Hydrogen enhanced fatigue crack propagation of bainitic and tempered martensitic steels

Corrosion Science

Volumn 38, Issue 11, 1996, Pages 2049-2060

  Tau, L ^a   Chan, S L I ^a   Shin, C S ^a  

^a NATIONAL TAIWAN UNIVERSITY   (Taiwan)

Author keywords

A. steels; B. hydrogen embrittlement; C. corrosion fatigue

Indexed keywords

BAINITE; CORROSION FATIGUE; CRACK PROPAGATION; FRACTURE MECHANICS; HYDROGEN EMBRITTLEMENT; ISOTHERMS; MARTENSITE; METALLOGRAPHIC MICROSTRUCTURE; STRESS CORROSION CRACKING; TEMPERING; TENSILE TESTING; THERMAL EFFECTS;

HYDROGEN ENHANCED FATIGUE CRACK PROPAGATION (FCP);

STEEL;

CRACK PROPAGATION; FATIGUE; HYDROGEN EMBRITTLEMENT; STEELS;

EID: 0030295133     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0010-938X(96)89123-2     Document Type: Article

References (36)

1. R. P. Gangloff, Environment Induced Cracking of Metals, (eds. R. P. Gangloff and M. B. Ives), NACE-10, NACE, 55 (1989).
2. R. P. Wei and R. P. Gangloff, Fracture Mechanics: Perspectives and Directions, (eds. R. P. Wei and R. P. Gangloff), ASTM STP 1020, 233 (1989).
3. R. Krishnamurthy, C. N. Marzinsky and R. P. Gangloff, Hydrogen Effects on Material Behavior, (eds. N. R. Moody and A. W. Thompson), TMS, 891 (1990).
4. I. M. Bernstein and A. W. Thompson (eds.), Hydrogen Effects in Metals, AIME, USA (1981).
5. J. W. Christian and D. V. Edmonds, Phase Transformations in Ferrous Alloys, (eds. A. R. Marder and J. I. Goldstein), AIME, New York, 293 (1984).
6. H. K. D. H. Bhadeshia, Phase Transformations '87 (ed. G. W. Lorimer), Institute of Metals, London, 309 (1987).
7. Viewpoint Set No, 11, Scripta Met., 21, 1009 (1987).
8. H. K. D. H. Bhadeshia (ed.), Bainite in Steels, Cambridge University Press (1992).
9. G. B. Olson, Scripta Met. 21, 1023 (1987).
10. G. B. Olson, H. K. D. H. Bhadeshia and M. Cohen, Phase Transformations '87, (ed. G. W. Lorimer), Institute of Metals, London, 22 (1987)
11. H. G. A. Bates and K. A. Ridal (eds.), Creep, Institute Mech. Eng., London, 99 (1963).
12. M. C. Murphy and G. D. Branch, J. Iron Steel Inst. 207, 11347 (1969).
13. J. Barford and G. Willoughby, Metal Sci. 5, 32 (1971).
14. M. C. Murphy and G. D. Branch, J. Iron Steel Inst. 209, 546 (1971).
15. G. E. Kerns, M. T. Wang and R. W. Staehle, Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, (eds. R. W. Staehie et al.), NACE-5. NACE, 700 (1977).
16. T. Fujita and Y. Yamada, Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, (eds. R. W. Staehle et al.), NACE-5, NACE, 736 (1977).
17. I. M. Bernstein and A. W. Thompson, Advances in Corrosion Science and Technology (eds. M. G. Fontana and R. W. Staehle), Plenum, New York, 7(53) (1988).
18. F. C. Akbasoglu and D. V. Edmonds, Metall. Trans. A 21A, 889 (1990).
19. G. E. Hollox, R. A. Hobbs and J. M. Hampshire, Wear 68, 229 (1981).
20. P. L. Andresen, R. P. Gangloff, L. F. Coffin and F. P. Ford, Fatigue '87, (eds. R. O. Ritchie and E. A. Starke, Jr.), EMAS, UK, 1723 (1987).
21. R. P. Gangloff, Mater. Sci. and Eng. A103, 157 (1988).
22. F. P. L. Kavishe, Inter. J. of Fracture 27, 13 (1985).
23. A. Saxena and S. J. Hudak, Inter. J. of Fracture 14, 453 (1978).
24. S. L. I. Chan and J. A. Charles, Mater. Sci. and Technol. 1, 956 (1986).
25. M. A. V. Devanathan and Z. Stachurski, Proc. Roy. Soc. London A270, 90 (1962).
26. A. J. Kumnick and H. H. Johnson, Metall. Trans. A 5, 1199 (1974).
27. R. O. Ritchie and S. Suresh, Metall. Trans. A 13A, 937 (1982).
28. D. L. Davidson, Fat. Eng. Mater. Struc. 3, 229 (1981).
29. A. Ohtsuka, K. Mori and T. Miyata, Eng. Fract. Mech. 7, 425 (1975).
30. Y. Sakamoto and K. Takao, Proc. 2nd Int. Congress Hydrogen in Metals, Paris, Vol. 1. paper 1. A8 (1977).
31. S. L. I. Chan, Ph. D. Thesis, University of Cambridge (1985).
32. G. M. Pressouyre, Metall. Trans. A 14A, 2183 (1983).
33. D. L. Johnson, G. Krauss, J. K. Wu and K. P. Tang, Metall. Trans. A 18A, 717 (1987).
34. J. D. Hobson and C. Skes, J. Iron Steel Inst. 169, 209 (1951).
35. J. W. Kennedy and J. A. Whittaker, Corros. Sci. 8, 359 (1968).
36. M. Gao and R. P. Wei, Metall. Trans. A 6A, 2039 (1985).