Cyclic fatigue of Zirconia

Fatigue and Fracture of Engineering Materials and Structures

Volumn 19, Issue 12, 1996, Pages 1411-1420

  Schmitt, R ^a   Fett, T ^a   Munz, D ^a  

^a UNIVERSITY OF KARLSRUHE   (Germany)

Author keywords

Ceramic materials; Cyclic fatigue; Lifetimes; Static fatigue; Zirconia

Indexed keywords

CERAMIC MATERIALS; CRACK PROPAGATION; CRACKS; FATIGUE OF MATERIALS; FATIGUE TESTING; STRESS ANALYSIS; STRESS INTENSITY FACTORS;

CYCLIC FATIGUE; PARTIALLY STABILIZED ZIRCONIA; STATIC FATIGUE;

ZIRCONIA;

EID: 0030397106     PISSN: 8756758X     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1460-2695.1996.tb00177.x     Document Type: Article

References (23)

1. A. G. Evans (1980) Fatigue in ceramics. Int. J. Fract. 16, 485-498.
2. A. G. Evans and E. R. Fuller (1974) Crack propagation in ceramic materials under cyclic loading conditions. Metall. Trans. 5, 27-33.
3. C. P. Chen and W. J. Knapp (1973) Fatigue fracture of an alumina ceramic at several temperatures. Fract. Mech. Ceram. 2, 691-702.
4. R. F. Pabst, I. Bognar and J. B. Zwissler (1980) Ergebnisse zur statischen, dynamischen und zyklischen Ermüdung bei keramischen Werkstoffen. Ber. Dt. Keram. Ges. 57, 13-16.
5. 3. J. Mater. Sci. Lett. 12, 220-222.
6. T. Fett, G. Martin, D. Munz and G. Thun (1991) Determination of da/dN-ΔK-curves for small cracks in alumina in alternating bending tests. J. Mat. Sci. 26, 3320-3328.
7. D. A. Krohn and D. P. H. Hasselman (1972) Static and cyclic fatigue behaviour of a polycrystalline aluminia. J. Amer. Ceram. Soc. 55, 208-211.
8. R. H. Dauskardt, W. Yu and R. O. Ritchie (1987) Fatigue crack propagation in transforming toughened zirconia ceramics. J. Amer. Ceram. Soc. 70, C248-C252.
9. R. H. Dauskardt and R. O. Ritchie (1989) Cyclic fatigue-crack growth behavior in ceramics. Instron J. pp. 7-17.
10. G. Grathwohl (1988) Ermüdung von Keramik unter Schwingbeanspruchung. Mat.-wiss. u. Werkstofftech. 19, 113-124.
11. 3 system. J. Amer. Ceram. Soc. 74, 318-325.
12. T. Liu (1990) Herstellung, Degradation und Ermüdung von umwandlungsverstärktem Y-TZP(A) und Ce-TZP Werkstoffen, doctoral thesis, Universität Karlsruhe.
13. R. H. Dauskardt, D. B. Marshall and R. O. Ritchie (1990) Cyclic fatigue-crack propagation in magnesia-partially-stabilized zirconia ceramics. J. Amer. Ceram. Soc. 73, 893-903.
14. A. Steffen, R. Dauskardt and R. Ritchie (1991) Cyclic fatigue life and crack-growth behavior of microstructurally small cracks in magnesia-partially-stabilized zirconia ceramics. J. Amer. Ceram. Soc. 74, 1259-1268.
15. D. L. Davidson, J. B. Campbell and S. Lankford (1991) Fatigue crack growth through partially stabilized zirconia at ambient and elevated temperatures. Acta Metall. Mater. 39, 1319-1330.
16. S.-Y. Liu and I.-W. Chen (1991) Fatigue of yttria-stabilized zirconia: I, Fatigue damage, fracture origins, and lifetime prediction. J. Amer. Ceram. Soc. 74, 1197-1205.
17. S.-Y. Liu and I.-W. Chen (1991) Fatigue of yttria-stabilized zirconia: II, Crack propagation, fatigue striations, and short-crack behavior J. Amer. Ceram. Soc. 74, 1206-1216.
18. I-curves by a modified evaluation of lifetime measurements in static bending tests. J. Amer. Ceram. Soc. 68, C213-C215.
19. D. R. Thomas, L. J. Bain and C. E. Antle (1969) Interferences on the Parameters of the Weibull distribution. Technometrics 11, 445-460.
20. T. Fett and G. Thun (1991) German Design Patent G 9107645.5.
21. R. Warren and B. Johannesson (1984) Creation of stable cracks in hard metals using "bridge" indentation. Powder Metall. 27, 25-29.
22. T. Nose and T. Fujii (1988) Evaluation of fracture toughness for ceramic materials by a single-edge-precracked-beam method. J. Amer. Ceram. Soc. 71, 328-333.
23. T. Fett and D. Munz (1991) Subcritical growth of macrocracks in zirconia. J. Mater. Sci. Lett. 10, 1103-1106.