Effect of ammonia concentrations on SCC of α-brass under mode III loading

Scripta Materialia

Volumn 35, Issue 12, 1996, Pages 1475-1480

  Qiao, L J ^a   Luo, J L ^a  

^a UNIVERSITY OF ALBERTA   (Canada)

Author keywords

brass; Ammonia solution; Normal stress; Shear stress; Stress corrosion cracking

Indexed keywords

AMMONIA; CRACK PROPAGATION; FRACTURE MECHANICS; SHEAR STRESS; STRESS ANALYSIS; STRESS CORROSION CRACKING;

FRACTURE BEHAVIOUR; NORMAL STRESS; SHEAR STRESS PLANE;

BRASS;

EID: 0030417370     PISSN: 13596462     EISSN: None     Source Type: Journal    
DOI: 10.1016/S1359-6462(96)00321-1     Document Type: Article

References (19)

1. L. J. Qiao, Corrosion, 479, 43 (1987).
2. L. J. Qiao, W. Y. Chu and C. M. Hsiao, Corrosion, 50, 44 (1988).
3. R. M. Latanision and R. W. Staehle, Fundamental Aspects of Stress Corrosion Cracking, ed., R. W. Staehle, A. J. Forty, and D. Van Rooyen, p. 214, NACE, Houston, TX (1969).
4. G. J. Theus and R. W. Staehle, Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, ed., R. W. Staehle, J. Hochmann, R. D. McCright, and J. E. Slater, p. 845, NACE, Houston, TX (1977)
5. A. J. Forty, P. Humble, Phil. Mag., 247, 8 (1963).
6. A. J. Jr., McEvily, A. P. Bond, J. Electrochem. Soc., 131, 112 (1965).
7. E. N. Pugh, A. J. Forty, Fundamental Aspects of Stress Corrosion Cracking, eds, R. W. Staehle, A. J. Forty and D. Van Rooyen, p. 117, NACE, Houston, TX (1969).
8. R.N. Parkins, Parkins Symposium on Fundamental Aspects of Stress Corrosion Cracking, eds, S.M. Bruemmer, E. I. Meletis, R. H. Jones, W.W. Gerberich, F.P. Ford, and R.W. Staehle, p.3, TMS, Warrendale, Pennsylvania (1992).
9. U. Bertocci, E. N. Pugh, and R. E. Ricker, Environmentally-Induced Cracking of Metals, Eds., R. Gangloff and M. Ives, p. 273, NACE, Houston, TX, (1989).
10. E. N. Pugh, Stress Corrosion Research, ed., H. Arup and R. N. Parkins, p.177, Sijthoff and Noordhoff, Netherlands, (1979).
11. J. A. Beavers, Stress-Corrosion Cracking, ed., R. H. Jones, p. 211, ASM, Ohio (1993).
12. J. A. S. Green, H. W. Hayden, W. G. Montague, Effect of Hydrogen on Behavior of Materials, ed., A. W. Thompson, I. M. Bernstein, p. 200, ASM, Warrendale, Pennsylvania, (1976).
13. H. W. Hayden, S. Floreen, Corrosion, 429, 27 (1971).
14. H. Li, R.H. Jones, J.P. Hirth and D.S. Gelles, Metall, and Mater. Trans. A, 26A, 2259 (1995).
15. J. A. S. Green and H. W. Hayden, Hydrogen in Metals, ed., A. W. Thompson, I. M. Bernstein, p. 235, ASM, Warrendale, Pennsylvania, (1976).
16. L. J. Qiao, W. Y. Chu and C. M. Hsiao, Scripta Metall., 7, 21 (1987).
17. D. A. Vermilyea, Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, ed., R. W. Staehle, J. Hochmann, R. D. McCright, and J. E. Slater, p. 208, NACE, Houston, TX (1977)
18. K. Sieradzki and R. C. Newman, Philos. Mag. A 51, 95 (1981).
19. J. P. Benthem, and W. T. Koiter, "Methods on Analysis and Solutions of Crack Problems", G. C. Shi, editor, Noordhoff, Holland (1973).