Failure of silicon nitride rolling elements with ring crack defects

Ceramics International

Volumn 24, Issue 5, 1998, Pages 379-386

  Hadfield, M ^a  

^a BOURNEMOUTH UNIVERSITY   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

CRACKS; FAILURE ANALYSIS; FINITE ELEMENT METHOD; HOT ISOSTATIC PRESSING; ROLLER BEARINGS; SCANNING ELECTRON MICROSCOPY; STRESS ANALYSIS; SURFACE STRUCTURE;

DYE PENETRATION TEST; RING CRACK DEFECTS;

SILICON NITRIDE;

EID: 0031618518     PISSN: 02728842     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0272-8842(97)00025-4     Document Type: Article

References (15)

1. SCOTT, D. & BLACKWELL, J., Hot pressed silicon nitride as a rolling bearing material - a preliminary assessment. Wear, 24 (1973) 61-67.
2. GIELISSE, P. J., WILSON, M. P., BORASE, V. N., HEUNG, L. K. & KIEHLE, A. J., Ceramic materials for high temperature gas bearings. Report on ONR Contract No. N00014-68-0215-008, Sept. 1972.
3. CUNDILL, R. T., Rolling element bearings into the 21st century. IMechE Seminar, London, Nov. 1990.
4. HÜBER, M. T., Zur theorie de Beruhrung fester elastische Korper. Ann. der Physics, 14 (1904) 153.
5. YINGZHI, LI. & HILLS, D. A., The Hertzian cone crack. Trans. of the ASME, 58 (1991) 120-127.
6. UEDA, K., Contact-stress deformation and fracture in ceramics. Jap. J. Tribology, 34(2) (1989) 123-131.
7. WARREN, P. D., HILLS, D. A. & DAI, D. N., Mechanics of Hertzian cracking. Tribology Int., 28(6) (1995) 357-362.
8. HADFIELD, M., STOLARSKI, T. A., CUNDILL, R. T. & HORTON, S., Failure modes of ceramic elements with ring crack defects. Tribology Int., 26 (1992) 157-164.
9. TOURRET, R. & WRIGHT, E. P., Rolling contact fatigue: performance testing of lubricants. International Symposium, Institute of Petroleum, Oct. 1976.
10. JACOBSON, B. O., Rheology and Elastohydrodynamic Lubrication. Baker and Taylor, Elsevier, Amsterdam, 1991.
11. Engineering Sciences Data, No. 84017, Contact phenomena. 2: stress field and failure criteria in concentrated elastic contacts under combined normal and tangential loading, Oct. 1984.
12. HERTZ, H., On the contact of elastic solids. J. Reine Angew Math., 92 (1881) 156-171.
13. JOHNSON, K. L., Contact Mechanics. Cambridge University Press, UK, 1985.
14. TABOR, D., The mechanism of rolling contact II. The elastic range. Roy. Soc. Proc.: Ser. A, 229 (1955) 198-220.
15. HADFIELD, M., STOLARSKI, T. A. & CUNDILL, R. T., Failure modes of ceramics in rolling contact. Roy. Soc. Proc.: Ser. A, 443 (1993) 607-621.