Characterization of Synergistic Effects between Erosion and Corrosion in an Aqueous Environment Using Electrochemical Techniques

Corrosion

Volumn 52, Issue 12, 1996, Pages 934-946

  Zhou, S ^a,b   Stack, M M ^c   Newman, R C ^a  

^a UNIVERSITY OF MANCHESTER   (United Kingdom)

^b National Physics Laboratory   (United Kingdom)

^c NONE

Author keywords

Aqueous environments; Carbonate bicarbonate solution; Corrosion rate; Dissolution; Electrochemical testing; Erosion corrosion; Mild steel; Passivation; Rotating cylinder electrode; Synergistic effects; Velocity; Weight loss

Indexed keywords

CARBON STEEL; CORROSION RESISTANCE; DISSOLUTION; ELECTROCHEMICAL CORROSION; ELECTROCHEMICAL ELECTRODES; EROSION; PASSIVATION; REACTION KINETICS; SOLUTIONS;

EROSION CORROSION RATE; ROTATING CYLINDER ELECTRODE (RCE); SYNERGISTIC EFFECTS;

STEEL CORROSION;

EID: 0030385093     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3292087     Document Type: Article

References (25)

1. R.J.K. Wood, S.P. Hutton, Wear 140 (1990): p. 387-394.
2. K.C. Barker, A. Ball, Brit. Corros. J. 24, 3 (1989): p. 222-228.
3. Y. Zheng, Z. Yao, X. Wei, W. Ke, Wear 186-187 (1995): p. 555-561.
4. Y. Li, I.M. Hutchings, G.T. Burstein, Wear 186-187 (1995): p. 515-522.
5. C.H. Pitt, Y.M. Chang, Corrosion 42, 6 (1986): p. 312-317.
6. B.W. Madsen, Wear 123, 2 (1988): p. 127-142.
7. Y. Oka, M. Matsumura, M. Yamawaki, "Slurry Erosion-Corrosion on Commercially Pure Iron in a Vibratory Testing Facility." Proc. 7th Int. Conf. Erosion by Liquid and Solid Impact, ELSI VII, paper no. 40, eds. J.E. Field, J.P. Dear (Cambridge, U.K.: Cavendish Laboratory, University of Cambridge, 1987).
8. Z. Yue, P. Zhou, J. Shi, "Some Factors Influencing Erosion-Corrosion Performance of Materials," Proc. Conf. Wear of Materials, ed. K.C. Ludema (New York, NY: ASME, 1987), p. 763-768.
9. J.M. Sutcliffe, R.R. Fessler, W.K. Boyd, R.N. Parkins, Corrosion 28 (1972): p. 313.
10. E. Deltombe, M. Pourbaix, 6th Proc. Com. Int. Thermodyn. Cinet. Electrochim. (London, England: Butterworths. 1954), p. 124.
11. F. Umemura, S. Matukura, T. Kawamoto, Corros. Eng. 36 (1987): p. 567-578.
12. M. Matsumura, Y. Oka, H. Hiura, M. Yano, ISIJ Int. 31, 2 (1991): p. 168-176.
13. D.H. Davies, G.T. Burstein, Corrosion 36 (1980): p. 416.
14. P. Southworth, A. Hamnett, A.M. Riley, J.M. Sykes, Corros. Sci. 28 (1988): p. 1,139.
15. M.J. Graham, J.A. Bardwell, R. Goetz, D.F. Mitchell, B. Macdougall, Corros. Sci. 31 (1990): p. 139-148.
16. J. Postlethwaite, E.B. Tinker, M.W. Hawrylak, Corrosion 30, 8 (1974): p. 285-290.
17. K.D. Efird, Corrosion 33 (1976): p. 3.
18. M.M. Stack, S. Zhou, R.C. Newman, Wear 186-187 (1995): p. 523-532.
19. R. Oltra, G.M. Indrianjafy, M Keddam, H. Takenouti, Corros. Sci. 35 (1993): p. 827-832.
20. D.H. Davies, G.T. Burstein, Corrosion 36 (1980): p. 416.
21. E.B. Castro, C.R. Valentini, C.A. Moina, J.R. Vilche, A.J. Arvia, Corros. Sci. 26, 10 (1988): p. 781-793.
22. M. Eisenberg, C.W. Tobias, C.R. Wilke, J. Electrochem. Soc. 101, 6 (1954): p. 306-319.
23. S. Zhou, M.M. Stack, R.C. Newman, Corros. Sci. 38,7 (1996): p. 1,071-1,084.
24. 2- Solutions" (Ph.D. thesis, University of Newcastle Upon Tyne, 1991).
25. M.M. Stack, S. Zhou, R.C. Newman, Mater. Sci. Technol. 21 (1996): p. 261-268.