Volumn 40, Issue 1, 1998, Pages 15-25

Metallographic and fractographic observations of hydrides during delayed hydride cracking in Zr-2.5% Nb alloy

Author keywords

[No Author keywords available]

Indexed keywords

BRITTLE FRACTURE; CRACKING (CHEMICAL); FRACTOGRAPHY; FRACTURE MECHANICS; METALLOGRAPHY; MORPHOLOGY; OPTICAL MICROSCOPY; SCANNING ELECTRON MICROSCOPY; ZIRCONIUM ALLOYS;

EID: 0031653560     PISSN: 10445803     EISSN: None     Source Type: Journal    
DOI: 10.1016/s1044-5803(97)00091-0     Document Type: Article
Times cited : (10)

References (12)
  • 1
    • 0018690787 scopus 로고
    • Fracture toughness of zirconium hydride and its influence on the crack resistance of zirconium alloys
    • L. A. Simpson and C. Cann: Fracture toughness of zirconium hydride and its influence on the crack resistance of zirconium alloys. J. Nucl. Mater. 87: 303-316 (1979).
    • (1979) J. Nucl. Mater. , vol.87 , pp. 303-316
    • Simpson, L.A.1    Cann, C.2
  • 2
    • 0003089846 scopus 로고
    • Pickering pressure tube cracking experience
    • E. C. W. Perryman: Pickering pressure tube cracking experience. Nucl. Energy 17:95-105 (1978).
    • (1978) Nucl. Energy , vol.17 , pp. 95-105
    • Perryman, E.C.W.1
  • 3
    • 85169144619 scopus 로고
    • Factors controlling hydrogen assisted subcritical crack growth in Zr-2.5% Nb alloys
    • ASTM STP 633, ASTM, Philadelphia
    • L. A. Simpson and K. Nuttall: Factors controlling hydrogen assisted subcritical crack growth in Zr-2.5% Nb alloys. In Zirconium in the Nuclear Industry, ASTM STP 633, ASTM, Philadelphia, pp. 608-629 (1977).
    • (1977) Zirconium in the Nuclear Industry , pp. 608-629
    • Simpson, L.A.1    Nuttall, K.2
  • 4
    • 85126662659 scopus 로고
    • Susceptibility of zirconium alloys to delayed hydrogen cracking
    • ASTM STP 633, ASTM, Philadelphia
    • C. E. Coleman and J. F. R. Ambler: Susceptibility of zirconium alloys to delayed hydrogen cracking. In Zirconium in the Nuclear Industry, ASTM STP 633, ASTM, Philadelphia, pp. 589-607 (1977).
    • (1977) Zirconium in the Nuclear Industry , pp. 589-607
    • Coleman, C.E.1    Ambler, J.F.R.2
  • 5
    • 0039798344 scopus 로고
    • Hydrogen embrittlement effects in hydride-forming metals
    • The Metallurgical Society of CIM
    • R. Dutton: Hydrogen embrittlement effects in hydride-forming metals. In Hydrogen in Metals, Vol. 16, The Metallurgical Society of CIM, (1978).
    • (1978) Hydrogen in Metals , vol.16
    • Dutton, R.1
  • 6
    • 0017542224 scopus 로고
    • Mechanism of hydrogen induced cracking in hydride-forming materials
    • R. Dutton, K. Nuttal, M. Puls, and L. A. Simpson: Mechanism of hydrogen induced cracking in hydride-forming materials. Metall. Trans. 8A:1553-1562 (1977).
    • (1977) Metall. Trans. , vol.8 A , pp. 1553-1562
    • Dutton, R.1    Nuttal, K.2    Puls, M.3    Simpson, L.A.4
  • 7
    • 0019662696 scopus 로고
    • Criteria for fracture initiation at hydrides in zirconium-2.5 pet niobium alloy
    • L. A. Simpson: Criteria for fracture initiation at hydrides in zirconium-2.5 pet niobium alloy. Metall. Trans. 12A:2113-2124 (1981).
    • (1981) Metall. Trans. , vol.12 A , pp. 2113-2124
    • Simpson, L.A.1
  • 8
    • 0026223832 scopus 로고
    • Delayed hydride cracking behavior for Zircaloy-2 tubing
    • F. H. Haung and W. J. Mills: Delayed hydride cracking behavior for Zircaloy-2 tubing. Metall. Trans. 22A:2049-2060 (1991).
    • (1991) Metall. Trans. , vol.22 A , pp. 2049-2060
    • Haung, F.H.1    Mills, W.J.2
  • 11
    • 0030218620 scopus 로고    scopus 로고
    • Hydride morphology and striation formation during delayed hydride cracking in Zr-2.5% Nb
    • G. K. Shek, M. T. Jovanovic, H. Seahra, Y. Ma, D. Li, and R. L. Eadie: Hydride morphology and striation formation during delayed hydride cracking in Zr-2.5% Nb. J. Nucl. Mater. 231:221-230 (1996).
    • (1996) J. Nucl. Mater. , vol.231 , pp. 221-230
    • Shek, G.K.1    Jovanovic, M.T.2    Seahra, H.3    Ma, Y.4    Li, D.5    Eadie, R.L.6
  • 12
    • 0039798340 scopus 로고
    • Acoustic emission study of the various stages of hydrogen induced cracking in Zr-2.5% Nb alloy
    • L. Simpson, ed., Pergamon Press, Oxford
    • K. Tangri and W. K. Yuan: Acoustic emission study of the various stages of hydrogen induced cracking in Zr-2.5% Nb alloy. In Fracture Problems and Solutions in the Energy Industry, L. Simpson, ed., Pergamon Press, Oxford, pp. 27-38 (1982).
    • (1982) Fracture Problems and Solutions in the Energy Industry , pp. 27-38
    • Tangri, K.1    Yuan, W.K.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.