Transmission electron microscopy study of stress-ruptured aged 304H stainless steel after prolonged exposure in service

Journal of Materials Engineering and Performance

Volumn 5, Issue 6, 1996, Pages 691-694

  Sengupta, A ^a,b   Balogh, M ^c  

^a WAYNE STATE UNIVERSITY   (United States)

^b GM Ovonic   (United States)

^c GENERAL MOTORS CORPORATION   (United States)

Author keywords

Exposure; Stainless steel; Stress rupture; TEM

Indexed keywords

AGING OF MATERIALS; CONDENSER TUBES; FRACTURE MECHANICS; SERVICE LIFE; STEEL METALLOGRAPHY; STRESSES; SUPERHEATER TUBES; TRANSMISSION ELECTRON MICROSCOPY;

HIGH-TEMPERATURE APPLICATIONS; LONG-TERM APPLICATIONS; STRESS RUPTURE;

STAINLESS STEEL;

EID: 0030392862     PISSN: 10599495     EISSN: None     Source Type: Journal    
DOI: 10.1007/BF02646903     Document Type: Article

References (14)

1. B. Weiss and R. Stickler, Phase Instabilities during High Temperature Exposure of 316 Austenitic Steel, Metallurgical Transactions A, Vol 3, 1972, p 851
2. A.A. Tavasoli, A. Bisson, and R. Soulat, Ferrite Decomposition in Austenitic Stainless Steel Weld Metals, Metal Science, Vol 18, 1984, p 345
3. S. Ahila, S. Ramakrishna Iyer, and V.M. Radhakrishnan, High Temperature Stability of 2.25Cr-1Mo Steel during Creep, Materials at Higher Temperatures, Vol 12, 1994, p 5
4. M.D. Mathew, G. Sasikala, S.L. Mannan, and P. Rodriguez, A Comparative Study of Creep Rupture Properties of Type 316 Stainless Steel Base and Weld Metals, J Engg. Materials and Technology, Vol 115, 1993, p 163
5. R.A. Varin and J. Haftek, Structural Changes in a Ferrite Heat-resistant Steel After Long-term Service, Materials Science and Engineering, Vol 62, 1984, p 129
6. R.G. Baker and J. Nutting, The Tempering of 2.25Cr-1Mo Steel after Quenching and Normalizing, Iron and Steel Institute Journal, Vol 192, 1959, p 257
7. T. Wada and V.A. Biss, Restoration of Elevated Temperature Tensile Strength in 2.25Cr-1Mo Steel, Metallurgical Transactions A, Vol 16, 1983, p 845
8. N.S. Cheruvu, Degradation of Mechanical Properties of Cr-Mo-V and 2.25Cr-1Mo Steel Components after Long-term Service at Elevated Temperature, Metallurgical Transactions A, Vol 20, 1989, p 87
9. W.B. Jones and J.A. Van Den Avyle, Substructure and Strengthening Mechanisms in 2.25Cr-1Mo Steel at Elevated Temperature, Metallurgical Transactions A, Vol 11, 1980, p 1275
10. ASTM A 213, "Standard Specification for Seamless Ferritic and Austenitic Alloy Steel Boiler, Superheater and Heat Exchanger Tubes," Annual Book of ASTM Standards, Vol 0.1.01, 1994, p 109
11. 6 Carbides on Grain Boundaries in an Austenitic Stainless Steel, Vol 242, May 1986, p 814-819
12. K.B.S. Rao, H. Schuster, and G.R. Halford, On Massive Carbide Precipitation during High Temperature Low Cycle Fatigue in Alloy 800H, Scripta Metallurgica et Materialia, Vol 31, 1994, p 381
13. M. Ahmad, K.A. Shoaib, M.A. Shaikh, and J.A. Akhtar, Identification of Surface Carbides and Spinels in Welded Austenitic Stainless Steels, Journal of Materials Science, Vol 29, 1994, p 1169
14. P.H. Pumphrey and I.W. Edington, The Structure of the Semicoherent Interface between Grain Boundary Nucleated M23C6 and Austenitic Stainless Steel, Acta Metall., Vol 22, Jan 1974, p 89-94