and Stiffness Reduction in Cross-Ply Laminated Composites," J. Compos. Mater., 23, 695-713 (1989).
19. Y. M. Han and H. T. Hahn, "Ply Cracking and Property Degradation of Symmetric Balanced Laminates under General In-Plane Loading," Compos. Sci. Technol. 35, 377-97 (1989).
20. S. C. Tan and R. J. Nuismer, "A Theory for Progressive Matrix Cracking in Composite Laminates," J. Compos. Mater., 23, 1029-47 (1989).
21. Z. Hashin, "Analysis of Cracked Laminates: A Variational Approach," Mech. Mater., 4, 121-36 (1985).
22. Z. Hashin, "Analysis of Orthogonally Cracked Laminates under Tension," J. Appl. Mech., 54, 872-79 (1985).
23. N. Laws, G. J. Dvorak, and M. Hejasi, "Stiffness Changes in Unidirectional Composites Caused by Crack Systems," Mech. Mater., 2, 123-37 (1983).
24. R. Talreja, "Transverse Cracking and Stiffness Reduction in Composite Laminates," J. Compos. Mater., 19, 355-75 (1985).
25. F. Namiki, "Thermomechanical Behavior of a Carbon-Carbon Composite"; Master's Thesis. University of Delaware, Newark, DE, 1993.