Fatigue strength prediction of soda-lime glass

Theoretical and Applied Fracture Mechanics

Volumn 27, Issue 2, 1997, Pages 107-114

  Lu B T ^a  

^a NORTHWESTERN POLYTECHNICAL UNIVERSITY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

FATIGUE OF MATERIALS; LIME; LOADS (FORCES); STATISTICAL METHODS; STRENGTH OF MATERIALS; STRESS CONCENTRATION; WEIBULL DISTRIBUTION;

SODA-LIME GLASS;

GLASS;

FATIGUE LIFE ANALYSIS; GLASS;

EID: 0031170991     PISSN: 01678442     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0167-8442(97)00012-8     Document Type: Article

References (25)

1. S.-Y. Liu, T.-W. Chen, Fatigue deformation mechanisms of zirconia ceramics, J. Am. Ceram. Soc. 75 (5) (1992) 1191-1204.
2. A.A. Steffen, R.H. Dauskardt, R.O. Ritchie, Cyclic fatigue life and crack growth behavior of microstructurally small cracks in magnesia-partially-stabilized zirconia ceramics, J. Am Ceram. Soc. 74 (6) (1991) 1259-1268.
3. T.-S. Liu, R. Matt, Grathwohl, Static and cyclic fatigue of 2Y-TZP ceramics with natural flaws, J. Eur. Ceram. Soc. 11 (1993) 133-141.
4. T.A. Michalske, S.W. Freiman, A molecular mechanism for stress corrosion in vitreous silica, J. Am. Ceram. Soc. 66 (4) (1983) 284.
5. T.A. Michalske, B.C. Banker, Slow fracture model based on strained structures, J. Appl. Phys. 56 (10) (1984) 2666.
6. M. Okazaki, A.J. McEvily, T. Tanaka, On the mechanism of fatigue crack growth in silicon nitride, Metall. Trans. 22A (6) (1990) 1425-1434.
7. M.J. Reece, F. Guiu, M.F.R. Sammur, J. Am. Ceram. Soc. 72 (2) (1989) 348.
8. S. Suresh, J.R. Brockenbrouch, Theory and experiments of fracture in cyclic compression: single phase ceramics, transformating toughening ceramics and ceramics composites, Acta Metall. Mater. 36 (6) (1988) 1455-1470.
9. 4 under static and cyclic loads, Jpn. Mater. Soc. 36 (1987) 1122.
10. 2 Ceramics, Ph.D. Dissertation, Xi'an Jaotong University, Xi'an, China, 1991.
11. D.S. Jacobs, I.-W. Chen, Cyclic fatigue in ceramics, a balance between crack shielding accumulation and degradation, J. Am. Ceram. Soc. 78 (3) (1995) 513-520.
12. B.N. Cox, D.B. Marshall, Overview: concepts for bridged cracks in fracture and fatigue, Acta Metall. Mater. 42 (2) (1994) 341-363.
13. R.H. Dauskadt, D.B. Marshall, R.O. Ritchie, Cyclic fatigue-crack propagation in magnesia-partially-stabilized zirconia, J. Am. Ceram. Soc. 73 (2) (1990) 893-903.
14. S. Lathabai, J. Rodel, B.R. Lawn, Cyclic fatigue from frictional degradation at bridged grain in alumina, J. Am. Ceram. Soc. 74 (6) (1991) 1340-1348.
15. H.N. Ko, Fatigue behaviour of sintered Al2O3 under rotary bending and static fatigue, J. Mater. Sci. Lett. 12 (1993) 1866-1870.
16. Y. Mutoh, Fatigue crack growth in several ceramic materials, Fatigue Fract. Eng. Mater. Struct. 16 (3) (1993) 875-884.
17. M. Yoda, Crack growth of C(T) specimens and indentation crack in glass, Int. J. Fract. 39 (1989) R23-R28.
18. B.-T. Lü, C. Wen, Subcritical crack growth and fatigue strength of soda-lime glass, 1996, J. Inorg. Mater. to be published.
19. O. Buxbaum, C.M. Sonsino, F.J. Esper, Fatigue design citeria for ceramic components under cyclic loading, Int. J. Fatigue 16 (4) (1994) 257-265.
20. F.-H. Wang, X.-L. Zheng, M.-X. Lu, Notch strength and statistical analysis of ceramics, Eng. Fract. Mech. 52 (5) (1995) 917.
21. B.-T. Lü, C. Wen, Notched flexual strength of soda-lime glass, 1996, J. Inorg. Mater, to be published.
22. M. Nishida, Stress Concentration Factors, Mositota Press, 1971 (in Japanese).
23. A.G. Evans, Slow crack growth in brittle materials under dynamic loading conditions, Int. J. Fract. 10 (1974) 251.
24. J.R. Davidge, J.R. Mclaren, J. Tappin, Strength-probability-time(SPT) relationships in ceramics, J. Mater. Sci. 8 (1973) 1699.
25. M.J. Hoffman, W. Lentz, M.V. Swain, Y.-W. Mai, Cyclic fatigue lifetime predictions of partially stabilized zirconia with crack resistance curve characteristics, J. Eur. Ceram. Soc. 11 (1993) 445-453.