An accelerated test method for determining near-threshold stress intensity values in HSLA steels

Fatigue and Fracture of Engineering Materials and Structures

Volumn 20, Issue 12, 1997, Pages 1657-1664

  Liu Nash, G ^a   Todd, J A ^a   Mostovoy, S ^a  

^a Illinois Institute of Technology   (United States)

Author keywords

Accelerated tests; HSLA steel; Hydrogen embrittlement; Near fatigue threshold data

Indexed keywords

CRACK PROPAGATION; FATIGUE TESTING; HYDROGEN EMBRITTLEMENT; STEEL CORROSION; STRESS ANALYSIS; STRESS CORROSION CRACKING; STRESS INTENSITY FACTORS;

CONTOURED DOUBLE CANTILEVER BEAMS (CDCB); HIGH STRENGTH LOW ALLOY (HSLA) STEEL; STRESS RATIO;

STEEL BEAMS AND GIRDERS;

EID: 0031338012     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1460-2695.1997.tb01518.x     Document Type: Article

References (23)

1. F. E. Havens and D. M. Bench (May 1969) Fatigue strength of quenched and tempered carbon steel plates and welded joints in sea water. Paper OTC 1046, 1969, Offshore Technology Conference, Houston.
2. J. W. Cochera, J. P. Tralmer and P. W. Marshall (May 1969) Fatigue of structural steels for offshore platforms. Paper OTC 2604, 1976, Offshore Technology Conference, Houston.
3. J. C. Walter, E. Olbjorn, O. Allstad and G. Elde (April 1976) Safety against corrosion fatigue offshore. Publication No. 94, Det Norske Veritas, Norik, Norway.
4. G. S. Booth and J. G. Wylde (1977) Fatigue problems in north sea structures. Metals Science 11, 308.
5. C. E. Jaske, D. Broek, J. E. Slater and W. E. Anderson (1978) Corrosion fatigue of structural steels in seawater and for offshore application. Corrosion Fatigue Technology, ASTM STP 642, 19-47.
6. T. G. Gooch and G. S. Booth (1979) Corrosion fatigue of offshore structures. Metal Science 13(7), 402-410.
7. J. A. Todd, P. Li, G. Liu and V. Raman (1987) Microstructural studies of corrosion fatigue cracks in ASTM A710. In: Environmental Degradation of Engineering Materials, III (Edited by M. R. Louthan, R. P. McNitt and R. D. Sisson, Jr.), 533-541.
8. J. A. Todd, P. Li, G. Liu and V. Raman (1988) A new mechanism of crack closure in cathodically protected ASTM A710 Steel, Scripta Metall. 22, 745-750.
9. Y. Itoh, S. Sewerage and H. Cache (1980) Prediction of fatigue crack growth rate in welding residual stress field. Engng Fract. Mech. 33(3), 397-407.
10. H. J. Spies, G. Punch, C. Henkel and K. Roessler (1989) Fatigue crack propagation in high strength low alloy steels. Theoret. Appl. Fract. Mech. 11(2), 121-125.
11. L. R. Link (1990) Fatigue crack growth of weldments, ASTM STP 1058, ASTM, Philadelphia, PA, 16-33.
12. K. J. Kang, J. H. Song, and Y. Yon (1990) Fatigue crack growth and closure behavior through a compressive residual stress field. Fatigue Fract. Engng Mater. Struct. 13(1), 1-13.
13. A. K. Sablok, and W. H. Hartt (1990) Fatigue of welded structural and high-strength steel plate specimens in seawater. In: Fatigue and Fracture Testing of Weldments, ASTM STP 1058 (Edited by H. I. McHenry and J. M. Potter), ASTM, Philadelphia, 78-95.
14. R. W. Chang, Y. G. Kweon and C. B. Lim, Influence of the welding heat input on fatigue crack growth in offshore structural steel welds. In: Proc. Eighth Internat. Conf, on Offshore Mechanics and Arctic Engineering, ASME, N.Y., 419-430.
15. P. T. Tubby and G. S. Booth (1992) Corrosion fatigue crack growth rate studies in two weldable steels. Proc. 11th Intern. Conf, on Offshore Mechanics and Arctic Engineering, Vol. III: Materials Engineering (Edited by M. M. Salama, G. S. Booth, E. A. Patterson, J. V. Haskell and A. Stacey), Calgary, Canada, 539-549.
16. J. A. Todd, L. Chen and E. Y. Yankov (1993) Near-threshold fatigue crack growth behavior of Mil S-24645 HSLA steel and its weldments. ASME J. Offshore Mech. Arctic Engng Conf. 115(3), 154-161.
17. J. A. Todd, L. Chen, E. Y. Yankov and H. Tao (1993) A comparison of the near-threshold corrosion fatigue crack propagation in MIL S-24645 HSLA steel and its weld metal. ASME J. Offshore Mech. Arctic Engng 115(2), 131-136.
18. J. A. Todd, L. Chen, E. Y. Yankov and S. Mostovoy (1993) Crack closure effects on fatigue crack growth thresholds in a HSLA steel used for pressure vessel applications. In: Service Experience and life Management: Nuclear Fossil Petrochemical Plants (Edited by W. Bamford, W. E. Warke and D. Bagnoli), Proc. ASME Pressure Vessel and Piping Conference, Denver, PVP, Vol. 261, July 25-29, ASME Journal of Engineering Materials and Technology, 201-212 (accepted for publication in the ASME Journal of Pressure Vessel Technology).
19. J. A. Todd, L. Chen, E. Y. Yankov and S. Mostovoy (1993) Crack closure effects on fatigue crack growth thresholds in a HSLA steel used for pressure vessel applications. In: Service Experience and life Management: Nuclear Fossil Petrochemical Plants (Edited by W. Bamford, W. E. Warke and D. Bagnoli), Proc. ASME Pressure Vessel and Piping Conference, Denver, PVP, Vol. 261, July 25-29, ASME Journal of Engineering Materials and Technology, 201-212 (accepted for publication in the ASME Journal of Pressure Vessel Technology).
20. ASTM Standard E 647-91 (1992) Annual Book of ASTM Standards, Section 3, 674-701.
21. ia, fast fracture and crack arrest. ASTM STP 627 (Edited by G. T. Hahn and M. F. Kanninen), American Society for Testing and Materials, 327-391.
22. S. Mostovoy, P. B. Crosley and E. J. Ripling (Sept. 1967) Use of crack-line-loaded specimens for measuring plane-strain fracture toughness. J. Mater. 2(3), 661-681.
23. G. Liu-Nash, R. P. Foley and S. Mostovoy (Feb. 1997) Fatigue test compliance drop during the transition from a hydrogen rich to an air environment. Submitted to Scripta Metall.