Fatigue failure probability in a powder metallurgy Ni-base superalloy

Engineering Fracture Mechanics

Volumn 57, Issue 1, 1997, Pages 41-55

  Grison, J ^a   Remy, L ^a  

^a CENTRE DES MATÉRIAUX   (France)

Author keywords

Engineering fatigue crack initiation; Fatigue failure; Inclusion; Probability; Superalloy

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; CRACKS; FATIGUE OF MATERIALS; FRACTURE MECHANICS; GEOMETRY; INCLUSIONS; MATHEMATICAL MODELS; NICKEL POWDER METALLURGY; PROBABILITY; SUPERALLOYS; SURFACES;

FATIGUE CRACKS; FATIGUE FAILURE;

FAILURE ANALYSIS;

FAILURE; FATIGUE; POWDER METALLURGY;

EID: 0031148367     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0013-7944(97)00006-4     Document Type: Article

References (21)

1. Hyzak, J. M. and Bernstein, I. M., The effect of defects on the fatigue crack initiation process in two P M superalloys: Part I. Fatigue origins. Metall. Trans. A, 1982, 13A, 33-43.
2. Lautridou, J. C., Debussac, A. and Soniak, F., A probabilistic model for fatigue life prediction of P.M. Ni base superalloys containing inclusions. In Fatigue 93, ed. J. P. Baillon and J. I. Dickson. Vol. 1, 1993, pp. 285-290.
3. Weibull, W., A statistical distribution function of wide applicability. J. appl. Mech., 1951, 18, 293-297.
4. Jayatilaka and Trustrum. Statistical approach to brittle fracture. J. Mater. Sci., 1977, 12, 1426-1430.
5. Morris, W. L. and James, M. R., Statistical aspects of fatigue failure due to alloy microstructure. Fatigue Mechanisms: Advances in Quantitative Measurement of Physical Damage, ASTM STP 811, ed. J. Lankford, D. L. Davidson, W. L. Morris and R. P. Wei. American Society for Testing and Materials, 1983, pp. 179-206.
6. McCartney, L. N., Can safety factors be reduced safely when designing against fatigue? Fatigue of Engng Mater, and Structures, 1980, 2, 387-400.
7. Pineau, A., Superalloy discs durability and damage tolerance in relation to inclusion. In High Temperature Materials For Power Engineering, Part II, ed. E. Bachelet. Liège, 1990, pp. 913-933.
8. Brückner-Foit, A., Jäckels, H. and Quadfasel, U., Prediction of the lifetime distribution of high-strength components subjected to fatigue loading. Fatigue Fracture Mater. Struct., 1993, 16(8), 891-908.
9. deBussac, A., Prediction of the competition between surface and internal fatigue crack initiation in PM alloys. Fatigue Fracture Mater. Struct., 1994, 17(11), 1319-1325.
10. Grison, J., Fatigue crack initiation at inclusions in a powder metallurgy superalloy, Astroloy. Thesis, Ecole des Mines de Paris, 1994.
11. Grison, J., Rémy, L., Bernède, P., Effect of crack length and environment on fatigue crack growth in a powder metallurgy Ni-base superalloy, submitted to Materials Science and Engineering, 1996.
12. Grison, J., Rémy, L., Fatigue crack initiation from ion metallic inclusions in powder metallurgy Ni-base superalloy, submitted to Fatigue. Fracture of Eng. Materials and Structures, 1996.
13. Rémy, L., Application of fatigue crack growth data to low cycle fatigue at high temperature. Handbook of fatigue Crack Propagation in Metallic Structures, ed. A. Carpinten, Elsevier, 1994, pp. 1307-1346.
14. Lautridou, J. C., Guèdou, J. Y. and Honnorat, Y., Effect of inclusions on LCF life of PM superalloys for turboengine discs. High Temperature Materials for Power Engineering 1990, ed. E. Bachelet et al. 1990, pp. 1163-1172.
15. Grison, J. and Rémy, L., Crack initiation in a P.M. superalloy and life prediction in low cycle fatigue. Fatigue 93, ed. J. P. Baillon and J. I. Dickson, 1993, pp. 871-876.
16. Soniak, F., Growth of short cracks under fatigue in an alloy for turboengine discs. Thesis, Ecole des Mines de Paris, 1989.
17. Beevers, C. J., Bell, K., Karlson, R. L. and Starke, E. A., A model for fatigue crack closure. Engng Fracture Mech. 1984, 29, 93-100.
18. Paucod, T., Schwartz, F., Ducrocq, C. and Lasalmonie, A., Comparison of the cleanliness assessment techniques in P.M. superalloys. High Temperature Mater, for Power Engng, ed. E. Bachelet. Kluwer, Liège, 1990, pp. 913-933.
19. Isida, M., Stress-intensity factor for the tension of an eccentrically cracked strip. Trans. ASME. Ser. E. J. appl. Mech., 1966, 33, 674-675.
20. Murakami, Y., Stress Intensity Factors Handbook. Committee on Fracture Mechanics, The Society of Material Science, Japan, First editor: Y. Murakami, Co-editors: S. Aoki, H. Miyata, K. Tohgo, N. Hasebe, M. Toya, Y. Itoh, H. Terarda and R. Yuuki, Pergamon Press, 1988.
21. Murakami, Y. and Endo, M., Effects of defects, inclusions and inhomogeneities on fatigue strength. Fatigue. 1994, 16, 163-182.