Calculation of hydrogen concentrations near crack tips using the boundary element method

American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP

Volumn 336, Issue , 1996, Pages 69-73

  Liu, Xiaokun ^a   Todd, Judith A ^a   Wang, Jianjun ^b  

^a Illinois Institute of Technology   (United States)

^b DURHAM UNIVERSITY   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

BOUNDARY ELEMENT METHOD; COMPUTER SIMULATION; CRACKS; DIFFUSION IN SOLIDS; HYDROGEN; HYDROGEN EMBRITTLEMENT; PLASTICITY; SCANNING ELECTRON MICROSCOPY; STRAIN; STRESSES;

CRACK TIPS; HYDROGEN DIFFUSION; PLASTIC ZONE;

STEEL STRUCTURES;

EID: 0030396315     PISSN: 0277027X     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Article

References (11)

1. J. D. Burk, "Hydrogen-Induced Cracking in Surface Production System: Mechanism, Inspection, Repair, and Prevention," SPE 25583, P.559, 1993.
2. 2S Refinery Service," in: M. Prager, Ed., "Interaction of Steels with Hydrogen in Petroleum Industry Pressure Vessel Service," P. 7, MPC, 1989.
3. Wu Shiding, Chen Lian and Liu Minzhi, "Distribution of Hydrogen Concentration near Notch Tip under Mode I Loading," Acta Metallurgica Sinica, P. A86, Vol. 26, No. 2, 1990.
4. R. L. Schulte and P. N. Adler, in: N. F. Fiore and B. J. Berkowitz, Eds., "Advanced Techniques for Characterizing Hydrogen in Metals," P. 233, AIME, 1982.
5. A. R. Troiano, "The Role of Hydrogen and Other Interstitials in the Mechanical Behavior of metals," Trans. ASM, P. 54, Vol. 52, 1960.
6. Y. Hirose and T. Mura, "Nucleation Mechanism of Stress Corrosion Cracking from Notches," Engineering Fracture Mechanics, P. 317, Vol. 19, No. 2, 1984
7. Y. Hirose and T. Mura, "Crack Nucleation and Propagation of Corrosion Fatigue in High-Strength Steel," Engineering Fracture Mechanics, P. 859, Vol. 19, No. 8, 1984.
8. S. I. Ochiai, S. Yoshinaga and Y. Kikuta, "Formulation of Stress(strain)-Induced Diffusion of Hydrogen and Its Solution by Computer-Aided Finite Element Method," Trans Iron Steel Inst Jpn, P. 503, Vol. 15, 1975.
9. Y. Kikuta, K. Sugimoto, S. I. Ochiai and K. Iwata, "Hydrogen-Dislocation Interaction and Its Parallelism with Hydrogen Embrittlement," Trans Iron Steel Insp Jpn, P. 87, Vol. 15, 1975.
10. X. Liu, J. Wang, S. Jin, "The Investigation of Stress Corrosion Cracking Characteristics of GC-4 Ultra-high Strength Steel Using Slow Strain Rate Technique", Acta Aeronautica et Astronautica Sinica, P. A479, Vol. 10, No. 9, 1989.
11. Makio Iino, "The Extension of Hydrogen Blister-Crack Array in Linepipe Steels", Metal. Trans. A, P. 1581, Vol. 9A, 1978.