Progressive damage and residual strength of a carbon fibre reinforced metal laminate

Journal of Composite Materials

Volumn 31, Issue 8, 1997, Pages 762-787

  Lawcock, Glyn ^a,b   Ye, Lin ^a   Mai, Yiu Wing ^a  

^a UNIVERSITY OF SYDNEY   (Australia)

^b PURDUE UNIVERSITY   (United States)

Author keywords

Average stress criterion; C scan; Failure mechanisms; Fibre reinforced metal laminates; Notch size; Progressive damage; Residual strength

Indexed keywords

CARBON FIBRE REINFORCED METAL LAMINATES; RESIDUAL STRENGTH;

CARBON FIBERS; CRACKS; ETCHING; FAILURE (MECHANICAL); LAMINATED COMPOSITES; MICROSCOPIC EXAMINATION; RESIDUAL STRESSES; TENSILE STRENGTH;

FIBER REINFORCED METALS;

EID: 0030674111     PISSN: 00219983     EISSN: None     Source Type: Journal    
DOI: 10.1177/002199839703100802     Document Type: Article

References (21)

1. Schijve, J., H. T. M. Van Lipzig, G. F. J. A. Van Gestel and A. H. W. Hoeymakers. 1979. "Fatigue Properties of Adhesive-Bonded Laminated Sheet Material of Aluminium Alloys," Eng. Fract. Mech., 12:561.
2. Kirk, J. N., M. Munro and P. W. R. Beaumont. 1978. "The Fracture Energy of Hybrid Carbon and Glass Fibre Composites," J. Mater. Sci., 13:2197.
3. Marissen, R. 1987. "Fatigue Mechanisms in ARALL, a Fatigue Resitant Hybrid Aluminium Aramid Composite Material." Fatigue 87, 3:1271.
4. Verbruggen, M. L. C. E. and J. W. Gunnink. 1990. "Metal Laminates-A Family of Advanced Materials," 11th Int. European SAMPE Conf., p. 455.
5. Whitney, J. M. and R. J. Niusmer. 1974. "Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations," J. Comp. Mat'ls, 8:253.
6. Nuismer, R. J. and J. M. Whitney. 1975. "Uniaxial Failure of Composite Laminates Containing Stress Concentrations," in Fracture Mechanics of Composites, ASTM STP 593, p. 117.
7. Wegman, R. F. 1989. "Surface Preparation Techniques for Adhesive Bonding," Noyes Publications, Park Ridge, New Jersey.
8. Oken, S. and R. R. June. 1971. "Analytical and Experimental Investigation of Aircraft Metal Structures Reinforced with Filamentary Composites," NASA Contractor Report CR-1859.
9. Hull, D. 1981. "An Introduction to Composite Materials," Cambridge University Press.
10. Vogelsang, L. B. 1982. "Development of a New Hybrid Material (ARALL) for Aircraft Structures," Seminar at University of Manchester, Institute of Science.
11. Mattousch, A. C. 1993. "Test Procedures for Fibre Metal Laminates," Report TD-4-93-003, by Structural Laminates, Delft, The Netherlands.
12. Zhen, S. 1983. "The D Criterion in Notched Composite Laminates," J. R'forced Plastics & Comp., 2:98.
13. Konish, H. J. and J. M. Whitney. 1975. "Approximate Stress in an Orthotropic Plate Containing a Circular Hole," J. Comp. Mat'ls., 9:157.
14. Tan, S. C. 1987. "Finite Width Correction Factors for Anisotropic Plate Containing a Central Opening," J. Comp. Mat'ls, 22:1080.
15. Irwin, G. R. 1958. "Fracture," in Handbuch der Phisk, 6, Springer, p. 551.
16. Li, K., A. Chudnovsky, Y. Kin and J. Macheret. 1995. "Experimental Investigation of Fatigue Crack Growth Behavior of Fibre/Metal Laminates under Uniaxial and Biaxial Loading," Polymer Composites, 16(1):52.
17. Macheret, J. and R. J. Bucci. 1993. "Crack Growth Resistance Curve Approach to Fibre/Metal Laminate Fracture Toughness Evaluation," Eng. Fract. Mech., 45(6):729.
18. Danmei, L., Q. Wei, Y. Weifeng, Y. Mei and Z. Reiping, "Fatigue Behavior of Fibre Aluminium Laminates with Different Residual Stresses," Fatigue Fract. Eng. Mater. Struct., 16(10):1035.
19. Marissen, R. 1984. "Flight Simulation Behavior of Aramid Reinforced Aluminium Laminates (ARALL)," Eng. Fract. Mech., 19(2):261.
20. Vermeeren, C. A. J. R. 1990. "The Blunt Notch Behavior of Metal Laminates: ARALL and GLARE," Report LR-617, Dept. of Aerospace Eng., Delft University of Technology, The Netherlands.
21. Awerbuch, J. and M. S. Madhukar. 1985. "Notched Strength of Composite Laminates: Predictions and Experiments - A Review," J. R'forced Plastics & Comp., 4:3.