Volumn 21, Issue 6, 1998, Pages 661-672

A first stage in the development of micromechanical simulations of the crystallographic propagation of fatigue cracks under multiaxial loading

Author keywords

Dislocations; Fatigue; Mode II; Multiaxial; Simulations; Stage I crack

Indexed keywords

CRACK PROPAGATION; CRYSTALLOGRAPHY; DISLOCATIONS (CRYSTALS); FATIGUE TESTING; FRICTION; GRAIN BOUNDARIES; MICROCRACKS; NUCLEATION; STRESS ANALYSIS; TORSIONAL STRESS;

EID: 0031644843     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1046/j.1460-2695.1998.00524.x     Document Type: Article
Times cited : (21)

References (23)
  • 1
    • 0022754735 scopus 로고
    • Kinetic study on the propagation of fatigue crack in pure aluminium single crystals under different modes of loading
    • Z. X. Tong, L. Liu, S. Lin and C. M. Hsiao (1986) Kinetic study on the propagation of fatigue crack in pure aluminium single crystals under different modes of loading. Scripta Metall. 20, 967-970.
    • (1986) Scripta Metall. , vol.20 , pp. 967-970
    • Tong, Z.X.1    Liu, L.2    Lin, S.3    Hsiao, C.M.4
  • 2
    • 0005978356 scopus 로고
    • The characteristics of Stage I fatigue fracture in a high strength nickel alloy
    • M. Gell and G. R. Leverant (1968) The characteristics of Stage I fatigue fracture in a high strength nickel alloy. Acta Metall. 16, 553-561.
    • (1968) Acta Metall. , vol.16 , pp. 553-561
    • Gell, M.1    Leverant, G.R.2
  • 3
    • 0021506067 scopus 로고
    • Fatigue crack growth along planar slip bands
    • K. Tanaka and T. Mura (1984) Fatigue crack growth along planar slip bands. Acta Metall. 32(10), 1731-1740.
    • (1984) Acta Metall. , vol.32 , Issue.10 , pp. 1731-1740
    • Tanaka, K.1    Mura, T.2
  • 4
    • 0000636584 scopus 로고
    • A theory for fatigue failure under multiaxial stress-strain conditions
    • M. W. Brown and K. J. Miller (1973) A theory for fatigue failure under multiaxial stress-strain conditions. Proc. Inst. Mech. Engrs 187, 65-73.
    • (1973) Proc. Inst. Mech. Engrs , vol.187 , pp. 65-73
    • Brown, M.W.1    Miller, K.J.2
  • 5
    • 0023854625 scopus 로고
    • A critical plane approach to multiaxial fatigue damage including out-of-phase loading
    • A. Fatemi and D. F. Socie (1988) A critical plane approach to multiaxial fatigue damage including out-of-phase loading. Fatigue Fract. Engng Mater. Struct. 11, 149-165.
    • (1988) Fatigue Fract. Engng Mater. Struct. , vol.11 , pp. 149-165
    • Fatemi, A.1    Socie, D.F.2
  • 6
    • 0030681559 scopus 로고    scopus 로고
    • Crack initiation mechanisms in torsional fatigue
    • V. Doquet (1997) Crack initiation mechanisms in torsional fatigue. Fatigue Fract. Engng Mater. Struct. 20, 227-235.
    • (1997) Fatigue Fract. Engng Mater. Struct. , vol.20 , pp. 227-235
    • Doquet, V.1
  • 7
    • 0026133812 scopus 로고
    • Dislocation emission and fatigue crack growth threshold
    • R. Pippan (1991) Dislocation emission and fatigue crack growth threshold. Acta Metall. Mater. 39(3), 255-262.
    • (1991) Acta Metall. Mater. , vol.39 , Issue.3 , pp. 255-262
    • Pippan, R.1
  • 8
    • 0030393129 scopus 로고    scopus 로고
    • A dislocation model for the two critical stress intensities required for threshold fatigue crack propagation
    • A. J. Wilkinson and S. G. Roberts (1996) A dislocation model for the two critical stress intensities required for threshold fatigue crack propagation. Scripta Mater. 35(11), 1365-1371.
    • (1996) Scripta Mater. , vol.35 , Issue.11 , pp. 1365-1371
    • Wilkinson, A.J.1    Roberts, S.G.2
  • 9
    • 0019055362 scopus 로고
    • Fracture along planar slip bands
    • D. A. Koss and K. S. Chan (1980) Fracture along planar slip bands. Acta Metall. 28, 1245-1252.
    • (1980) Acta Metall. , vol.28 , pp. 1245-1252
    • Koss, D.A.1    Chan, K.S.2
  • 10
    • 0022009515 scopus 로고
    • Cleavage, dislocation emission, and shielding for cracks under general loading
