Fatigue strength as a function of preloading in dynamic fatigue testing of glass and ceramics

Journal of Engineering for Gas Turbines and Power

Volumn 119, Issue 3, 1997, Pages 493-499

  Gyekenyesi, J P ^b  

^a CLEVELAND STATE UNIVERSITY   (United States)

^b NASA GLENN RESEARCH CENTER   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK PROPAGATION; DYNAMIC LOADS; FATIGUE OF MATERIALS; FATIGUE TESTING; GLASS; STRENGTH OF MATERIALS;

DYNAMIC FATIGUE LOADING;

CERAMIC MATERIALS;

EID: 0031192116     PISSN: 07424795     EISSN: 15288919     Source Type: Journal    
DOI: 10.1115/1.2817011     Document Type: Article

References (23)

1. Wiederhorn, S. M, and Bolz, L. H., “Stress Corrosion and Static Fatigue of Glass,“J. Am. Ceram. Sac., Vol. 53, 1970, pp. 543-548.
2. Evans, A. G., and Wiederhorn, S. M., “Crack Propagation and Failure Prediction in Silicon Nitride at Elevated Temperatures,” J. Mater. Sei., Vol. 9, 1974, pp. 270-278.
3. Hübner, H., and Jillek, W., “Subcritical Crack Extension and Crack Resistance in Polycrystalline Alumina,” J. Mater. Sei, Vol, 12, 1977, pp, 117-125.
4. Sakaguchi, S., Sawaki, Y., Abe, Y., and Kawasaki, T., “Delayed Failure in Silica Glass,” J. Mater. Sei, Vol. 17, 1982, pp. 2878-2886.
5. Dauskardt, R. H., James, M. R., Porter, J. R., and Ritchie, R. O., “Cyclic Fatigue-Crack Growth in SiC-Whisker-Reinforced Alumina Ceramic Composite: Long-and Small-Crack Behavior,” J. Am. Ceram. Soc., Vol. 75, 1992, pp. 759-771.
6. 4,” J. Am. Ceram. Soc, Vol. 61, 1978, pp. 226-230.
7. Henager, C. H., and Jones, R. H., “Environmental Effects on Slow Crack Growth in Silicon Nitride,” Ceram. Eng. Sei. Proc., Vol. 9, 1988, pp. 1525-1530.
8. Horibe, S., and Hirahara, R., “Cyclic Fatigue of Ceramic Materials: Influence of Crack Path and Fatigue Mechanisms,” Acta Metall. Mater., Vol. 39, 1991, pp. 1309-1317.
9. Ritter, J. E., “Engineering Design and Fatigue Failure of Brittle Materials,” in: Fracture Mechanics of Ceramics, Vol. 4, Bradt, R. C., Hasselman, D. P. H., and Lange, F. F., eds., Plenum Publishing Co., New York, 1978, pp. 661-686.
10. Trantina, G. G., “Strength and Life Prediction for Hot-Pressed Silicon Nitride,” J. Am. Ceram. Soc., Vol. 62, 1979, pp. 377-380.
11. 4,” J. Am. Ceram. Soc., Vol. 65, 1982, pp. 15-21.
12. Quinn, G. D., and Quinn, J. B., “Slow Crack Growth in Hot-Pressed Silicon Nitride,” in: Fracture Mechanics of Ceramics, Vol. 6, Bradt, R. C., Evans, A. G., Hasselman, D. P. H., and Lange, F. F., eds., Plenum Press, New York, 1983, pp. 603-636.
13. Chuck, L., McCullum, D. E., Hecht, N. L., and Goodrich, S. M., “High Temperature Tension-Tension Cyclic Fatigue for a Hipped Silicon Nitride,” Ceram. Eng. Sei. Proc., Vol. 12, 1991, pp. 1509-1523.
14. Choi, S. R., Salem, J. A., and Palko, J. A., “Comparison of Tension and Flexure to Determine Fatigue Life Prediction Parameters at Elevated Temperatures,” in Life Prediction Methodologies and Data for Ceramic Materials, ASTM STP 1201, Brinkman, C. R., and Duffy, S. F., eds., ASTM, Philadelphia, 1994, pp. 98-111.
15. Choi, S. R., Salem, J. A., Nemeth, N., and Gyekenyesi, J. P., “Elevated Temperature Slow Crack Growth of Silicon Nitride Under Dynamic, Static, and Cyclic Flexural Loading,” Ceram. Eng. Sci. Proc., Vol. 15, 1994, pp. 597-604.
16. “Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Flexural Testing at Ambient Temperature,” in balloting process, ASTM C28 (Advanced Ceramics) Main Committee, American Society for Testing and Materials, Philadelphia, 1997.
17. Ritter, J. E., Oates, P. B., Fuller, E. R., and Wiederhorn, S. M., “Proof Testing of Ceramics, Part 1 Experiment,” J. Mater. Sci., Vol. 15, 1980, pp. 2275-2281.
18. Fuller, E. R., Wiederhorn, S. M., Ritter, J. E., and Oates, P. B., “Proof Testing of Ceramics, Part 2 Theory,” J. Mater. Sci., Vol. 15, 1980, pp. 2282-2295.
19. Lawn, B.R., Marshall, D. B., Anstis, G. R., and Dabbs, T. P., “Fatigue Analysis of Brittle Materials Using Indentation Flaws, Part 1. General Theory,” J. Mater. Sci., Vol. 16, 1981, pp. 2846-2854.
20. Choi, S. R., Ritter, J. E., and Jakus, K., “Failure of Glass With Subthreshold Flaws,” J. Am. Ceram. Soc., Vol. 73, 1990, pp. 268-274.
21. Marshall, D. B., Lawn, B. R., and Chantikul, P., “Residual Stress Effects in Sharp-Contact Cracking: I,” J. Mater. Sci., Vol. 14, 1979, pp. 2001-2012.
22. Choi, S. R., and Salem, J. A., “Preloading Technique in Dynamic Fatigue Testing of Ceramics: Effect of Preloading on Strength Variation,” J. Mater. Sci. Letters, Vol. 15, 1996, pp. 1963-1965.
23. Choi, S. R., and Salem, J. A., “Effect of Preloading on Fatigue Strength in Dynamic Fatigue Testing of Ceramic Materials at Elevated Temperature,” Ceram. Eng. Sci. Proc., Vol. 16, 1995, pp. 87-94.