Damage accumulation mechanisms in thermal barrier coatings

American Society of Mechanical Engineers, Aerospace Division (Publication) AD

Volumn 51, Issue , 1996, Pages 251-257

  Newaz, G M ^a   Nusier, S Q ^a   Chaudhury, Z A ^a   Wright, K P ^b  

^a Wayne State University   (United States)

^b GE AVIATION   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

COALESCENCE; FAILURE (MECHANICAL); LOADS (FORCES); MICROCRACKS; MICROSCOPIC EXAMINATION; OXIDATION; OXIDES; REACTION KINETICS; SUPERALLOYS; THERMAL CYCLING; THERMAL LOAD; ZIRCONIA;

ELECTRON BEAM PLASMA VAPOR DEPOSITION COATING; FICK LAW; MECHANISTIC MODEL; SPALLATION; THERMAL BARRIER COATINGS; THERMALLY GROWN OXIDE;

COATINGS;

EID: 0030397239     PISSN: 07334230     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Article

References (19)

1. Evans, A. G., Crumley, G. B. and Demaray, R.E., "On the Mechanical Behavior of Brittle Coatings and Layers," Oxidation of Metals, Vol. 20. Nos.5/6, 1983, pp. 193-214.
2. Evans, A.G. and J. W. Hutchinson, On the Mechanics of Delamination and Spalling in Compressed Films, Int. J. Solids Structures, Vol. 20, No. 5, pp. 455-466, 1984.
3. Evans, H.E., "Cracking and Spalling of Protective Oxide Layers," J. of Materials Science and Engineering, A120, 1989, pp. 139-146.
4. Chang, G. C., Phucharoen, W. and Miller, R.A., "Finite Element Thermal Stress Solutions for Thermal Barrier Coatings," Surface and Coatings technology, Vol. 32, 1987, pp. 307-325.
5. Suo, Z., "Wrinkling of the Oxide Scale on an Aluminum-Containing Alloy at High Temperatures," J. of Mechanics of Physics and Solids, Vol. 43, #6, 1995, pp. 829-846.
6. Miller, R.A, and Lowell , C.E, "Failure Mechanisms of Thermal Barrier Coatings Exposed to Elevated Temperature," Thin Solid Films, Vol. 99, pp. 265-270.
7. Strangman, T.E., " Thermal Strain-Tolerant Abradable Thermal Barrier Coatings," J. of Engineering Gas Turbines and Power, Vol. 114, 1992, pp. 264-267.
8. Meier, S. M., Nissley, D.M., Sheffler, K.D. and Cruse, T.A., "Thermal Barrier Coating Life Prediction Model Development," J. of Engineering for Gas Turbines and Power, Vol 114, 1992, pp. 258-263.
9. Siegler, D. R. , "Adherence Behavior of Oxide Grown in Air and Synthetic Exhaust Gas on Fe-Cr-Al Alloys Containing Strong Sulfide Forming Elements Ca, Mg, Y, Ce, La Ti and Zr," Oxidation of Metals, Vol. 40, 1993, pp.555-583.
10. 3 Oxide Scale on the Fe-Cr-Al and Fe-Cr-Al-Y Alloys, J. of Oxidation of Metals, Vol. 41, 1994, pp. 343-364.
11. Thompson, J. M. T., and Hunt, G. W. , A General Theory of Elastic Stability. Wiley, New York (1973).
12. Nusier, S.Q. and Newaz, G. M., Unpublished Results, Wayne State University, Detroit, 1996.
13. Neu, R. W., and Sehitoglu H., "Thermomechanical Fatigue, Oxidation, and Creep: Part I. Damage Mechanisms", Met. Trans. , A 20A ,Sep. 1989, pp. 1755-1767.
14. Wittig, L. A., "A Micromechanical Model of Oxidation Effects in SiC/Ti Metal Matrix Composites", Master's thesis, Texas A&M University, College Station, Texas, 1993
15. Aifantis, E. C., "On the Problem of Diffusion in Solids", Acta Mechanica, Vol. 37 1980, pp. 265-296.
16. Wittig, L. A., and Allen, D. H., "Modeling the Effects of Oxidation on Damage in SiC/Ti-15-3 Metal Matrix Composites", J. of Eng. Mat. and Tech. 116 (July 1994) , pp.421-427.
17. Neu, R. W., and Sehitoglu H., "Thermomechanical Fatigue, Oxidation, and Creep: Part II. Life Prediction", Met. Trans. A 20A (Sep. 1989), pp. 1769-1783.
18. Wright, K.P., Private Communication, GE - Evendale, Ohio, 1996
19. Brindley, W. J., "Properties of Plasma Sprayed Bond Coats, Proceedings of TBC Workshop, NASA-LeRC, March, 1995, pp. 189-202