    • I. H. Lin and R. Thomson (1986) Cleavage, dislocation emission, and shielding for cracks under general loading. Acta Metall. 34, 187-206.
    • (1986) Acta Metall. , vol.34 , pp. 187-206
    • Lin, I.H.1    Thomson, R.2
  • 11
    • 0022074312 scopus 로고
    • An electron microscope study of crack tip deformation and its impact on the dislocation theory of fracture
    • S. M. Ohr. (1985) An electron microscope study of crack tip deformation and its impact on the dislocation theory of fracture. Mater. Sci. Engng 72, 1-35.
    • (1985) Mater. Sci. Engng , vol.72 , pp. 1-35
    • Ohr, S.M.1
  • 13
    • 0041972543 scopus 로고
    • Fatigue damage maps
    • (Edited by Ritchie and Starke), University of Virginia. EMAS, Wareley
    • D. F. Socie (1987) Fatigue damage maps. In: Proc. 3rd Int. Conf. on Fatigue and Fatigue Threshold (Edited by Ritchie and Starke), University of Virginia. EMAS, Wareley.
    • (1987) Proc. 3rd Int. Conf. on Fatigue and Fatigue Threshold
    • Socie, D.F.1
  • 14
    • 0018976978 scopus 로고
    • On the small crack fracture mechanics problem
    • J. Lankford (1980) On the small crack fracture mechanics problem. Int. J. Fract. 16(1), R7-R9.
    • (1980) Int. J. Fract. , vol.16 , Issue.1
    • Lankford, J.1
  • 15
  • 16
    • 0344841949 scopus 로고    scopus 로고
    • Quantification of friction effects during mode II fatigue crack propagation in a maraging steel
    • (Edited by E. Macha and Z. Mroz), Cracow, 8-12 September 1997
    • C. Pinna and V. Doquet (1997) Quantification of friction effects during mode II fatigue crack propagation in a maraging steel. In: Proc. 5th Int. Conf. on Biaxial/Multiaxial Fatigue & Fracture (Edited by E. Macha and Z. Mroz), Cracow, 8-12 September 1997, Vol. 2, 97-113.
    • (1997) Proc. 5th Int. Conf. on Biaxial/Multiaxial Fatigue & Fracture , vol.2 , pp. 97-113
    • Pinna, C.1    Doquet, V.2
  • 17
    • 0542397084 scopus 로고
    • The fatigue behaviour of two aluminium-zinc-magnesium alloys
    • S. Lynch and D. A. Ryder (1972) The fatigue behaviour of two aluminium-zinc-magnesium alloys. Scripta Met. 6, 181-186.
    • (1972) Scripta Met. , vol.6 , pp. 181-186
    • Lynch, S.1    Ryder, D.A.2
  • 18
    • 0011282183 scopus 로고
    • Dislocation nucleation from a crack tip: An analysis based on the Peierls concept
    • J. R. Rice (1992) Dislocation nucleation from a crack tip: an analysis based on the Peierls concept. J. Mech. Phys. Solids 40, 239-271.
    • (1992) J. Mech. Phys. Solids , vol.40 , pp. 239-271
    • Rice, J.R.1
  • 19
    • 0027678057 scopus 로고
    • Estimates from atomic models of tension-shear coupling in dislocation nucleation from a crack tip
    • Y. Sun, G. E. Beltz and J. R. Rice (1993) Estimates from atomic models of tension-shear coupling in dislocation nucleation from a crack tip. Mater. Sci. Engng A170, 67-85.
    • (1993) Mater. Sci. Engng , vol.A170 , pp. 67-85
    • Sun, Y.1    Beltz, G.E.2    Rice, J.R.3
  • 20
    • 0024063636 scopus 로고
    • The nature of the wall structure in persistent slip bands of fatigued metals
    • U. Essmann and K. Differt (1988) The nature of the wall structure in persistent slip bands of fatigued metals. Scripta Metall. 22, 1337-1342.
    • (1988) Scripta Metall. , vol.22 , pp. 1337-1342
    • Essmann, U.1    Differt, K.2
  • 21
    • 0022060118 scopus 로고
    • In situ TEM observations of the cyclic dislocations behaviour in persistent slip bands of copper single crystals
    • J. Lepinoux and L. P. Kubin (1985) In situ TEM observations of the cyclic dislocations behaviour in persistent slip bands of copper single crystals. Phil. Mag. A 51(5), 675-696.
    • (1985) Phil. Mag. A , vol.51 , Issue.5 , pp. 675-696
    • Lepinoux, J.1    Kubin, L.P.2
  • 23
    • 0020735548 scopus 로고
    • Double slip plane crack model
    • J. Weertman, I. H. Lin and R. Thomson (1983) Double slip plane crack model. Acta Metall 31(4), 473-482.
    • (1983) Acta Metall , vol.31 , Issue.4 , pp. 473-482
    • Weertman, J.1    Lin, I.H.2    Thomson, R.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.