On corrosion-induced stress states in binary noble metal alloys

Materials Science and Engineering: A

Volumn 232, Issue 1-2, 1997, Pages 88-102

  Mon, Kevin ^a   Ferrari, Mauro ^a,b  

^a Lawrence Berkeley National Laboratory   (United States)

^b Berkeley   (United States)

Author keywords

Corrosion induced stress; Metal alloys

Indexed keywords

COMPRESSION TESTING; EIGENVALUES AND EIGENFUNCTIONS; SEGREGATION (METALLOGRAPHY); STRAIN RATE; STRESS CONCENTRATION; STRESS CORROSION CRACKING;

NOBLE METAL ALLOYS;

BINARY ALLOYS;

EID: 0031186524     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/s0921-5093(97)00098-1     Document Type: Article

References (24)

1. E.N. Pugh, Progress toward understanding the stress corrosion problem, Corrosion 41 (1985) 517-526.
2. K. Sieradski, R.C. Newman, Stress corrosion cracking, J. Phys. Chem. Solids 48 (1987) 1101-1113.
3. R.N. Parkins, Current understanding of stress-corrosion cracking, J. Metals 44 (1992) 12-19.
4. T.B. Cassagne, W.F. Flanagan, B.D. Lichter, On the failure mechanism of chemically embrittled Cu3Au single crystals, Metall. Trans. A 17A (1986) 703-710.
5. R.C. Newman, T. Shahrabi, K. Sieradski, Film-induced cleavage of alpha-brass, Scr. Metall. 23 (1989) 71-74.
6. R.G. Kelley, A.J. Frost, T. Shahrabi, R.C. Newman, Brittle fracture of an Au/Ag alloy induced by a surface film, Metall. Trans. A 22 (1991) 531-541.
7. J.S. Chen, M. Salmeron, T.M. Devine, Intergranular and transgranular stress corrosion cracking of Cu-30Au, Corros. Sci. 34 (1993) 2071-2097.
8. K. Sieradski, R.C. Newman, Brittle behavior of ductile materials during stress corrosion cracking, Philos. Mag. A 51 (1985) 95-132.
9. R.C. Newman, K. Sieradski, Metallic corrosion, Science 263 (1994) 1708-1709.
10. H.W. Pickering, P.R. Swann, Electron metallography of chemical attack upon some alloys susceptible to stress corrosion cracking, Corrosion 19 (1963) 373t-389t.
11. H. Kaesche, Microtunneling during selective alloy dissolution and during pitting, in: H.S. Isaacs et al. (Eds.), Advances in Localized Corrosion, NACE, Houston, TX, 1990, pp. 153-60.
12. H. Kaiser, Selective dissolution of high and low diffusivity alloys - a comparison of kinetical and micromorphological aspects, Corros. Sci. 34 (1993) 633-699.
13. M. Ferrari, Composite homogenization via the equivalent poly-inclusion approach, Compos. Eng. 4 (1992) 37-45.
14. T. Mura, Micromechanics of Defects in Solids, Kluwer Academic, Boston, 1980.
15. B.A. Boley, J.H. Weiner, Theory of Thermal Stresses, Robert E. Krieger, Malabar, FL, 1960.
16. A. Sommerfeld, Thermodynamics and Statistical Mechanics, Academic Press, New York, 1964.
17. H.W. Pickering, Volume diffusion during anodic dissolution of a binary alloy, J. Electrochem. Soc. 115 (1968) 143-147.
18. T.B. Cassagne, W.F. Flanagan, B.D. Lichter, Transgranular stress-corrosion cracking of disordered Cu-25Au in aqueous chloride and sulfate media, Metall. Trans. A 19A (1988) 281-292.
19. M. Ferrari, Anisotropic layers with through-thickness thermal and material variations, J. Thermal Stresses 15 (1992) 439-445.
20. J.D. Eshelby, The determination of the elastic field of an ellipsoidal inclusion, and related problems, Proc. R. Soc. A 241 (1957) 376-396.
21. M. Ferrari, G.C. Johnson, Effective elasticities of short-fiber composites with arbitrary orientation distribution, Mech. Mater. 8 (1989) 67-73.
22. J.D. Fritz, B.W. Parks, H.W. Pickering, Coherency stress and transgranular stress corrosion cracking of Cu-18Au alloy, in: W.B. Lisagor et al. (Eds.), Environmentally Assisted Cracking: Science and Engineering, ASTM STP 1049, American Society for Testing Materials, 1990, pp. 76-85.
23. V.T. Granik, M. Ferrari, Microstructural mechanics of granular media, Mech. Mater. 15 (1993) 301-322.
24. J.C. Nadeau, A.H. Nashat, M. Ferrari, Isotropic plane elastostatics, in: M. Ferrari et al. (Eds.), Advances in Doublet Mechanics, Springer-Verlag, Berlin, 1996, pp. 157-176.