Initiation and growth of small cracks in directionally solidified MAR-M247 under creep-fatigue part II: Effect of angle between stress axis and solidification direction

Fatigue and Fracture of Engineering Materials and Structures

Volumn 21, Issue 6, 1998, Pages 751-760

  Okada, M ^a   Tsutsumi, M ^a   Kitamura, T ^a   Ohtani, R ^a  

^a KYOTO UNIVERSITY   (Japan)

Author keywords

Anisotropy; Crack growth; Crack initiation; Creep fatigue; Directionally solidified superalloy; Mar M247; Stress direction

Indexed keywords

ANISOTROPY; CRACK INITIATION; CRACK PROPAGATION; CREEP TESTING; FATIGUE TESTING; GRAIN BOUNDARIES; HIGH TEMPERATURE EFFECTS; METALLOGRAPHIC MICROSTRUCTURE; SOLIDIFICATION; STRESS ANALYSIS;

MAR M247 SUPERALLOY; SOLIDIFICATION DIRECTION;

SUPERALLOYS;

EID: 0031621816     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1046/j.1460-2695.1998.00454.x     Document Type: Article

References (13)

1. W. J. Molloy (1990) Investment-cast superalloys. Adv. Mater. Proc. 138(4), 23-30.
2. Y. Ohta, H. Hattori, K. Murakami, Y. Nakagawa and A. Ohtomo (1984) Creep properties of directionally solidified Mar-M247. Trans. Iron Steel Inst. Jpn., 24, B-164.
3. A. E. Gemma, B. S. Langer and G. R. Leverant (1975) Thermomechanical fatigue crack propagation in anisotropic (directionally solidified) nickel-base superalloy. In: Thermal Fatigue of Materials and Components, ASTM STP 612, ASTM, 199-213.
4. H. Hattori, Y. Nakagawa and A. Ohtomo (1984) Effect of orientation on high temperature low-cycle fatigue properties of directionally solidified Mar-M247. Trans. Iron Steel Inst. Jpn., 24, B-163.
5. H. Hattori and T. Degawa (1982) The characteristics of Ni-base superalloy Mar-M247 at high temperature. Prof. 104th Conf. Iron Steel Inst. Jpn., 1458.
6. T. Hasebe, M. Sakane and M. Ohnami (1993) Creep-fatigue life and cyclic constitutive relation of Mar-M247 nickel-base directionally solidified superalloy. J. Soc. Mater. Sci., Jpn., 42, 868-873.
7. M. Marchionni, G. A. Osinkolu and M. Maldini (1996) High temperature cyclic deformation of a directionally solidified Ni-base superalloy. Fatigue Fract. Engng Mater. Struct. 19, 955-962.
8. R. Ohtani, T. Kitamura, M. Okada, M. Tustsumi and M. Matsushita, Initiation and growth of small cracks in directionally solidified superalloy Mar-M247 under creep-fatigue Part I: effect of microstructure. Fatigue Fract. Engng Mater. Struct. 21, 741-750.
9. R. Ohtani, T. Kitamura, A. Nitta and K. Kuwabara (1988) High-temperature low cycle fatigue crack propagation and life laws of smooth specimens derived from the crack propagation laws. In: Low Cycle Fatigue, ASTM STP 942, ASTM, 1163-1180.
10. R. Ohtani and T. Kitamura (1988) Characterization of high temperature strength of metals based on the mechanics of crack propagation. In: High Temperature Creep-fatigue, JSMS Current Japanese Materials Research, Vol. 3, Elsevier, London, 65-90.
11. A. Nitta and K. Kuwabara (1988) Thermal-mechanical fatigue failure and life prediction. In: High Temperature Creep-fatigue. JSMS Current Japanese Materials Research, Vol. 3, The Society of Materials Science, Japan, Elsevier, London, 203-222.
12. R. Ohtani and T. Kitamura (1985) On the fatigue life law for smooth specimens at elevated temperatures derived from fracture mechanics law of crack propagation. J. Soc. Mater. Sci., Jpn., 34, 843-849.
13. R. Ohtani and T. Kitamura (1994) Creep-fatigue interaction under high-temperature conditions. In: Handbook of Fatigue Crack Propagation in Metallic Structures (Edited by A. Carpinteri), Elsevier, Amsterdam, 1347-1383.